HEADER Granulat 1920x700

Find the right compound

Select your fitting and find the right compound for your intend

Tensile Modulusin MPa
Tensile Strengthin MPa
Charpy impact strengthin kJ/mĀ²
558 Compounds found
Recommended Ā 
Tensile Modulus
Tensile Strength
Charpy impact strength
Description

AKROMIDĀ®

T5 GF 50 natural (7834)

PPA GF50

AKROMIDĀ® T5 GF 50 natural (7834) - 50% glass fibre reinforced with high stiffness and strength, high temperature resistance, e.g. under the hood applications

Modulus

18.500MPa

Strength

275MPa

Impact

95kJ/mĀ²

AKROMIDĀ® T5 GF 50 natural (7834) - 50% glass fibre reinforced with high stiffness and strength, high temperature resistance, e.g. under the hood applications

AKROMIDĀ®

Preliminary

T9 GF 30 grey (8134)

PPA GF30

AKROMIDĀ® T9 GF 30 grey (8134) - PPA, 50% glass fiber, high stiffness and strength, high temperature and chemical resistance, grey RAL 7047, E&E.

Modulus

10.000MPa

Strength

190MPa

Impact

70kJ/mĀ²

AKROMIDĀ® T9 GF 30 grey (8134) - PPA, 50% glass fiber, high stiffness and strength, high temperature and chemical resistance, grey RAL 7047, E&E.

AKROMIDĀ®

UL

A3 GF 35 1 HU black (8417)

PA66 GF35

AKROMIDĀ® A3 GF 35 1 HU black (8417) - PA 6.6, 35% glass fibre, heat ageing resistant, high rigidity and strength, very good flowability, UL listed HB.

Modulus

12.000MPa

Strength

215MPa

Impact

75kJ/mĀ²

AKROMIDĀ® A3 GF 35 1 HU black (8417) - PA 6.6, 35% glass fibre, heat ageing resistant, high rigidity and strength, very good flowability, UL listed HB.

AKROLENĀ®

Preliminary

NEXT PP LGF 40 2 black (8488BMBCI)

PP LGF40

AKROLENĀ® NEXT PP LGF 40 2 black (8488BMBCI) - Polypropylene copolymer, long glass fiber, biomass-balanced, sustainable, very high stiffness and strength, UV stabilised, sports & leisure, household, industrial.

Modulus

10.100MPa

Strength

140MPa

Impact

81kJ/mĀ²

AKROLENĀ® NEXT PP LGF 40 2 black (8488BMBCI) - Polypropylene copolymer, long glass fiber, biomass-balanced, sustainable, very high stiffness and strength, UV stabilised, sports & leisure, household, industrial.

AKROMIDĀ®

Preliminary

B3 GF 50 ECO black (7926)

PA6 GF50

AKROMIDĀ® B3 GF 50 ECO black (7926) - PA 6, GF 50, high strength, high stiffness, heat stabilised, recycled, Co2 reduction, sustainable.

Modulus

16.000MPa

Strength

200MPa

Impact

95kJ/mĀ²

AKROMIDĀ® B3 GF 50 ECO black (7926) - PA 6, GF 50, high strength, high stiffness, heat stabilised, recycled, Co2 reduction, sustainable.

AKROMIDĀ®

B3 1 S3 black (7956)

PA6-I

AKROMIDĀ® B3 1 S3 black (7956) - PA 6 unreinforced, impact modified whilst maintaining good flowability, for connecting and fixing systems

Modulus

2.200MPa

Strength

55MPa

Impact

180kJ/mĀ²

AKROMIDĀ® B3 1 S3 black (7956) - PA 6 unreinforced, impact modified whilst maintaining good flowability, for connecting and fixing systems

AKROMIDĀ®

Preliminary

B3 GF 40 5 black (8726)

PA6 GF40

AKROMIDĀ® B3 GF 40 5 black (8726) - PA6, 40% GF, high heat stabilised, UV stabilised, technical parts in industrial engineering, automotive industry, agriculture.

Modulus

12.500MPa

Strength

200MPa

Impact

95kJ/mĀ²

AKROMIDĀ® B3 GF 40 5 black (8726) - PA6, 40% GF, high heat stabilised, UV stabilised, technical parts in industrial engineering, automotive industry, agriculture.

152535480

AKROMIDĀ®

B28 GF 30 6 LT black (6931)PA6 GF30

AKROMIDĀ® B28 GF 30 6 LT black (6931) is a 30% glass fibre reinforced, easy flowing Polyamide 6. The material is characterised by high stiffness and strength. Furthermore, it is high heat stabilised and therefore perfectly suitable for automotive and industrial applications. The compound can be welded via laser welding.

Features

heat stabilised 160
laser transparent

Properties

Modulus

9.800MPa

Strength

185MPa

Impact

90kJ/mĀ²

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
1 mm/min | conditioned
9800 MPa
6400 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
185 MPa
100 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
3 %
5,5 %

Flexural modulus

ISO 178

2 mm/min | d.a.m.
8000 MPa

Flexural strength

ISO 178

2 mm/min | d.a.m.
250 MPa

Charpy impact strength

ISO 179-1/1eU

23Ā°C | d.a.m.
90 kJ/mĀ²

Charpy notched impact strength

ISO 179-1/1eA

23Ā°C | d.a.m.
12 kJ/mĀ²

Thermal Properties

Temperature of deflection under load HDT/A

ISO 75

1,8 MPa
210 Ā°C

Melting temperature

ISO 11357-3

DSC, 10K/min
220 Ā°C

Flammability

Burning rate

UL 94

1,6 mm Wall thickness
HB Class

Burning rate (<100 mm/min)

FMVSS 302

> 1 mm Thickness
+

General properties

Density

ISO 1183

23Ā°C
1,35 g/cmĀ³

Humidity absorption

ISO 1110

70Ā°C, 62% r.H.
2,1 - 2,3 %

Molding shrinkage

ISO 294-4

flow
transverse
0,1 - 0,3 %
0,5 - 0,7 %

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKROĀ®, AKROMIDĀ®, AKROLENĀ®, AKROLOYĀ®, AKROTEKĀ®, ICXĀ® and PRECITEĀ® are registered trademarks of the Feddersen Group.