PRECITE®

Preliminary

K GF 30 natural (7437)

PBT-PET- GF 30

PRECITE® K GF 30 natural (7437) is a 30% glass fibre reinforced PBT/PET blend with high strength and improved surface finish.

Modulus

10.800MPa

Strength

170MPa

Impact

60kJ/m²

PRECITE® K GF 30 natural (7437) is a 30% glass fibre reinforced PBT/PET blend with high strength and improved surface finish.

AKROMID®

A3 GF 25 FR natural (7649)

PA66 GF25 FR(40)

AKROMID® A3 GF 25 FR natural (7649) is a 25% glass fibre reinforced, halogen and red phosphourus free flame retardant polyamide 6.6 with high stiffness and strength and light inherent color

Modulus

9.200MPa

Strength

135MPa

Impact

63kJ/m²

AKROMID® A3 GF 25 FR natural (7649) is a 25% glass fibre reinforced, halogen and red phosphourus free flame retardant polyamide 6.6 with high stiffness and strength and light inherent color

AKROMID®

UL

A3 1 FR black (3051)

PA66 FR(30)

AKROMID® A3 1 FR black (3051) - PA6.6, unreinforced, flame retardant, UL-listed, E&E market.

Modulus

3.500MPa

Strength

83MPa

Impact

70kJ/m²

AKROMID® A3 1 FR black (3051) - PA6.6, unreinforced, flame retardant, UL-listed, E&E market.

AKROMID®

A3 GF 30 4 black (3571)

PA66 GF30

A3 GF 30 4 black (3571) - PA 6.6 30% glass fiber reinforced, hydrolysis and chemically stabilised, suitable for cooling systems in the automotive industry

Modulus

11.500MPa

Strength

210MPa

Impact

80kJ/m²

A3 GF 30 4 black (3571) - PA 6.6 30% glass fiber reinforced, hydrolysis and chemically stabilised, suitable for cooling systems in the automotive industry

AKROMID®

S3 8 natural (4881)

PA610

AKROMID® S3 8 natural (4881) - partly bio-based PA 6.10, low moisture absorption, increased chemical resistance, food contact

Modulus

2.300MPa

Strength

65MPa

Impact

180kJ/m²

AKROMID® S3 8 natural (4881) - partly bio-based PA 6.10, low moisture absorption, increased chemical resistance, food contact

AKROMID®

A3 1 S3 grey (2955)

PA66+PA6-I

AKROMID® A3 1 S3 grey (2955) - PA 6.6, unreinforced, impact modified, for connecting and fixing systems, automotive, E&E

Modulus

2.500MPa

Strength

68MPa

Impact

180kJ/m²

AKROMID® A3 1 S3 grey (2955) - PA 6.6, unreinforced, impact modified, for connecting and fixing systems, automotive, E&E

AKROMID®

Preliminary

NEXT B3 GF 30 1 L CI black (8375)

PA6 + PP GF30

AKROMID® NEXT B3 GF 30 1 L CI schwarz (8375) - PA6/PP-Blend, biomass-balanced, 30% glass fibre, lower density, good chemical resistance.

Modulus

8.800MPa

Strength

140MPa

Impact

70kJ/m²

AKROMID® NEXT B3 GF 30 1 L CI schwarz (8375) - PA6/PP-Blend, biomass-balanced, 30% glass fibre, lower density, good chemical resistance.

158596080

AKROMID®

Preliminary
Internal

NEXT 5.6 3 GF 35 9 FR natural (8401)PA56 GF35 FR(40)

AKROMID® NEXT 5.6 3 GF 35 9 FR natural (8401) is a partially bio-based and flame retardant PA 5.6 and meets the requirement according to UL94 V0 @ 1.6 mm. The flame-retardant system is free of red phosphorus and halogens. PA 5.6 is a HMD-free (hexamethylenediamine) alternative to PA 6.6. With 35% glass fibre reinforcement, the material is suitable for components with high strength requirements for E&E and E-Mobility, such as busbar supports, switches, terminal strips and connector housings.

Features

Bio-based
heat stabilised 130
flame retardant
E&E

Properties

Modulus

12.000MPa

Strength

160MPa

Impact

71kJ/m²

Sustainability

Biobased carbon content

35 %

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
1 mm/min | conditioned
12000 MPa
7200 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
160 MPa
105 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
2,5 %
4,1 %

Flexural modulus

ISO 178

2 mm/min | d.a.m.
2 mm/min | conditioned
12500 MPa
7700 MPa

Flexural strength

ISO 178

2 mm/min | d.a.m.
2 mm/min | conditioned
255 MPa
160 MPa

Flexural strain at break

ISO 178

2 mm/min | d.a.m.
2 mm/min | conditioned
2,8 %
4,0 %

Charpy impact strength

ISO 179-1/1eU

23°C | d.a.m.
23°C | conditioned
30°C | d.a.m.
-
71 kJ/m²
70 kJ/m²
69 kJ/m²

Charpy notched impact strength

ISO 179-1/1eA

23°C | d.a.m.
23°C | conditioned
30°C | d.a.m.
-
12 kJ/m²
15 kJ/m²
11 kJ/m²

Thermal Properties

Temperature of deflection under load HDT/A

ISO 75

1,8 MPa
230 °C

Melting temperature

ISO 11357-3

DSC, 10K/min
254 °C

Flammability

Burning rate

UL 94

1,6 mm Wall thickness
3,2 mm Wall thickness
V-0 Class
V-0 Class

GWFI

IEC 60695-2-12

0,8 mm Wall thickness
1,6 mm Wall thickness
960 °C
900 °C

GWIT

IEC 60695-2-13

0,8 mm Wall thickness
1,6 mm Wall thickness
725 °C
725 °C

Burning rate (<100 mm/min)

FMVSS 302

> 1 mm Thickness
+

General properties

Density

ISO 1183

23°C
1,43 g/cm³

Water absorption

ISO 62

23°C, saturated
2,0 %

Electrical Properties

Comparative tracking index

IEC 60112

Test liquid A
600 V

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.

Contact

Do you have any questions? We are happy to help.

Would you like to learn more about AKRO-PLASTIC GmbH? Contact us! We will be happy to help you.

Learn more