PRECITE®

Preliminary

K GF 30 natural (7437)

PBT-PET- GF 30

PRECITE® K GF 30 natural (7437) is a 30% glass fibre reinforced PBT/PET blend with high strength and improved surface finish.

Modulus

10.800MPa

Strength

170MPa

Impact

60kJ/m²

PRECITE® K GF 30 natural (7437) is a 30% glass fibre reinforced PBT/PET blend with high strength and improved surface finish.

AKROMID®

A3 GF 25 FR natural (7649)

PA66 GF25 FR(40)

AKROMID® A3 GF 25 FR natural (7649) is a 25% glass fibre reinforced, halogen and red phosphourus free flame retardant polyamide 6.6 with high stiffness and strength and light inherent color

Modulus

9.200MPa

Strength

135MPa

Impact

63kJ/m²

AKROMID® A3 GF 25 FR natural (7649) is a 25% glass fibre reinforced, halogen and red phosphourus free flame retardant polyamide 6.6 with high stiffness and strength and light inherent color

AKROMID®

UL

A3 1 FR black (3051)

PA66 FR(30)

AKROMID® A3 1 FR black (3051) - PA6.6, unreinforced, flame retardant, UL-listed, E&E market.

Modulus

3.500MPa

Strength

83MPa

Impact

70kJ/m²

AKROMID® A3 1 FR black (3051) - PA6.6, unreinforced, flame retardant, UL-listed, E&E market.

AKROMID®

A3 GF 30 4 black (3571)

PA66 GF30

A3 GF 30 4 black (3571) - PA 6.6 30% glass fiber reinforced, hydrolysis and chemically stabilised, suitable for cooling systems in the automotive industry

Modulus

11.500MPa

Strength

210MPa

Impact

80kJ/m²

A3 GF 30 4 black (3571) - PA 6.6 30% glass fiber reinforced, hydrolysis and chemically stabilised, suitable for cooling systems in the automotive industry

AKROMID®

S3 8 natural (4881)

PA610

AKROMID® S3 8 natural (4881) - partly bio-based PA 6.10, low moisture absorption, increased chemical resistance, food contact

Modulus

2.300MPa

Strength

65MPa

Impact

180kJ/m²

AKROMID® S3 8 natural (4881) - partly bio-based PA 6.10, low moisture absorption, increased chemical resistance, food contact

AKROMID®

A3 1 S3 grey (2955)

PA66+PA6-I

AKROMID® A3 1 S3 grey (2955) - PA 6.6, unreinforced, impact modified, for connecting and fixing systems, automotive, E&E

Modulus

2.500MPa

Strength

68MPa

Impact

180kJ/m²

AKROMID® A3 1 S3 grey (2955) - PA 6.6, unreinforced, impact modified, for connecting and fixing systems, automotive, E&E

AKROMID®

Preliminary

NEXT B3 GF 30 1 L CI black (8375)

PA6 + PP GF30

AKROMID® NEXT B3 GF 30 1 L CI schwarz (8375) - PA6/PP-Blend, biomass-balanced, 30% glass fibre, lower density, good chemical resistance.

Modulus

8.800MPa

Strength

140MPa

Impact

70kJ/m²

AKROMID® NEXT B3 GF 30 1 L CI schwarz (8375) - PA6/PP-Blend, biomass-balanced, 30% glass fibre, lower density, good chemical resistance.

158596080

AKROMID®

A3 GM 20/10 4 WIT black (4529)PA66 (GF20+GB10)

AKROMID® A3 GM 20/10 4 WIT black (4529) is a 20% glass fiber and 10% glass bead reinforced polyamide 6.6. It is characterized by high rigidity and strength. The material also convinces with a good surface and low tendency to warp and can be processed using a water injection process. In addition, the material is stabilized against hydrolysis and chemicals and is therefore ideally suited, for example, for technical components in the cooling water circuit in the automotive industry.

Features

hydrolysis / chemically stabilised
surface modified
low warpage
fluid injection (GIT/WIT/FIT)

Properties

Modulus

8.200MPa

Strength

175MPa

Impact

65kJ/m²

Sustainability

Recycled content

10 %

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
1 mm/min | conditioned
8200 MPa
5200 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
175 MPa
100 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
3,7 %
11,5 %

Flexural modulus

ISO 178

2 mm/min | d.a.m.
2 mm/min | conditioned
7600 MPa
5200 MPa

Flexural strength

ISO 178

2 mm/min | d.a.m.
2 mm/min | conditioned
260 MPa
170 MPa

Flexural strain at break

ISO 178

2 mm/min | d.a.m.
2 mm/min | conditioned
4,6 %
7,5 %

Charpy impact strength

ISO 179-1/1eU

23°C | d.a.m.
23°C | conditioned
30°C | d.a.m.
-
30°C | conditioned
-
65 kJ/m²
80 kJ/m²
50 kJ/m²
48 kJ/m²

Charpy notched impact strength

ISO 179-1/1eA

23°C | d.a.m.
23°C | conditioned
30°C | d.a.m.
-
30°C | conditioned
-
9 kJ/m²
9,5 kJ/m²
7 kJ/m²
6,5 kJ/m²

Thermal Properties

Temperature of deflection under load HDT/A

ISO 75

1,8 MPa
240 °C

Temperature of deflection under load HDT/B

ISO 75

0,45 MPa
260 °C

Melting temperature

ISO 11357-3

DSC, 10K/min
262 °C

Flammability

Burning rate

UL 94

0,8 mm Wall thickness
HB Class

Burning rate (<100 mm/min)

FMVSS 302

> 1 mm Thickness
+

General properties

Density

ISO 1183

23°C
1,36 g/cm³

Humidity absorption

ISO 1110

70°C, 62% r.H.
2,0 %

Molding shrinkage

ISO 294-4

flow
transverse
0,3 - 0,5 %
0,7 - 0,9 %

Electrical Properties

Volume resistivity IEC

DIN EN IEC 62631-3-2

d.a.m.
conditioned
1013 Ω x cm
1010 Ω x cm

Surface resistivity

DIN EN 62631-3-2

d.a.m.
conditioned
1012 Ω
1010 Ω

Rheological Properties

MVR

ISO 1133

275°C/5kg
6 cm³/10 min

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.