Find the right compound
Select your fitting and find the right compound for your intend
AKROMID®
NEXT U28 ICF 30 1 black (8233)
PA11 CF30
AKROMID® NEXT U28 ICF 30 1 black (8233) - PA11 made of renewable raw materials, recycled carbon fibre, low density, high ductility
15.300MPa
165MPa
75kJ/m²
AKROMID® NEXT U28 ICF 30 1 black (8233) - PA11 made of renewable raw materials, recycled carbon fibre, low density, high ductility
AKROMID®
A3 GF 50 ECO black (8571)
PA66 GF50
AKROMID® A3 GF 50 ECO black (8571) - PA 6.6, 50% glass fiber, recycling, high stiffness and strength, heat-stabilised, laser markable, automotive, mechanical engineering.
16.000MPa
190MPa
80kJ/m²
AKROMID® A3 GF 50 ECO black (8571) - PA 6.6, 50% glass fiber, recycling, high stiffness and strength, heat-stabilised, laser markable, automotive, mechanical engineering.
AKROMID®
NEXT U28 GF 35 1 natural (8642)
PA11 GF35
AKROMID® NEXT U28 GF 35 1 natural (8642) - PA11 made of renewable raw materials, low density, high ductility
8.200MPa
130MPa
100kJ/m²
AKROMID® NEXT U28 GF 35 1 natural (8642) - PA11 made of renewable raw materials, low density, high ductility
AKROMID®
B3 GF 40 5 black (8636)
PA6 GF40
AKROMID® B3 GF 40 5 black (8636) - PA6, 40% GF, high heat stabilised, UV stabilised, technical parts in industrial engineering, automotive industry, agriculture.
12.500MPa
200MPa
95kJ/m²
AKROMID® B3 GF 40 5 black (8636) - PA6, 40% GF, high heat stabilised, UV stabilised, technical parts in industrial engineering, automotive industry, agriculture.
AKROTEK®
PK-VM M 7 natural (8858)
PK M7
AKROTEK® PK-VM M 7 natural (8858) - 7 % mineral reinforced Polyketon, high flowability and good weldline perfomance.
2.700MPa
65MPa
120kJ/m²
AKROTEK® PK-VM M 7 natural (8858) - 7 % mineral reinforced Polyketon, high flowability and good weldline perfomance.
AKROMID®
A3 GF 35 1 HU black (8417)
PA66 GF35
AKROMID® A3 GF 35 1 HU black (8417) - PA 6.6, 35% glass fibre, heat ageing resistant, high rigidity and strength, very good flowability, UL listed HB.
12.000MPa
215MPa
75kJ/m²
AKROMID® A3 GF 35 1 HU black (8417) - PA 6.6, 35% glass fibre, heat ageing resistant, high rigidity and strength, very good flowability, UL listed HB.
AKROTEK®
PK-VM GF 10 black (8685)
PK GF10
AKROTEK® PK-VM GF 10 black (8685) - Polyketon, 10% glass fibre reinforced, chemical and hydrolysis resistance
3.500MPa
70MPa
55kJ/m²
AKROTEK® PK-VM GF 10 black (8685) - Polyketon, 10% glass fibre reinforced, chemical and hydrolysis resistance
AKROMID®
S3 GF 15 5 black (6062)PA610 GF15
AKROMID® S3 GF 15 5 black (6062) is a 15% glass fibre reinforced, high temperature stabilised polyamide 6.10 with average stiffness and strength and lower moisture absorption and high chemical resistance.
Properties
5.500MPa
120MPa
65kJ/m²
Sustainability
Biobased carbon content
Mechanical Properties
Tensile modulus
ISO 527-2
Tensile stress at break
ISO 527-2
Tensile strain at break
ISO 527-2
Flexural modulus
ISO 178
Flexural strength
ISO 178
Charpy impact strength
ISO 179-1/1eU
Charpy notched impact strength
ISO 179-1/1eA
Thermal Properties
Temperature of deflection under load HDT/A
ISO 75
Temperature of deflection under load HDT/C
ISO 75
Melting temperature
ISO 11357-3
Flammability
Burning rate
UL 94
Burning rate (<100 mm/min)
FMVSS 302
General properties
Density
ISO 1183
Humidity absorption
ISO 1110
Molding shrinkage
ISO 294-4
Disclaimer
All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.