Description

AKROTEKĀ®

PK-VM GF 30 natural (8661)

PK GF30

AKROTEKĀ® PK-VM GF 30 natural (8661) - Polyketon, 30% glass fiber reinforced, chemical and hydrolysis resistance

Modulus

8.300MPa

Strength

144MPa

Impact

76kJ/mĀ²

AKROTEKĀ® PK-VM GF 30 natural (8661) - Polyketon, 30% glass fiber reinforced, chemical and hydrolysis resistance

AKROLENĀ®

Preliminary

NEXT PP LGF 40 2 black (8488BMBCI)

PP LGF40

AKROLENĀ® NEXT PP LGF 40 2 black (8488BMBCI) - Polypropylene copolymer, long glass fiber, biomass-balanced, sustainable, very high stiffness and strength, UV stabilised, sports & leisure, household, industrial.

Modulus

10.100MPa

Strength

140MPa

Impact

81kJ/mĀ²

AKROLENĀ® NEXT PP LGF 40 2 black (8488BMBCI) - Polypropylene copolymer, long glass fiber, biomass-balanced, sustainable, very high stiffness and strength, UV stabilised, sports & leisure, household, industrial.

AKROMIDĀ®

Preliminary

T91 GF 30 FR natural (8667)

PPA GF30 FR(40)

AKROMIDĀ® T91 GF 30 FR natural (8667) - PA9T, flame retardant, 30% glass fiber, high stiffness, high strength, free of halogenes, good flowability, low water uptake, reflow soldering, SMT devices, E&E, automotive.

Modulus

10.500MPa

Strength

150MPa

Impact

55kJ/mĀ²

AKROMIDĀ® T91 GF 30 FR natural (8667) - PA9T, flame retardant, 30% glass fiber, high stiffness, high strength, free of halogenes, good flowability, low water uptake, reflow soldering, SMT devices, E&E, automotive.

AKROTEKĀ®

Preliminary

PK-VM GF 60 black (8689)

PK GF60

AKROTEKĀ® PK-VM GF 60 black (8689)- Polyketon, 60% glass fibre reinforced, chemical and hydrolysis resistance

Modulus

16.700MPa

Strength

170MPa

Impact

60kJ/mĀ²

AKROTEKĀ® PK-VM GF 60 black (8689)- Polyketon, 60% glass fibre reinforced, chemical and hydrolysis resistance

AKROTEKĀ®

Preliminary

PK-VM GF 10 black (8685)

PK GF10

AKROTEKĀ® PK-VM GF 10 black (8685) - Polyketon, 10% glass fibre reinforced, chemical and hydrolysis resistance

Modulus

3.500MPa

Strength

70MPa

Impact

55kJ/mĀ²

AKROTEKĀ® PK-VM GF 10 black (8685) - Polyketon, 10% glass fibre reinforced, chemical and hydrolysis resistance

AKROTEKĀ®

UL

PK-VM GF 30 7 HU black (8695)

PK GF30

AKROTEKĀ® PK-VM GF 30 7 HU black (8695) - Polyketon, 30% glass fibre reinforced, chemical and hydrolysis resistance

Modulus

8.000MPa

Strength

130MPa

Impact

65kJ/mĀ²

AKROTEKĀ® PK-VM GF 30 7 HU black (8695) - Polyketon, 30% glass fibre reinforced, chemical and hydrolysis resistance

AKROTEKĀ®

Preliminary

PK-VM M 7 natural (8858)

PK M7

AKROTEKĀ® PK-VM M 7 natural (8858) - 7 % mineral reinforced Polyketon, high flowability and good weldline perfomance.

Modulus

2.700MPa

Strength

65MPa

Impact

120kJ/mĀ²

AKROTEKĀ® PK-VM M 7 natural (8858) - 7 % mineral reinforced Polyketon, high flowability and good weldline perfomance.

154555680

AKROMIDĀ®

B3 GF 30 RM-M black (3016)PA6+X GF30

AKROMIDĀ® B3 GF 30 RM-M black (3016) is a 30% glass fiber reinforced polyamide 6 with high stiffness and strength. The material is characterised by a lower moisture uptake compared to standard PA 6 GF 30 compounds which results in less mechanical changes in the conditioned state. It is therefore perfectly suitable for components where high dimensional stability is required, e.g. in sports and leisure.

Features

reduced moisture
Sports & leisure

Properties

Modulus

11.000MPa

Strength

165MPa

Impact

70kJ/mĀ²

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
1 mm/min | conditioned
11000 MPa
7100 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
165 MPa
110 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
2,6 %
4,5 %

Flexural modulus

ISO 178

2 mm/min | d.a.m.
9600 MPa

Flexural strength

ISO 178

2 mm/min | d.a.m.
250 MPa

Flexural strain at break

ISO 178

2 mm/min | d.a.m.
3,2 %

Charpy impact strength

ISO 179-1/1eU

23Ā°C | d.a.m.
23Ā°C | conditioned
30Ā°C | d.a.m.
-
30Ā°C | conditioned
-
70 kJ/mĀ²
70 kJ/mĀ²
65 kJ/mĀ²
60 kJ/mĀ²

Charpy notched impact strength

ISO 179-1/1eA

23Ā°C | d.a.m.
23Ā°C | conditioned
30Ā°C | d.a.m.
-
30Ā°C | conditioned
-
12 kJ/mĀ²
15 kJ/mĀ²
10 kJ/mĀ²
10 kJ/mĀ²

Ball indentation hardness

ISO 2039-1

961N/30s | d.a.m.
230 MPa

Thermal Properties

Temperature of deflection under load HDT/A

ISO 75

1,8 MPa
210 Ā°C

Melting temperature

ISO 11357-3

DSC, 10K/min
222 Ā°C

Flammability

Burning rate

UL 94

0,8 mm Wall thickness
1,6 mm Wall thickness
3,2 mm Wall thickness
HB Class
HB Class
HB Class

Burning rate (<100 mm/min)

FMVSS 302

> 1 mm Thickness
+

General properties

Density

ISO 1183

23Ā°C
1,41 g/cmĀ³

Humidity absorption

ISO 1110

70Ā°C, 62% r.H.
1,5 - 1,7 %

Molding shrinkage

ISO 294-4

flow
transverse
0,1 - 0,3 %
0,5 - 0,7 %

Electrical Properties

Comparative tracking index

IEC 60112

Test liquid A
> 600 V

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKROĀ®, AKROMIDĀ®, AKROLENĀ®, AKROLOYĀ®, AKROTEKĀ®, ICXĀ® and PRECITEĀ® are registered trademarks of the Feddersen Group.

Contact

Do you have any questions? We are happy to help.

Would you like to learn more about AKRO-PLASTIC GmbH? Contact us! We will be happy to help you.

Learn more