AKROMID®

B3 GF 25 1 natural (2463)

PA6 GF25

AKROMID® B3 GF 25 1 natural (2463) is a 25% glass fibre reinforced, heat stabilised polyamide 6 with high stiffness and strength and light inherent color

Modulus

8.500MPa

Strength

160MPa

Impact

85kJ/m²

AKROMID® B3 GF 25 1 natural (2463) is a 25% glass fibre reinforced, heat stabilised polyamide 6 with high stiffness and strength and light inherent color

AKROMID®

B3 GF 50 S1 natural (3694)

PA6-I GF50

AKROMID® B3 GF 50 S1 natural (3694) - PA 6, 50% glass fiber reinforced, impact modified, industrial applications, housings and covers, automotive

Modulus

14.500MPa

Strength

190MPa

Impact

110kJ/m²

AKROMID® B3 GF 50 S1 natural (3694) - PA 6, 50% glass fiber reinforced, impact modified, industrial applications, housings and covers, automotive

AKROMID®

B3 GF 15 1 L natural (4690)

PA6+PP GF15

AKROMID® B3 GF 15 1 L natural (4690) - PA6/PP-Blend 15% glass fibre reinforced, lower density, cost reduced, calcium chloride

Modulus

5.200MPa

Strength

110MPa

Impact

60kJ/m²

AKROMID® B3 GF 15 1 L natural (4690) - PA6/PP-Blend 15% glass fibre reinforced, lower density, cost reduced, calcium chloride

AKROMID®

A3 GF 13 S3 natural (2788)

PA66-I GF13

AKROMID® A3 GF 13 S3 natural (2788) - PA 6.6, glass fiber reinforced, dry impact modified, for mechanical engineering and automotive industry

Modulus

5.200MPa

Strength

125MPa

Impact

75kJ/m²

AKROMID® A3 GF 13 S3 natural (2788) - PA 6.6, glass fiber reinforced, dry impact modified, for mechanical engineering and automotive industry

AKROLOY®

PA GF 50 grey (3807)

PA66 + PA6I/6T GF50

AKROLOY® PA GF 50 grey (3807) is a 50% glass fibre reinforced, semi-aromatic polyamide blend with very high stiffness and strength.

Modulus

17.200MPa

Strength

250MPa

Impact

105kJ/m²

AKROLOY® PA GF 50 grey (3807) is a 50% glass fibre reinforced, semi-aromatic polyamide blend with very high stiffness and strength.

AKROMID®

A28 GF 40 1 natural (4919)

PA66 GF40

AKROMID® A28 GF 40 1 natural (4919) - 40% glass fiber reinforced, easy flowing PA 6.6, heat stabilised, technical parts in industrial engineering and automotive industry

Modulus

13.000MPa

Strength

245MPa

Impact

95kJ/m²

AKROMID® A28 GF 40 1 natural (4919) - 40% glass fiber reinforced, easy flowing PA 6.6, heat stabilised, technical parts in industrial engineering and automotive industry

PRECITE®

Preliminary

K GF 30 natural (7437)

PBT-PET- GF 30

PRECITE® K GF 30 natural (7437) is a 30% glass fibre reinforced PBT/PET blend with high strength and improved surface finish.

Modulus

10.800MPa

Strength

170MPa

Impact

60kJ/m²

PRECITE® K GF 30 natural (7437) is a 30% glass fibre reinforced PBT/PET blend with high strength and improved surface finish.

157585980

AKROMID®

Internal

S3 GF 30 1 black (3259)PA610 GF30

AKROMID® S3 GF 30 1 black (3259) is a 30% glass fibre reinforced, heat stabilised polyamide 6.10 with high strength and stiffness, lower moisture absorption and high chemical resistance.

Features

heat stabilised 130
reduced moisture

Properties

Modulus

8.600MPa

Strength

160MPa

Impact

100kJ/m²

Sustainability

Biobased carbon content

59 %

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
1 mm/min | conditioned
8600 MPa
6200 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
160 MPa
110 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
4,5 %
7,5 %

Flexural modulus

ISO 178

2 mm/min | d.a.m.
7700 MPa

Flexural strength

ISO 178

2 mm/min | d.a.m.
230 MPa

Standard bending strength RP 3,5

ISO 178

2mm/min | d.a.m.
5,5 MPa

Charpy impact strength

ISO 179-1/1eU

23°C | d.a.m.
23°C | conditioned
30°C | d.a.m.
-
100 kJ/m²
100 kJ/m²
100 kJ/m²

Charpy notched impact strength

ISO 179-1/1eA

23°C | d.a.m.
30°C | d.a.m.
-
17 kJ/m²
12 kJ/m²

Ball indentation hardness

ISO 2039-1

961N/30s | d.a.m.
195 MPa

Thermal Properties

Temperature of deflection under load HDT/A

ISO 75

1,8 MPa
205 °C

Temperature of deflection under load HDT/C

ISO 75

8 MPa
145 °C

Melting temperature

ISO 11357-3

DSC, 10K/min
220 °C

Flammability

Burning rate

UL 94

UL
0,8 mm Wall thickness
UL
3,2 mm Wall thickness
HB Class
HB Class

Burning rate (<100 mm/min)

FMVSS 302

> 1 mm Thickness
+

General properties

Density

ISO 1183

23°C
1,31 g/cm³

Humidity absorption

ISO 1110

70°C, 62% r.H.
1,2 %

Molding shrinkage

ISO 294-4

flow
transverse
0,3 %
0,9 %

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.