AKROMIDĀ®

A3 GF 25 FR natural (7649)

PA66 GF25 FR(40)

AKROMIDĀ® A3 GF 25 FR natural (7649) is a 25% glass fibre reinforced, halogen and red phosphourus free flame retardant polyamide 6.6 with high stiffness and strength and light inherent color

Modulus

9.200MPa

Strength

135MPa

Impact

63kJ/mĀ²

AKROMIDĀ® A3 GF 25 FR natural (7649) is a 25% glass fibre reinforced, halogen and red phosphourus free flame retardant polyamide 6.6 with high stiffness and strength and light inherent color

AKROMIDĀ®

Preliminary

NEXT B3 GF 30 1 L CI black (8375)

PA6 + PP GF30

AKROMIDĀ® NEXT B3 GF 30 1 L CI schwarz (8375) - PA6/PP-Blend, biomass-balanced, 30% glass fibre, lower density, good chemical resistance.

Modulus

8.800MPa

Strength

140MPa

Impact

70kJ/mĀ²

AKROMIDĀ® NEXT B3 GF 30 1 L CI schwarz (8375) - PA6/PP-Blend, biomass-balanced, 30% glass fibre, lower density, good chemical resistance.

AKROMIDĀ®

B3 GF 20 1 natural (2462)

PA6 GF20

AKROMIDĀ® B3 GF 20 1 natural (2462) is a 20% glass fibre reinforced, heat stabilised polyamide 6 with medium stiffness and strength and light inherent color.

Modulus

6.800MPa

Strength

150MPa

Impact

73kJ/mĀ²

AKROMIDĀ® B3 GF 20 1 natural (2462) is a 20% glass fibre reinforced, heat stabilised polyamide 6 with medium stiffness and strength and light inherent color.

AKROMIDĀ®

B3 GF 15 8 L natural (5689)

PA6+PP GF15

AKROMIDĀ® B3 GF 15 8 L natural (5689) - PA6/PP-Blend, GF 15, with lower density, cost reduced, calcium chloride, food contact, FDA, EU10/2011

Modulus

5.200MPa

Strength

110MPa

Impact

65kJ/mĀ²

AKROMIDĀ® B3 GF 15 8 L natural (5689) - PA6/PP-Blend, GF 15, with lower density, cost reduced, calcium chloride, food contact, FDA, EU10/2011

PRECITEĀ®

Preliminary

K GF 30 natural (7437)

PBT-PET- GF 30

PRECITEĀ® K GF 30 natural (7437) is a 30% glass fibre reinforced PBT/PET blend with high strength and improved surface finish.

Modulus

10.800MPa

Strength

170MPa

Impact

60kJ/mĀ²

PRECITEĀ® K GF 30 natural (7437) is a 30% glass fibre reinforced PBT/PET blend with high strength and improved surface finish.

AKROMIDĀ®

B3 GF 35 1 black (20017)

PA6 GF35

AKROMIDĀ® B3 GF 35 1 black (20017) - 35% glass fiber reinforced PA 6, heat stabilised, technical parts in industrial engineering and automotive industry

Modulus

11.000MPa

Strength

185MPa

Impact

100kJ/mĀ²

AKROMIDĀ® B3 GF 35 1 black (20017) - 35% glass fiber reinforced PA 6, heat stabilised, technical parts in industrial engineering and automotive industry

AKROMIDĀ®

T9 GF 35 4 black (7858)

PPA GF35

AKROMIDĀ® T9 GF 35 4 schwarz (7858) is a 35% glass fibre reinforced polyphthalamide with medium stiffness and strength, as well as high chemical resistance. The compound is based on PA9T and has lower moisture uptake than conventional PA6T variants. This leads to a significantly higher consistency of the glass transition temperature and higher strength at elevated temperatures especially in conditioned state.

Modulus

11.000MPa

Strength

200MPa

Impact

75kJ/mĀ²

AKROMIDĀ® T9 GF 35 4 schwarz (7858) is a 35% glass fibre reinforced polyphthalamide with medium stiffness and strength, as well as high chemical resistance. The compound is based on PA9T and has lower moisture uptake than conventional PA6T variants. This leads to a significantly higher consistency of the glass transition temperature and higher strength at elevated temperatures especially in conditioned state.

158596080

AKROMIDĀ®

Internal

B28 GF 25 9 natural (6360)PA6 GF25

AKROMIDĀ® B28 GF 25 9 natural (6360) is a 25% glass fibre reinforced, processing optimised polyamide 6 with high rigidity and strength and light inherent color.

Properties

Modulus

8.000MPa

Strength

168MPa

Impact

Na

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
8000 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.
168 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.
3,4 %

Thermal Properties

Melting temperature

ISO 11357-3

DSC, 10K/min
220 Ā°C

Flammability

Burning rate

UL 94

0,4 mm Wall thickness
0,8 mm Wall thickness
1,6 mm Wall thickness
3,2 mm Wall thickness
HB Class
HB Class
HB Class
HB Class

Burning rate (<100 mm/min)

FMVSS 302

> 1 mm Thickness
+

Protection Bus

ECE 118

Appendix 6, 7, 8

General properties

Density

ISO 1183

23Ā°C
1,3 g/cmĀ³

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKROĀ®, AKROMIDĀ®, AKROLENĀ®, AKROLOYĀ®, AKROTEKĀ®, ICXĀ® and PRECITEĀ® are registered trademarks of the Feddersen Group.

Contact

Do you have any questions? We are happy to help.

Would you like to learn more about AKRO-PLASTIC GmbH? Contact us! We will be happy to help you.

Learn more