Select your fitting and find the right compound for your intend
AKROMID®
B3 ICF 10 1 black (6194)
PA6 CF10
AKROMID® B3 ICF 10 1 black (6194) is a 10% carbon fibre reinforced, heat stabilised polyamide 6 with good sliding properties
8.500MPa
125MPa
45kJ/m²
AKROMID® B3 ICF 10 1 black (6194) is a 10% carbon fibre reinforced, heat stabilised polyamide 6 with good sliding properties
AKROMID®
S3 GF 15 5 black (6062)
PA610 GF15
AKROMID® S3 GF 15 5 black (6062) is a 15% glass fibre reinforced, high temperature stabilised polyamide 6.10 with average stiffness and strength and lower moisture absorption and high chemical resistance.
5.500MPa
120MPa
65kJ/m²
AKROMID® S3 GF 15 5 black (6062) is a 15% glass fibre reinforced, high temperature stabilised polyamide 6.10 with average stiffness and strength and lower moisture absorption and high chemical resistance.
AKROMID®
A3 GF 30 HU grey (6600)
PA66 GF30
AKROMID® A3 GF 30 HU grey (6600) is a 30% glass fibre reinforced, heat stabilised polyamide 6.6 with high rigidity and strength, listet at UL in all colors
10.500MPa
200MPa
85kJ/m²
AKROMID® A3 GF 30 HU grey (6600) is a 30% glass fibre reinforced, heat stabilised polyamide 6.6 with high rigidity and strength, listet at UL in all colors
AKROTEK®
PK-HM natural (7536)
PK
AKROTEK® PK-HM natural (7536) - Polyketon, Tribology, friction and wear, chemical resistance, extrusion
1.400MPa
60MPa
180kJ/m²
AKROTEK® PK-HM natural (7536) - Polyketon, Tribology, friction and wear, chemical resistance, extrusion
AKROMID®
T9 GF 30 S1 black (7873)
PPA-I GF30
AKROMID® T9 GF 30 S1 black (7873) is a 30% glass fibre reinforced, cold impact strength polyphthalamide with medium stiffness and strength, as well as high chemical resistance. The compound is based on PA9T and has lower moisture uptake than conventional PA6T variants. This leads to a significantly higher consistency of the glass transition temperature and higher strength at elevated temperatures especially in conditioned state.
8.700MPa
165MPa
95kJ/m²
AKROMID® T9 GF 30 S1 black (7873) is a 30% glass fibre reinforced, cold impact strength polyphthalamide with medium stiffness and strength, as well as high chemical resistance. The compound is based on PA9T and has lower moisture uptake than conventional PA6T variants. This leads to a significantly higher consistency of the glass transition temperature and higher strength at elevated temperatures especially in conditioned state.
AKROMID®
B3 S1 black (7629)
PA6-I
AKROMID® B3 S1 black (7629) - PA 6 unreinforced and cold impact modified, for furniture and cunstruction industry, sports and leisure
1.700MPa
45MPa
180kJ/m²
AKROMID® B3 S1 black (7629) - PA 6 unreinforced and cold impact modified, for furniture and cunstruction industry, sports and leisure
AKROLOY®
PA GF 60 beige (7632)
PA66+PA6I/6T GF60
AKROLOY® PA GF 60 beige(7632) is a 60% glass fibre reinforced, semi-aromatic polyamide-blend with very high stiffness and strength, even in conditioned state.
22.300MPa
265MPa
85kJ/m²
AKROLOY® PA GF 60 beige(7632) is a 60% glass fibre reinforced, semi-aromatic polyamide-blend with very high stiffness and strength, even in conditioned state.
AKROMID®
AKROMID® B3 GF 30 9 black (8643) is a 30% glass fiber reinforced polyamide 6. It is characterised by a high stiffness and strength. Furthermore, the material is heat stabilised and therefore perfectly suitable for technical parts in industrial engineering and in the automotive industry.
Features
Properties
10.000MPa
150MPa
55kJ/m²
ISO 527-2
ISO 527-2
ISO 527-2
ISO 179-1/1eU
ISO 179-1/1eA
ISO 2039-1
ISO 75
ISO 75
ISO 75
ISO 11357-3
ISO 11359-1/2
UL 94
ISO 1183
ISO 1110
ISO 62
ISO 294-4
DIN EN IEC 62631-3-2
DIN EN 62631-3-2
Disclaimer
All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.