AKROMID®
B3 GF 50 1 grey (5507)
PA6 GF50
AKROMID® B3 GF 50 1 grey (5507) - 50% glass fiber reinforced PA 6, heat stabilised, technical parts in industrial engineering and automotive industry
16.500MPa
190MPa
70kJ/m²
AKROMID® B3 GF 50 1 grey (5507) - 50% glass fiber reinforced PA 6, heat stabilised, technical parts in industrial engineering and automotive industry
AKROMID®
B3 GF 40 5 black (7286)
PA6 GF40
AKROMID® B3 GF 40 5 black (7286) - 40% glass fiber reinforced PA 6, high heat stabilised, technical parts in industrial engineering and automotive industry
12.500MPa
200MPa
95kJ/m²
AKROMID® B3 GF 40 5 black (7286) - 40% glass fiber reinforced PA 6, high heat stabilised, technical parts in industrial engineering and automotive industry
AKROMID®
B3 S1 natural (7748)
PA6-I
AKROMID® B3 S1 natural (7748) is an unreinforced, cold impact strength polyamide 6
1.350MPa
35MPa
180kJ/m²
AKROMID® B3 S1 natural (7748) is an unreinforced, cold impact strength polyamide 6
AKROMID®
A3 GF 30 6 natural (6398)
PA66 GF30
AKROMID® A3 GF 30 6 natural (6398) is a 30% glass fibre reinforced, inorganic high heat stabilised polyamide 6.6 with high stiffness and strength
10.000MPa
200MPa
85kJ/m²
AKROMID® A3 GF 30 6 natural (6398) is a 30% glass fibre reinforced, inorganic high heat stabilised polyamide 6.6 with high stiffness and strength
AKROMID®
B3 GF 15 grey (6270)
PA6 GF15
AKROMID® B3 GF 15 grey (6270) is a 15% glass fibre reinforced polyamide 6 with average stiffness and strength.
6.000MPa
110MPa
50kJ/m²
AKROMID® B3 GF 15 grey (6270) is a 15% glass fibre reinforced polyamide 6 with average stiffness and strength.
AKROMID®
T5 ICF 20 black (6773)
PPA CF20
AKROMID® T5 ICF 20 black (6773) is a 20% carbon fibre reinforced polyphthalamide with good flexural strength and good sliding properties
18.000MPa
222MPa
37kJ/m²
AKROMID® T5 ICF 20 black (6773) is a 20% carbon fibre reinforced polyphthalamide with good flexural strength and good sliding properties
AKROMID®
A3 GM 25/15 1 black (7003)
PA66 (GF25+GB15)
AKROMID® A3 GM 25/15 1 black (7003) - 25% glass fibre, 15% glass bead, heat stabilised, polyamide 6.6, good surface, low warpage
10.000MPa
180MPa
70kJ/m²
AKROMID® A3 GM 25/15 1 black (7003) - 25% glass fibre, 15% glass bead, heat stabilised, polyamide 6.6, good surface, low warpage
AKROTEK®
PK-VM GF 10 natural (8679)PK GF10
AKROTEK® PK-VM GF 10 natural (8679) is a 10% glass fibre reinforced Polyketone with average stiffness and strength. Due to its very good media resistance, the material is suitable for use in applications that carry cooling water. This type was developed as the successor to PK-VM GF 10 natural (8534) in order to meet the requirements for a larger processing window during processing.
Features
Properties
3.600MPa
75MPa
61kJ/m²
Mechanical Properties
Tensile modulus
ISO 527-2
Tensile stress at break
ISO 527-2
Tensile strain at break
ISO 527-2
Charpy impact strength
ISO 179-1/1eU
Thermal Properties
Temperature of deflection under load HDT/A
ISO 75
Melting temperature
ISO 11357-3
Flammability
Burning rate
UL 94
Burning rate (<100 mm/min)
FMVSS 302
General properties
Humidity absorption
ISO 1110
Molding shrinkage
ISO 294-4
Disclaimer
All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.
Contact
Do you have any questions? We are happy to help.
Would you like to learn more about AKRO-PLASTIC GmbH? Contact us! We will be happy to help you.