HEADER Granulat 1920x700

Find the right compound

Select your fitting and find the right compound for your intend

Tensile Modulusin MPa
Tensile Strengthin MPa
Charpy impact strengthin kJ/m²
558 Compounds found
Recommended  
Tensile Modulus
Tensile Strength
Charpy impact strength
Description

AKROMID®

UL

A3 GF 30 HU grey (6600)

PA66 GF30

AKROMID® A3 GF 30 HU grey (6600) is a 30% glass fibre reinforced, heat stabilised polyamide 6.6 with high rigidity and strength, listet at UL in all colors

Modulus

10.500MPa

Strength

200MPa

Impact

85kJ/m²

AKROMID® A3 GF 30 HU grey (6600) is a 30% glass fibre reinforced, heat stabilised polyamide 6.6 with high rigidity and strength, listet at UL in all colors

AKROMID®

UL

B3 1 FR black (6580)

PA6 FR(30)

AKROMID® B3 1 FR black (6580) - PA6, unreinforced, flame retardant, UL-listed, good surface, public transportation, new mobility.

Modulus

3.600MPa

Strength

75MPa

Impact

78kJ/m²

AKROMID® B3 1 FR black (6580) - PA6, unreinforced, flame retardant, UL-listed, good surface, public transportation, new mobility.

AKROMID®

Preliminary

T5 GF 40 6 natural (8003)

PPA GF40

AKROMID® T5 GF 40 6 natural (8003) - 40% glass fibre reinforced with high stiffness and strength, high temperature resistance, e.g. under the hood applications

Modulus

16.000MPa

Strength

245MPa

Impact

80kJ/m²

AKROMID® T5 GF 40 6 natural (8003) - 40% glass fibre reinforced with high stiffness and strength, high temperature resistance, e.g. under the hood applications

AKROLEN®

Preliminary

NEXT PP LGF 40 2 black (8488BMBCI)

PP LGF40

AKROLEN® NEXT PP LGF 40 2 black (8488BMBCI) - Polypropylene copolymer, long glass fiber, biomass-balanced, sustainable, very high stiffness and strength, UV stabilised, sports & leisure, household, industrial.

Modulus

10.100MPa

Strength

140MPa

Impact

81kJ/m²

AKROLEN® NEXT PP LGF 40 2 black (8488BMBCI) - Polypropylene copolymer, long glass fiber, biomass-balanced, sustainable, very high stiffness and strength, UV stabilised, sports & leisure, household, industrial.

AKROTEK®

Preliminary

PK-VM GF 10 black (8685)

PK GF10

AKROTEK® PK-VM GF 10 black (8685) - Polyketon, 10% glass fibre reinforced, chemical and hydrolysis resistance

Modulus

3.500MPa

Strength

70MPa

Impact

55kJ/m²

AKROTEK® PK-VM GF 10 black (8685) - Polyketon, 10% glass fibre reinforced, chemical and hydrolysis resistance

AKROMID®

Preliminary

NEXT U28 GF 35 1 natural (8642)

PA11 GF35

AKROMID® NEXT U28 GF 35 1 natural (8642) - PA11 made of renewable raw materials, low density, high ductility

Modulus

8.200MPa

Strength

130MPa

Impact

100kJ/m²

AKROMID® NEXT U28 GF 35 1 natural (8642) - PA11 made of renewable raw materials, low density, high ductility

AKROMID®

Preliminary

B3 GF 40 5 black (8726)

PA6 GF40

AKROMID® B3 GF 40 5 black (8726) - PA6, 40% GF, high heat stabilised, UV stabilised, technical parts in industrial engineering, automotive industry, agriculture.

Modulus

12.500MPa

Strength

200MPa

Impact

95kJ/m²

AKROMID® B3 GF 40 5 black (8726) - PA6, 40% GF, high heat stabilised, UV stabilised, technical parts in industrial engineering, automotive industry, agriculture.

152535480

AKROMID®

A3 1 L black (4652)PA66 + PP

AKROMID® A3 1 L black (4652) is an unreinforced PA6.6/PP-blend with reduced density compared to standard PA6.6. The material can be used where weight and cost reduction is required.

Features

heat stabilised 130
reduced density

Properties

Modulus

2.300MPa

Strength

54MPa

Impact

180kJ/m²

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
1 mm/min | conditioned
2300 MPa
1300 MPa

Tensile stress at yield

ISO 527-2

50 mm/min | d.a.m.
50 mm/min | conditioned
54 MPa
40 MPa

Tensile strain at break

ISO 527-2

50 mm/min | d.a.m.
50 mm/min | conditioned
30 %
> 50 %

Charpy impact strength

ISO 179-1/1eU

23°C | d.a.m.
23°C | conditioned
30°C | d.a.m.
-
30°C | conditioned
-
no break
no break
no break
no break

Charpy notched impact strength

ISO 179-1/1eA

23°C | d.a.m.
23°C | conditioned
30°C | d.a.m.
-
30°C | conditioned
-
6,5 kJ/m²
12 kJ/m²
5 kJ/m²
4 kJ/m²

Thermal Properties

Temperature of deflection under load HDT/A

ISO 75

1,8 MPa
65 °C

Temperature of deflection under load HDT/B

ISO 75

0,45 MPa
150 °C

Melting temperature

ISO 11357-3

DSC, 10K/min
262 °C

Flammability

Burning rate

UL 94

0,8 mm Wall thickness
HB Class

GWFI

IEC 60695-2-12

0,8 mm Wall thickness
750 °C

GWIT

IEC 60695-2-13

0,8 mm Wall thickness
800 °C

Burning rate (<100 mm/min)

FMVSS 302

> 1 mm Thickness
+

General properties

Density

ISO 1183

23°C
1,04 g/cm³

Humidity absorption

ISO 1110

70°C, 62% r.H.
1,7 %

Molding shrinkage

ISO 294-4

flow
transverse
2,5 %
1,8 %

Rheological Properties

MVR

ISO 1133

275°C/5kg
29 cm³/10 min

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.