AKROMID®

B3 GM 15/15 black (1830)

PA6 (GF15+GB15)

AKROMID® B3 GM 15/15 black (1830) is a 15% glass fibre and 15% glass bead reinforced polyamide 6 with good surface and low warpage

Modulus

7.200MPa

Strength

130MPa

Impact

64kJ/m²

AKROMID® B3 GM 15/15 black (1830) is a 15% glass fibre and 15% glass bead reinforced polyamide 6 with good surface and low warpage

AKROMID®

A3 GF 15 1 black (2382)

PA66 GF15

AKROMID® A3 GF 15 1 black (2382) is a 15% glass fibre reinforced, heat stabilised polyamide 6.6 with medium stiffness and strength.

Modulus

6.400MPa

Strength

140MPa

Impact

35kJ/m²

AKROMID® A3 GF 15 1 black (2382) is a 15% glass fibre reinforced, heat stabilised polyamide 6.6 with medium stiffness and strength.

AKROMID®

B3 GF 15 S3 black (2345)

PA6-I GF15

AKROMID® B3 GF 15 S3 black (2345) - PA 6 with 15% glass fiber reinforcement and impact modified, good surface appearance

Modulus

5.500MPa

Strength

110MPa

Impact

75kJ/m²

AKROMID® B3 GF 15 S3 black (2345) - PA 6 with 15% glass fiber reinforcement and impact modified, good surface appearance

AKROMID®

A3 GF 40 1 natural (2381)

PA66 GF40

AKROMID® A3 GF 40 1 natural (2381) is a 40% glass fibre reinforced, heat stabilised polyamide 6.6 with high rigidity and strength and light inherent color.

Modulus

13.100MPa

Strength

225MPa

Impact

100kJ/m²

AKROMID® A3 GF 40 1 natural (2381) is a 40% glass fibre reinforced, heat stabilised polyamide 6.6 with high rigidity and strength and light inherent color.

AKROMID®

A3 GF 15 1 natural (2308)

PA66 GF15

AKROMID® A3 GF 15 1 natural (2308) - 15% glass fibre, heat stabilised, polyamide 6.6, medium stiffness and strength

Modulus

6.400MPa

Strength

140MPa

Impact

45kJ/m²

AKROMID® A3 GF 15 1 natural (2308) - 15% glass fibre, heat stabilised, polyamide 6.6, medium stiffness and strength

AKROMID®

A3 GF 25 1 natural (2390)

PA66 GF25

AKROMID® A3 GF 25 1 natural (2390) is a 25% glass fibre reinforced, heat stabilised polyamide 6.6 with high stiffness and strength and light inherent color.

Modulus

8.500MPa

Strength

185MPa

Impact

70kJ/m²

AKROMID® A3 GF 25 1 natural (2390) is a 25% glass fibre reinforced, heat stabilised polyamide 6.6 with high stiffness and strength and light inherent color.

AKROMID®

A3 S1 natural (2310)

PA66-I

AKROMID® A3 S1 natural (2310) - PA 6.6, unreinforced, cold impact modified, for connecting and fixing systems, automotive, E&E

Modulus

2.000MPa

Strength

50MPa

Impact

180kJ/m²

AKROMID® A3 S1 natural (2310) - PA 6.6, unreinforced, cold impact modified, for connecting and fixing systems, automotive, E&E

156575880

AKROMID®

B3 GF 40 black (6077)PA6 GF40

AKROMID® B3 GF 40 black (6077) is a 40% glass fiber reinforced, heat stabilised polyamide 6. It is characterised by a very high stiffness and strength. The material is perfectly suitable for safety-related parts in the automotive interior.

Properties

Modulus

13.000MPa

Strength

205MPa

Impact

110kJ/m²

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
1 mm/min | conditioned
13000 MPa
7800 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
205 MPa
140 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
4 %
7 %

Flexural modulus

ISO 178

2 mm/min | d.a.m.
12600 MPa

Charpy impact strength

ISO 179-1/1eU

23°C | d.a.m.
23°C | conditioned
30°C | d.a.m.
-
40°C | d.a.m.
-
110 kJ/m²
106 kJ/m²
105 kJ/m²
100 kJ/m²

Charpy notched impact strength

ISO 179-1/1eA

23°C | d.a.m.
23°C | conditioned
30°C | d.a.m.
-
40°C | d.a.m.
-
20 kJ/m²
30 kJ/m²
15 kJ/m²
15 kJ/m²

Thermal Properties

Temperature of deflection under load HDT/A

ISO 75

1,8 MPa
215 °C

Temperature of deflection under load HDT/B

ISO 75

0,45 MPa
220 °C

Temperature of deflection under load HDT/C

ISO 75

8 MPa
170 °C

Melting temperature

ISO 11357-3

DSC, 10K/min
220 °C

Flammability

Burning rate

UL 94

1,6 mm Wall thickness
HB Class

Burning rate (<100 mm/min)

FMVSS 302

> 1 mm Thickness
+

General properties

Density

ISO 1183

23°C
1,46 g/cm³

Humidity absorption

ISO 1110

70°C, 62% r.H.
1,8 %

Water absorption

ISO 62

23°C, saturated
5,5 %

Molding shrinkage

ISO 294-4

flow
transverse
0,1 - 0,3 %
0,5 - 0,7 %

Electrical Properties

Volume resistivity IEC

DIN EN IEC 62631-3-2

d.a.m.
conditioned
1013 Ω x cm
1010 Ω x cm

Comparative tracking index

IEC 60112

Test liquid A
600 V

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.