HEADER Granulat 1920x700

Find the right compound

Select your fitting and find the right compound for your intend

Tensile Modulusin MPa
Tensile Strengthin MPa
Charpy impact strengthin kJ/m²
558 Compounds found
Recommended  
Tensile Modulus
Tensile Strength
Charpy impact strength
Description

AKROMID®

Preliminary

B3 S1 natural (7748)

PA6-I

AKROMID® B3 S1 natural (7748) is an unreinforced, cold impact strength polyamide 6

Modulus

1.350MPa

Strength

35MPa

Impact

180kJ/m²

AKROMID® B3 S1 natural (7748) is an unreinforced, cold impact strength polyamide 6

AKROMID®

UL
Preliminary

A3 GF 50 8 HU black (8116)

PA66 GF50

AKROMID® A3 GF 50 8 HU black (8116) - PA 6.6, 50% glass fibre, heat ageing resistant, high rigidity and strength, UL HB all colors listed, NSF 61, WRAS, EU10/2011

Modulus

17.400MPa

Strength

265MPa

Impact

115kJ/m²

AKROMID® A3 GF 50 8 HU black (8116) - PA 6.6, 50% glass fibre, heat ageing resistant, high rigidity and strength, UL HB all colors listed, NSF 61, WRAS, EU10/2011

AKROLOY®

PA GF 30 black (2718)

PA66+PA6I/6T

AKROLOY® PA GF 30 black (2718) is a 30% glass fibre reinforced, semi-aromatic polyamide blend with high stiffness and strength, even in conditioned state. The advanced version of this Product is AKROLOY® PA GF 30 black (6415) with a modern stabilization technology, featuring improved weld-line strength and an even wider process window.

Modulus

10.500MPa

Strength

210MPa

Impact

80kJ/m²

AKROLOY® PA GF 30 black (2718) is a 30% glass fibre reinforced, semi-aromatic polyamide blend with high stiffness and strength, even in conditioned state. The advanced version of this Product is AKROLOY® PA GF 30 black (6415) with a modern stabilization technology, featuring improved weld-line strength and an even wider process window.

AKROMID®

B3 GF 30 2 RM-D black (3424)

PA6+ABS GF30

AKROMID® B3 GF 30 2 RM-D black (3424) is a 30% glass fibre reinforced, UV-stabilised polyamide 6 with limited moisture absorption.

Modulus

9.300MPa

Strength

145MPa

Impact

55kJ/m²

AKROMID® B3 GF 30 2 RM-D black (3424) is a 30% glass fibre reinforced, UV-stabilised polyamide 6 with limited moisture absorption.

AKROTEK®

Preliminary

PK-VM GF 10 black (8685)

PK GF10

AKROTEK® PK-VM GF 10 black (8685) - Polyketon, 10% glass fibre reinforced, chemical and hydrolysis resistance

Modulus

3.500MPa

Strength

70MPa

Impact

55kJ/m²

AKROTEK® PK-VM GF 10 black (8685) - Polyketon, 10% glass fibre reinforced, chemical and hydrolysis resistance

AKROTEK®

UL

PK-VM GF 30 7 HU black (8695)

PK GF30

AKROTEK® PK-VM GF 30 7 HU black (8695) - Polyketon, 30% glass fibre reinforced, chemical and hydrolysis resistance

Modulus

8.000MPa

Strength

130MPa

Impact

65kJ/m²

AKROTEK® PK-VM GF 30 7 HU black (8695) - Polyketon, 30% glass fibre reinforced, chemical and hydrolysis resistance

AKROMID®

Preliminary

B3 GF 40 5 black (8725)

PA6 GF40

AKROMID® B3 GF 40 5 black (8725) - PA6, 40% GF, high heat stabilised, UV stabilised, technical parts in industrial engineering, automotive industry, agriculture.

Modulus

12.500MPa

Strength

200MPa

Impact

95kJ/m²

AKROMID® B3 GF 40 5 black (8725) - PA6, 40% GF, high heat stabilised, UV stabilised, technical parts in industrial engineering, automotive industry, agriculture.

152535480

AKROMID®

Preliminary

B3 GF 40 S1 black (8647)PA6-I GF40

EXPERIMENTAL GRADE AKROMID® B3 GF 40 S1 black (8647) is a 40% glass fiber reinforced, impact modified polyamide 6. It is characterised by a high cold impact a very high stiffness and strength. The material is perfectly suitable for safety-related parts in the automotive interior.

Features

impact modified
reduced density

Properties

Modulus

11.000MPa

Strength

175MPa

Impact

105kJ/m²

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
1 mm/min | conditioned
11000 MPa
7200 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
175 MPa
125 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
4,5 %
8 %

Charpy impact strength

ISO 179-1/1eU

23°C | d.a.m.
23°C | conditioned
30°C | d.a.m.
-
30°C | conditioned
-
40°C | d.a.m.
-
40°C | conditioned
-
105 kJ/m²
125 kJ/m²
120 kJ/m²
120 kJ/m²
120 kJ/m²
120 kJ/m²

Charpy notched impact strength

ISO 179-1/1eA

23°C | d.a.m.
23°C | conditioned
30°C | d.a.m.
-
30°C | conditioned
-
40°C | d.a.m.
-
40°C | conditioned
-
26 kJ/m²
38 kJ/m²
20 kJ/m²
20 kJ/m²
20 kJ/m²
20 kJ/m²

Thermal Properties

Temperature of deflection under load HDT/A

ISO 75

1,8 MPa
205 °C

Melting temperature

ISO 11357-3

DSC, 10K/min
220 °C

Flammability

Burning rate

UL 94

1,6 mm Wall thickness
HB Class

General properties

Density

ISO 1183

23°C
1,42 g/cm³

Humidity absorption

ISO 1110

70°C, 62% r.H.
1,5 %

Molding shrinkage

ISO 294-4

flow
transverse
0.25 - 0.45 %
0.7 - 0.9 %

Electrical Properties

Volume resistivity IEC

DIN EN IEC 62631-3-2

d.a.m.
1013 Ω x cm

Rheological Properties

Flowability

AKRO

1 mm Thickness
2 mm Thickness
100 mm
310 mm

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.