AKROMID®

B3 ICF 20 black (5103)

PA6 CF20

AKROMID® B3 ICF 20 black (5103) is a 20% carbon fibre reinforced polyamide 6 with high flexural strength and good sliding properties

Modulus

13.500MPa

Strength

150MPa

Impact

55kJ/m²

AKROMID® B3 ICF 20 black (5103) is a 20% carbon fibre reinforced polyamide 6 with high flexural strength and good sliding properties

AKROLOY®

PA GF 40 black (2845)

PA66 + PA6I/6T GF40

AKROLOY® PA GF 40 black (2845) is a 40% glass fibre reinforced, semi-aromatic polyamide blend with very high stiffness and strength, even in conditioned state. The advanced version of this Product is AKROLOY® PA GF 40 black (6416) with a modern stabilization technology, featuring improved weld-line strength and an even wider process window.

Modulus

13.000MPa

Strength

230MPa

Impact

95kJ/m²

AKROLOY® PA GF 40 black (2845) is a 40% glass fibre reinforced, semi-aromatic polyamide blend with very high stiffness and strength, even in conditioned state. The advanced version of this Product is AKROLOY® PA GF 40 black (6416) with a modern stabilization technology, featuring improved weld-line strength and an even wider process window.

AKROMID®

B3 GF 20 1 black (2483)

PA6 GF20

AKROMID® B3 GF 20 1 black (2483) is a 20% glass fibre reinforced, heat stabilised polyamide 6 with medium stiffness and strength

Modulus

6.800MPa

Strength

150MPa

Impact

73kJ/m²

AKROMID® B3 GF 20 1 black (2483) is a 20% glass fibre reinforced, heat stabilised polyamide 6 with medium stiffness and strength

AKROMID®

B3 LA black (4056)

PA6

AKROMID® B3 LA black (4056) - PA6, unreinforced, laser markable, E&E, automotive, industry

Modulus

3.400MPa

Strength

85MPa

Impact

180kJ/m²

AKROMID® B3 LA black (4056) - PA6, unreinforced, laser markable, E&E, automotive, industry

AKROMID®

B3 1 L black (4525)

PA6+PP

AKROMID® B3 1 L schwarz (4525) - PA/PP-Blend lightweight, cost reduced

Modulus

2.300MPa

Strength

55MPa

Impact

180kJ/m²

AKROMID® B3 1 L schwarz (4525) - PA/PP-Blend lightweight, cost reduced

AKROMID®

A3 GF 30 4 black (3571)

PA66 GF30

A3 GF 30 4 black (3571) - PA 6.6 30% glass fiber reinforced, hydrolysis and chemically stabilised, suitable for cooling systems in the automotive industry

Modulus

11.500MPa

Strength

210MPa

Impact

80kJ/m²

A3 GF 30 4 black (3571) - PA 6.6 30% glass fiber reinforced, hydrolysis and chemically stabilised, suitable for cooling systems in the automotive industry

AKROMID®

B3 GF 15 1 L natural (4690)

PA6+PP GF15

AKROMID® B3 GF 15 1 L natural (4690) - PA6/PP-Blend 15% glass fibre reinforced, lower density, cost reduced, calcium chloride

Modulus

5.200MPa

Strength

110MPa

Impact

60kJ/m²

AKROMID® B3 GF 15 1 L natural (4690) - PA6/PP-Blend 15% glass fibre reinforced, lower density, cost reduced, calcium chloride

158596080

AKROMID®

B3 GK 30 natural (2719)PA6 GB30

AKROMID® B3 GK 30 natural (2719) is a PA 6 filled with 30% glass beads. It is characterized by a high surface quality and low tendency to warp, which makes it suitable for use in technically demanding components in mechanical engineering and in the automotive industry.

Features

surface modified
low warpage

Properties

Modulus

4.400MPa

Strength

70MPa

Impact

30kJ/m²

Sustainability

Recycled content

30 %

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
1 mm/min | conditioned
4400 MPa
1820 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
70 MPa
38 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
5 %
35 %

Flexural modulus

ISO 178

2 mm/min | d.a.m.
2 mm/min | conditioned
3140 MPa
1570 MPa

Flexural strength

ISO 178

2 mm/min | d.a.m.
2 mm/min | conditioned
95 MPa
55 MPa

Charpy impact strength

ISO 179-1/1eU

23°C | d.a.m.
23°C | conditioned
30 kJ/m²
60 kJ/m²

Charpy notched impact strength

ISO 179-1/1eA

23°C | d.a.m.
23°C | conditioned
3 kJ/m²
5 kJ/m²

Ball indentation hardness

ISO 2039-1

358N/30s | conditioned
961N/30s | d.a.m.
90 MPa
180 MPa

Thermal Properties

Temperature of deflection under load HDT/A

ISO 75

1,8 MPa
70 °C

Temperature of deflection under load HDT/B

ISO 75

0,45 MPa
185 °C

Melting temperature

ISO 11357-3

DSC, 10K/min
222 °C

Vicat softening temperature B50

ISO 306

50°C/50N
205 °C

Flammability

Burning rate

UL 94

1,6 mm Wall thickness
HB Class

Burning rate (<100 mm/min)

FMVSS 302

> 1 mm Thickness
+

General properties

Density

ISO 1183

23°C
1,34 g/cm³

Humidity absorption

ISO 1110

70°C, 62% r.H.
2,1 %

Water absorption

ISO 62

23°C, saturated
6,5 %

Molding shrinkage

ISO 294-4

flow
transverse
0,9 %
1,0 %

Electrical Properties

Volume resistivity IEC

DIN EN IEC 62631-3-2

d.a.m.
1015 Ω x cm

Surface resistivity

DIN EN 62631-3-2

d.a.m.
1013 Ω

Rheological Properties

MVR

ISO 1133

275°C/5kg
100 cm³/10 min

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.