Description

AKROMID®

T5 GF 50 natural (7834)

PPA GF50

AKROMID® T5 GF 50 natural (7834) - 50% glass fibre reinforced with high stiffness and strength, high temperature resistance, e.g. under the hood applications

Modulus

18.500MPa

Strength

275MPa

Impact

95kJ/m²

AKROMID® T5 GF 50 natural (7834) - 50% glass fibre reinforced with high stiffness and strength, high temperature resistance, e.g. under the hood applications

AKROMID®

Preliminary

T9 GF 30 grey (8134)

PPA GF30

AKROMID® T9 GF 30 grey (8134) - PPA, 50% glass fiber, high stiffness and strength, high temperature and chemical resistance, grey RAL 7047, E&E.

Modulus

10.000MPa

Strength

190MPa

Impact

70kJ/m²

AKROMID® T9 GF 30 grey (8134) - PPA, 50% glass fiber, high stiffness and strength, high temperature and chemical resistance, grey RAL 7047, E&E.

AKROMID®

UL

A3 GF 35 1 HU black (8417)

PA66 GF35

AKROMID® A3 GF 35 1 HU black (8417) - PA 6.6, 35% glass fibre, heat ageing resistant, high rigidity and strength, very good flowability, UL listed HB.

Modulus

12.000MPa

Strength

215MPa

Impact

75kJ/m²

AKROMID® A3 GF 35 1 HU black (8417) - PA 6.6, 35% glass fibre, heat ageing resistant, high rigidity and strength, very good flowability, UL listed HB.

AKROLEN®

Preliminary

NEXT PP LGF 40 2 black (8488BMBCI)

PP LGF40

AKROLEN® NEXT PP LGF 40 2 black (8488BMBCI) - Polypropylene copolymer, long glass fiber, biomass-balanced, sustainable, very high stiffness and strength, UV stabilised, sports & leisure, household, industrial.

Modulus

10.100MPa

Strength

140MPa

Impact

81kJ/m²

AKROLEN® NEXT PP LGF 40 2 black (8488BMBCI) - Polypropylene copolymer, long glass fiber, biomass-balanced, sustainable, very high stiffness and strength, UV stabilised, sports & leisure, household, industrial.

AKROMID®

Preliminary

B3 GF 50 ECO black (7926)

PA6 GF50

AKROMID® B3 GF 50 ECO black (7926) - PA 6, GF 50, high strength, high stiffness, heat stabilised, recycled, Co2 reduction, sustainable.

Modulus

16.000MPa

Strength

200MPa

Impact

95kJ/m²

AKROMID® B3 GF 50 ECO black (7926) - PA 6, GF 50, high strength, high stiffness, heat stabilised, recycled, Co2 reduction, sustainable.

AKROMID®

B3 1 S3 black (7956)

PA6-I

AKROMID® B3 1 S3 black (7956) - PA 6 unreinforced, impact modified whilst maintaining good flowability, for connecting and fixing systems

Modulus

2.200MPa

Strength

55MPa

Impact

180kJ/m²

AKROMID® B3 1 S3 black (7956) - PA 6 unreinforced, impact modified whilst maintaining good flowability, for connecting and fixing systems

AKROMID®

Preliminary

B3 GF 40 5 black (8726)

PA6 GF40

AKROMID® B3 GF 40 5 black (8726) - PA6, 40% GF, high heat stabilised, UV stabilised, technical parts in industrial engineering, automotive industry, agriculture.

Modulus

12.500MPa

Strength

200MPa

Impact

95kJ/m²

AKROMID® B3 GF 40 5 black (8726) - PA6, 40% GF, high heat stabilised, UV stabilised, technical parts in industrial engineering, automotive industry, agriculture.

152535480

AKROMID®

B3 ICF 10 black (5118)PA6 CF10

AKROMID® B3 ICF 10 black (5118) is a 10% carbon fibre reinforced polyamide 6 with high flexural strength and good sliding properties

Properties

Modulus

8.000MPa

Strength

120MPa

Impact

50kJ/m²

Sustainability

Recycled content

10 %

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
1 mm/min | conditioned
8000 MPa
3200 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
120 MPa
52 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
4 %
12 %

Flexural modulus

ISO 178

2 mm/min | d.a.m.
2 mm/min | conditioned
7000 MPa
3400 MPa

Flexural strength

ISO 178

2 mm/min | d.a.m.
2 mm/min | conditioned
200 MPa
100 MPa

Flexural strain at break

ISO 178

2 mm/min | d.a.m.
2 mm/min | conditioned
4,5 %
7 %

Charpy impact strength

ISO 179-1/1eU

23°C | d.a.m.
23°C | conditioned
30°C | d.a.m.
-
50 kJ/m²
95 kJ/m²
37 kJ/m²

Charpy notched impact strength

ISO 179-1/1eA

23°C | d.a.m.
23°C | conditioned
30°C | d.a.m.
-
4 kJ/m²
9 kJ/m²
3 kJ/m²

Thermal Properties

Temperature of deflection under load HDT/A

ISO 75

1,8 MPa
188 °C

Melting temperature

ISO 11357-3

DSC, 10K/min
220 °C

Flammability

Burning rate

UL 94

1,6 mm Wall thickness
HB Class

General properties

Density

ISO 1183

23°C
1,17 g/cm³

Humidity absorption

ISO 1110

70°C, 62% r.H.
2,9 %

Molding shrinkage

ISO 294-4

flow
transverse
0,3 - 0,5 %
0,6 - 0,8 %

Electrical Properties

Surface resistivity

DIN EN 62631-3-2

d.a.m.
1011 Ω

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.

Contact

Do you have any questions? We are happy to help.

Would you like to learn more about AKRO-PLASTIC GmbH? Contact us! We will be happy to help you.

Learn more