AKROMID^®

B3 S1 natural (7748)

PA6-I

AKROMID® B3 S1 natural (7748) is an unreinforced, cold impact strength polyamide 6

Modulus

1.350MPa

Strength

35MPa

Impact

180kJ/m²

AKROMID® B3 S1 natural (7748) is an unreinforced, cold impact strength polyamide 6

AKROMID^®

Preliminary

A3 GF 50 8 HU black (8116)

PA66 GF50

AKROMID® A3 GF 50 8 HU black (8116) - PA 6.6, 50% glass fibre, heat ageing resistant, high rigidity and strength, UL HB all colors listed, NSF 61, WRAS, EU10/2011

Modulus

17.400MPa

Strength

265MPa

Impact

115kJ/m²

AKROMID® A3 GF 50 8 HU black (8116) - PA 6.6, 50% glass fibre, heat ageing resistant, high rigidity and strength, UL HB all colors listed, NSF 61, WRAS, EU10/2011

AKROLOY^®

PA GF 30 black (2718)

PA66+PA6I/6T

AKROLOY® PA GF 30 black (2718) is a 30% glass fibre reinforced, semi-aromatic polyamide blend with high stiffness and strength, even in conditioned state. The advanced version of this Product is AKROLOY® PA GF 30 black (6415) with a modern stabilization technology, featuring improved weld-line strength and an even wider process window.

Modulus

10.500MPa

Strength

210MPa

Impact

80kJ/m²

AKROMID^®

B3 GF 30 2 RM-D black (3424)

PA6+ABS GF30

AKROMID® B3 GF 30 2 RM-D black (3424) is a 30% glass fibre reinforced, UV-stabilised polyamide 6 with limited moisture absorption.

Modulus

9.300MPa

Strength

145MPa

Impact

55kJ/m²

AKROMID® B3 GF 30 2 RM-D black (3424) is a 30% glass fibre reinforced, UV-stabilised polyamide 6 with limited moisture absorption.

AKROTEK^®

Preliminary

PK-VM GF 10 black (8685)

PK GF10

AKROTEK® PK-VM GF 10 black (8685) - Polyketon, 10% glass fibre reinforced, chemical and hydrolysis resistance

Modulus

3.500MPa

Strength

70MPa

Impact

55kJ/m²

AKROTEK® PK-VM GF 10 black (8685) - Polyketon, 10% glass fibre reinforced, chemical and hydrolysis resistance

AKROTEK^®

PK-VM GF 30 7 HU black (8695)

PK GF30

AKROTEK® PK-VM GF 30 7 HU black (8695) - Polyketon, 30% glass fibre reinforced, chemical and hydrolysis resistance

Modulus

8.000MPa

Strength

130MPa

Impact

65kJ/m²

AKROTEK® PK-VM GF 30 7 HU black (8695) - Polyketon, 30% glass fibre reinforced, chemical and hydrolysis resistance

AKROMID^®

Preliminary

B3 GF 40 5 black (8725)

PA6 GF40

AKROMID® B3 GF 40 5 black (8725) - PA6, 40% GF, high heat stabilised, UV stabilised, technical parts in industrial engineering, automotive industry, agriculture.

Modulus

12.500MPa

Strength

200MPa

Impact

95kJ/m²

AKROMID® B3 GF 40 5 black (8725) - PA6, 40% GF, high heat stabilised, UV stabilised, technical parts in industrial engineering, automotive industry, agriculture.

1 52 53 5480

AKROMID^®

T5 GF 50 black (6247)PPA GF50

AKROMID® T5 GF 50 black (6247) is a 50% glass fibre reinforced polyphthalamide. It is characterised by its very high stiffness and strength, even at elevated temperatures up to 120°C. Due to its low moisture absorption, the mechanical properties remain nearly unchanged even in conditioned state. Not only the good creep resistance, but also the hydrolysis and chemical resistance complement the property profile and make it the material of your choice for under the hood applications and connectors with special strength requirements.

Features

heat stabilised 160

hydrolysis / chemically stabilised

reduced moisture

metal substitution

Properties

Modulus

19.000MPa

Strength

275MPa

Impact

90kJ/m²

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.

1 mm/min | conditioned

19000 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.

5 mm/min | conditioned

275 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.

5 mm/min | conditioned

2,2 %

Poisson´s ratio

ISO 527-2

0,05% - 0,25% | d.a.m.

0,42

Flexural modulus

ISO 178

2 mm/min | d.a.m.

2 mm/min | conditioned

19000 MPa

Flexural strength

ISO 178

2 mm/min | d.a.m.

2 mm/min | conditioned

440 MPa

380 MPa

Flexural strain at break

ISO 178

2 mm/min | d.a.m.

2 mm/min | conditioned

2,6 %

Charpy impact strength

ISO 179-1/1eU

23°C | d.a.m.

23°C | conditioned

30°C | d.a.m.

30°C | conditioned

40°C | d.a.m.

40°C | conditioned

90 kJ/m²

83 kJ/m²

75 kJ/m²

70 kJ/m²

65 kJ/m²

Charpy notched impact strength

ISO 179-1/1eA

23°C | d.a.m.

23°C | conditioned

30°C | d.a.m.

30°C | conditioned

40°C | d.a.m.

40°C | conditioned

13 kJ/m²

12 kJ/m²

11 kJ/m²

12 kJ/m²

11 kJ/m²

Thermal Properties

Temperature of deflection under load HDT/A

ISO 75

1,8 MPa

280 °C

Temperature of deflection under load HDT/B

ISO 75

0,45 MPa

> 280 °C

Temperature of deflection under load HDT/C

ISO 75

8 MPa

237 °C

Glass transition temperature

ISO 11357-2

DSC, 2nd heating

135 °C

Melting temperature

ISO 11357-3

DSC, 10K/min

325 °C

Coefficient of linear thermal expansion

ISO 11359-1/2

23°C to 80°C | parallel

23°C to 80°C | transverse

0,14 10⁻⁴/K

0,47 10⁻⁴/K

Temperature index for 50% loss of tensile strength

IEC 60216

20.000 h

155 °C

Flammability

Burning rate

UL 94

1,6 mm Wall thickness

HB Class

Burning rate (<100 mm/min)

FMVSS 302

> 1 mm Thickness

General properties

Density

ISO 1183

23°C

1,65 g/cm³

Humidity absorption

ISO 1110

70°C, 62% r.H.

0,8 %

Molding shrinkage

ISO 294-4

flow

transverse

0,1 - 0,3 %

0,4 - 0,6 %

Electrical Properties

Comparative tracking index

IEC 60112

Test liquid A

600 V

Rheological Properties

Flowability

AKRO

1 mm Thickness

2 mm Thickness

100 mm

280 mm

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.

Find the right compound

T5 GF 50 black (6247)PPA GF50

Mechanical Properties

Tensile modulus

Tensile stress at break

Tensile strain at break

Poisson´s ratio

Flexural modulus

Flexural strength

Flexural strain at break

Charpy impact strength

Charpy notched impact strength

Thermal Properties

Temperature of deflection under load HDT/A

Temperature of deflection under load HDT/B

Temperature of deflection under load HDT/C

Glass transition temperature

Melting temperature

Coefficient of linear thermal expansion

Temperature index for 50% loss of tensile strength

Flammability

Burning rate

Burning rate (<100 mm/min)

General properties

Density

Humidity absorption

Molding shrinkage

Electrical Properties

Comparative tracking index

Rheological Properties

Flowability

Do you have any questions? We are happy to help.

Find the right compound

T5 GF 50 black (6247).css-117ixes{line-height:1.5;display:block;margin-top:var(--chakra-space-2);font-weight:var(--chakra-fontWeights-normal);font-size:var(--chakra-fontSizes-sm);color:var(--chakra-colors-kisPrimaryTextLight-700);}PPA GF50

Mechanical Properties

Tensile modulus

Tensile stress at break

Tensile strain at break

Poisson´s ratio

Flexural modulus

Flexural strength

Flexural strain at break

Charpy impact strength

Charpy notched impact strength

Thermal Properties

Temperature of deflection under load HDT/A

Temperature of deflection under load HDT/B

Temperature of deflection under load HDT/C

Glass transition temperature

Melting temperature

Coefficient of linear thermal expansion

Temperature index for 50% loss of tensile strength

Flammability

Burning rate

Burning rate (<100 mm/min)

General properties

Density

Humidity absorption

Molding shrinkage

Electrical Properties

Comparative tracking index

Rheological Properties

Flowability

Do you have any questions? We are happy to help.

T5 GF 50 black (6247)PPA GF50