AKROMIDĀ®

A3 GF 35 2 black (7226)

PA66 GF35

AKROMIDĀ® A3 GF 35 2 black (7226) - 35% glass fiber reinforced PA 6.6, UV-stabilised, technical parts in industrial engineering and automotive industry

Modulus

11.500MPa

Strength

215MPa

Impact

90kJ/mĀ²

AKROMIDĀ® A3 GF 35 2 black (7226) - 35% glass fiber reinforced PA 6.6, UV-stabilised, technical parts in industrial engineering and automotive industry

PRECITEĀ®

P3 GF 10 black (7813)

PBT GF 10

PRECITEĀ® P3 GF 10 black (7813) is a 10% glass fibre reinforced, medium viscous poly(butylene terephthalate) with medium stiffness and toughness as well as high dimensional and chemical resistance.

Modulus

4.600MPa

Strength

90MPa

Impact

25kJ/mĀ²

PRECITEĀ® P3 GF 10 black (7813) is a 10% glass fibre reinforced, medium viscous poly(butylene terephthalate) with medium stiffness and toughness as well as high dimensional and chemical resistance.

AKROMIDĀ®

B3 GF 30 2 RM-D black (3424)

PA6+ABS GF30

AKROMIDĀ® B3 GF 30 2 RM-D black (3424) is a 30% glass fibre reinforced, UV-stabilised polyamide 6 with limited moisture absorption.

Modulus

9.300MPa

Strength

145MPa

Impact

55kJ/mĀ²

AKROMIDĀ® B3 GF 30 2 RM-D black (3424) is a 30% glass fibre reinforced, UV-stabilised polyamide 6 with limited moisture absorption.

AKROMIDĀ®

C3 1 S3 black (4297)

PA66+PA6

AKROMIDĀ® C3 1 S3 black (4297) - PA 6.6/6 blend unreinforced, impact modified whilst maintaining good flowability, for connecting and fixing systems

Modulus

2.500MPa

Strength

65MPa

Impact

180kJ/mĀ²

AKROMIDĀ® C3 1 S3 black (4297) - PA 6.6/6 blend unreinforced, impact modified whilst maintaining good flowability, for connecting and fixing systems

AKROMIDĀ®

T5 GF 50 8 black (6205)

PPA GF50

AKROMIDĀ® T5 GF 50 8 black (6205) - PPA, 50% glass fiber, food contact, kitchen and household appliances, fitting, water meter, ACS, WRAS, NSF 61, EU 10/2011, FDA

Modulus

19.000MPa

Strength

270MPa

Impact

85kJ/mĀ²

AKROMIDĀ® T5 GF 50 8 black (6205) - PPA, 50% glass fiber, food contact, kitchen and household appliances, fitting, water meter, ACS, WRAS, NSF 61, EU 10/2011, FDA

AKROMIDĀ®

T5 GF 40 8 black (6458)

PPA GF40

AKROMIDĀ® T5 GF 40 8 black (6458) - PPA, 40% glass fiber, food contact, kitchen and household appliances, fitting, water meter, ACS, WRAS, NSF 61, EU 10/2011, FDA

Modulus

15.000MPa

Strength

245MPa

Impact

80kJ/mĀ²

AKROMIDĀ® T5 GF 40 8 black (6458) - PPA, 40% glass fiber, food contact, kitchen and household appliances, fitting, water meter, ACS, WRAS, NSF 61, EU 10/2011, FDA

AKROMIDĀ®

UL

B3 1 FR natural (6437)

PA6 FR(30)

AKROMIDĀ® B3 1 FR natural (6437) - PA6, unreinforced, flame retardant, UL-listed, good surface, public transportation, new mobility.

Modulus

3.500MPa

Strength

75MPa

Impact

85kJ/mĀ²

AKROMIDĀ® B3 1 FR natural (6437) - PA6, unreinforced, flame retardant, UL-listed, good surface, public transportation, new mobility.

150515280

AKROMIDĀ®

B25 GF 60 1 LA black (8281)PA6 GF60

AKROMIDĀ® B25 GF 60 1 LA black (8281) is a 60% glass fibre reinforced, slightly heat stabilised, easy flowing polyamide 6 with very high stiffness and strength, lasermarkable.

Features

laser markable
easy flow

Properties

Modulus

21.000MPa

Strength

255MPa

Impact

95kJ/mĀ²

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
1 mm/min | conditioned
21000 MPa
14200 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
255 MPa
175 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
2,4 %
4 %

Flexural modulus

ISO 178

2 mm/min | d.a.m.
20000 MPa

Flexural strength

ISO 178

2 mm/min | d.a.m.
400 MPa

Charpy impact strength

ISO 179-1/1eU

23Ā°C | d.a.m.
23Ā°C | conditioned
95 kJ/mĀ²
105 kJ/mĀ²

Charpy notched impact strength

ISO 179-1/1eA

23Ā°C | d.a.m.
23Ā°C | conditioned
20 kJ/mĀ²
26 kJ/mĀ²

Thermal Properties

Temperature of deflection under load HDT/A

ISO 75

1,8 MPa
220 Ā°C

Temperature of deflection under load HDT/B

ISO 75

0,45 MPa
220 Ā°C

Temperature of deflection under load HDT/C

ISO 75

8 MPa
190 Ā°C

Melting temperature

ISO 11357-3

DSC, 10K/min
220 Ā°C

Coefficient of linear thermal expansion

ISO 11359-1/2

23Ā°C to 80Ā°C | parallel
23Ā°C to 80Ā°C | transverse
0,13 10ā»ā“/K
0,60 10ā»ā“/K

Flammability

Burning rate

UL 94

1,6 mm Wall thickness
HB Class

GWFI

IEC 60695-2-12

1,6 mm Wall thickness
650 Ā°C

GWIT

IEC 60695-2-13

1,6 mm Wall thickness
675 Ā°C

Burning rate (<100 mm/min)

FMVSS 302

> 1 mm Thickness
+

General properties

Density

ISO 1183

23Ā°C
1,7 g/cmĀ³

Humidity absorption

ISO 1110

70Ā°C, 62% r.H.
0,9 - 1,2 %

Molding shrinkage

ISO 294-4

flow
transverse
0,1 - 0,3 %
0,3 - 0,5 %

Electrical Properties

Volume resistivity IEC

DIN EN IEC 62631-3-2

d.a.m.
conditioned
1013 ā„¦ x cm
1010 ā„¦ x cm

Surface resistivity

DIN EN 62631-3-2

d.a.m.
conditioned
1012 ā„¦
1010 ā„¦

Rheological Properties

Flowability

AKRO

1 mm Thickness
2 mm Thickness
120 mm
420 mm

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKROĀ®, AKROMIDĀ®, AKROLENĀ®, AKROLOYĀ®, AKROTEKĀ®, ICXĀ® and PRECITEĀ® are registered trademarks of the Feddersen Group.

Contact

Do you have any questions? We are happy to help.

Would you like to learn more about AKRO-PLASTIC GmbH? Contact us! We will be happy to help you.

Learn more