AKROMID^®

C3 GF 25 1 FR grey (8803)

PA66+PA6 GF25 FR(40)

AKROMID® C3 GF 25 1 FR grey (8803) - PA6/6.6 blend, 25% glass fiber, flame retardant, good flowability, RAL 7035, lasermarkable, high strength, UL-listed, automotive, E&E.

Modulus

9.100MPa

Strength

120MPa

Impact

46kJ/m²

AKROMID® C3 GF 25 1 FR grey (8803) - PA6/6.6 blend, 25% glass fiber, flame retardant, good flowability, RAL 7035, lasermarkable, high strength, UL-listed, automotive, E&E.

AKROMID^®

Preliminary

T91 GF 30 FR natural (8667)

PPA GF30 FR(40)

AKROMID® T91 GF 30 FR natural (8667) - PA9T, flame retardant, 30% glass fiber, high stiffness, high strength, free of halogenes, good flowability, low water uptake, reflow soldering, SMT devices, E&E, automotive.

Modulus

10.500MPa

Strength

150MPa

Impact

55kJ/m²

AKROTEK^®

PK-VM GF 30 natural (8661)

PK GF30

AKROTEK® PK-VM GF 30 natural (8661) - Polyketon, 30% glass fiber reinforced, chemical and hydrolysis resistance

Modulus

8.300MPa

Strength

144MPa

Impact

76kJ/m²

AKROTEK® PK-VM GF 30 natural (8661) - Polyketon, 30% glass fiber reinforced, chemical and hydrolysis resistance

AKROTEK^®

Preliminary

PK-VM GF 10 black (8685)

PK GF10

AKROTEK® PK-VM GF 10 black (8685) - Polyketon, 10% glass fibre reinforced, chemical and hydrolysis resistance

Modulus

3.500MPa

Strength

70MPa

Impact

55kJ/m²

AKROTEK® PK-VM GF 10 black (8685) - Polyketon, 10% glass fibre reinforced, chemical and hydrolysis resistance

AKROMID^®

A3 GF 35 1 HU black (8417)

PA66 GF35

AKROMID® A3 GF 35 1 HU black (8417) - PA 6.6, 35% glass fibre, heat ageing resistant, high rigidity and strength, very good flowability, UL listed HB.

Modulus

12.000MPa

Strength

215MPa

Impact

75kJ/m²

AKROMID® A3 GF 35 1 HU black (8417) - PA 6.6, 35% glass fibre, heat ageing resistant, high rigidity and strength, very good flowability, UL listed HB.

AKROLEN^®

Preliminary

NEXT PP LGF 40 2 black (8488BMBCI)

PP LGF40

AKROLEN® NEXT PP LGF 40 2 black (8488BMBCI) - Polypropylene copolymer, long glass fiber, biomass-balanced, sustainable, very high stiffness and strength, UV stabilised, sports & leisure, household, industrial.

Modulus

10.100MPa

Strength

140MPa

Impact

81kJ/m²

AKROMID^®

Preliminary

NEXT U28 GF 35 1 natural (8642)

PA11 GF35

AKROMID® NEXT U28 GF 35 1 natural (8642) - PA11 made of renewable raw materials, low density, high ductility

Modulus

8.200MPa

Strength

130MPa

Impact

100kJ/m²

AKROMID® NEXT U28 GF 35 1 natural (8642) - PA11 made of renewable raw materials, low density, high ductility

1 53 54 5580

AKROMID^®

B3 GF 30 1 natural (2464)PA6 GF30

AKROMID® B3 GF 30 1 natural (2464) is a 30% glass fiber reinforced polyamide 6. It is characterised by a high stiffness and strength. Furthermore, the material is heat stabilised and therefore perfectly suitable for technical parts in industrial engineering and in the automotive industry. The material has a light inherent color.

Features

heat stabilised 130

Properties

Modulus

10.300MPa

Strength

185MPa

Impact

95kJ/m²

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.

1 mm/min | conditioned

10300 MPa

6200 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.

5 mm/min | conditioned

185 MPa

110 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.

5 mm/min | conditioned

3 %

5,5 %

Flexural modulus

ISO 178

2 mm/min | d.a.m.

2 mm/min | conditioned

9200 MPa

5800 MPa

Flexural strength

ISO 178

2 mm/min | d.a.m.

2 mm/min | conditioned

270 MPa

175 MPa

Flexural strain at break

ISO 178

2 mm/min | d.a.m.

2 mm/min | conditioned

3,7 %

5,6 %

Charpy impact strength

ISO 179-1/1eU

23°C | d.a.m.

23°C | conditioned

30°C | d.a.m.

95 kJ/m²

105 kJ/m²

85 kJ/m²

Charpy notched impact strength

ISO 179-1/1eA

23°C | d.a.m.

23°C | conditioned

30°C | d.a.m.

13 kJ/m²

18 kJ/m²

12 kJ/m²

Izod notched impact strength

ISO 180/1A

23°C | d.a.m.

14 kJ/m²

Ball indentation hardness

ISO 2039-1

961N/30s | d.a.m.

230 MPa

Thermal Properties

Temperature of deflection under load HDT/A

ISO 75

1,8 MPa

210 °C

Temperature of deflection under load HDT/B

ISO 75

0,45 MPa

220 °C

Temperature of deflection under load HDT/C

ISO 75

8 MPa

150 °C

Melting temperature

ISO 11357-3

DSC, 10K/min

220 °C

Coefficient of linear thermal expansion

ISO 11359-1/2

23°C to 80°C | parallel

23°C to 80°C | transverse

0,16 10⁻⁴/K

0,95 10⁻⁴/K

Temperature index for 50% loss of tensile strength

IEC 60216

5.000 h

20.000 h

160 - 175 °C

130 - 150 °C

Flammability

Burning rate

UL 94

0,8 mm Wall thickness

HB Class

GWFI

IEC 60695-2-12

1,6 mm Wall thickness

650 °C

Burning rate (<100 mm/min)

FMVSS 302

> 1 mm Thickness

General properties

Density

ISO 1183

23°C

1,36 g/cm³

Humidity absorption

ISO 1110

70°C, 62% r.H.

2,1 - 2,3 %

Water absorption

ISO 62

23°C, saturated

6,3 - 6,9 %

Molding shrinkage

ISO 294-4

flow

transverse

0,1 - 0,3 %

0,5 - 0,7 %

Electrical Properties

Volume resistivity IEC

DIN EN IEC 62631-3-2

d.a.m.

conditioned

10¹³ Ω x cm

10¹⁰ Ω x cm

Surface resistivity

DIN EN 62631-3-2

d.a.m.

conditioned

10¹² Ω

10¹⁰ Ω

Comparative tracking index

IEC 60112

Test liquid A

600 V

Rheological Properties

Flowability

AKRO

2 mm Thickness

480 mm

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.

Find the right compound

B3 GF 30 1 natural (2464)PA6 GF30

Mechanical Properties

Tensile modulus

Tensile stress at break

Tensile strain at break

Flexural modulus

Flexural strength

Flexural strain at break

Charpy impact strength

Charpy notched impact strength

Izod notched impact strength

Ball indentation hardness

Thermal Properties

Temperature of deflection under load HDT/A

Temperature of deflection under load HDT/B

Temperature of deflection under load HDT/C

Melting temperature

Coefficient of linear thermal expansion

Temperature index for 50% loss of tensile strength

Flammability

Burning rate

GWFI

Burning rate (<100 mm/min)

General properties

Density

Humidity absorption

Water absorption

Molding shrinkage

Electrical Properties

Volume resistivity IEC

Surface resistivity

Comparative tracking index

Rheological Properties

Flowability

Do you have any questions? We are happy to help.

Find the right compound

B3 GF 30 1 natural (2464).css-117ixes{line-height:1.5;display:block;margin-top:var(--chakra-space-2);font-weight:var(--chakra-fontWeights-normal);font-size:var(--chakra-fontSizes-sm);color:var(--chakra-colors-kisPrimaryTextLight-700);}PA6 GF30

Mechanical Properties

Tensile modulus

Tensile stress at break

Tensile strain at break

Flexural modulus

Flexural strength

Flexural strain at break

Charpy impact strength

Charpy notched impact strength

Izod notched impact strength

Ball indentation hardness

Thermal Properties

Temperature of deflection under load HDT/A

Temperature of deflection under load HDT/B

Temperature of deflection under load HDT/C

Melting temperature

Coefficient of linear thermal expansion

Temperature index for 50% loss of tensile strength

Flammability

Burning rate

GWFI

Burning rate (<100 mm/min)

General properties

Density

Humidity absorption

Water absorption

Molding shrinkage

Electrical Properties

Volume resistivity IEC

Surface resistivity

Comparative tracking index

Rheological Properties

Flowability

Do you have any questions? We are happy to help.