AKROMID®

B3 GF 50 1 grey (5507)

PA6 GF50

AKROMID® B3 GF 50 1 grey (5507) - 50% glass fiber reinforced PA 6, heat stabilised, technical parts in industrial engineering and automotive industry

Modulus

16.500MPa

Strength

190MPa

Impact

70kJ/m²

AKROMID® B3 GF 50 1 grey (5507) - 50% glass fiber reinforced PA 6, heat stabilised, technical parts in industrial engineering and automotive industry

AKROMID®

B3 GF 40 5 black (7286)

PA6 GF40

AKROMID® B3 GF 40 5 black (7286) - 40% glass fiber reinforced PA 6, high heat stabilised, technical parts in industrial engineering and automotive industry

Modulus

12.500MPa

Strength

200MPa

Impact

95kJ/m²

AKROMID® B3 GF 40 5 black (7286) - 40% glass fiber reinforced PA 6, high heat stabilised, technical parts in industrial engineering and automotive industry

AKROMID®

Preliminary

B3 S1 natural (7748)

PA6-I

AKROMID® B3 S1 natural (7748) is an unreinforced, cold impact strength polyamide 6

Modulus

1.350MPa

Strength

35MPa

Impact

180kJ/m²

AKROMID® B3 S1 natural (7748) is an unreinforced, cold impact strength polyamide 6

AKROMID®

A3 GF 30 6 natural (6398)

PA66 GF30

AKROMID® A3 GF 30 6 natural (6398) is a 30% glass fibre reinforced, inorganic high heat stabilised polyamide 6.6 with high stiffness and strength

Modulus

10.000MPa

Strength

200MPa

Impact

85kJ/m²

AKROMID® A3 GF 30 6 natural (6398) is a 30% glass fibre reinforced, inorganic high heat stabilised polyamide 6.6 with high stiffness and strength

AKROMID®

B3 GF 15 grey (6270)

PA6 GF15

AKROMID® B3 GF 15 grey (6270) is a 15% glass fibre reinforced polyamide 6 with average stiffness and strength.

Modulus

6.000MPa

Strength

110MPa

Impact

50kJ/m²

AKROMID® B3 GF 15 grey (6270) is a 15% glass fibre reinforced polyamide 6 with average stiffness and strength.

AKROMID®

Preliminary

T5 ICF 20 black (6773)

PPA CF20

AKROMID® T5 ICF 20 black (6773) is a 20% carbon fibre reinforced polyphthalamide with good flexural strength and good sliding properties

Modulus

18.000MPa

Strength

222MPa

Impact

37kJ/m²

AKROMID® T5 ICF 20 black (6773) is a 20% carbon fibre reinforced polyphthalamide with good flexural strength and good sliding properties

AKROMID®

A3 GM 25/15 1 black (7003)

PA66 (GF25+GB15)

AKROMID® A3 GM 25/15 1 black (7003) - 25% glass fibre, 15% glass bead, heat stabilised, polyamide 6.6, good surface, low warpage

Modulus

10.000MPa

Strength

180MPa

Impact

70kJ/m²

AKROMID® A3 GM 25/15 1 black (7003) - 25% glass fibre, 15% glass bead, heat stabilised, polyamide 6.6, good surface, low warpage

149505180

AKROTEK®

UL
Preliminary

PK-VM GF 30 FR orange (8537)PK GF30 FR(40)

AKROTEK® PK-VM GF 30 FR orange (8537) is a 30% glass fibre reinforced, flame retardant and process improved Polyketone compound, colored in orange similar to RAL 2003. The flame retardant system is free of red phosphorous and halogens. Due to its good chemical resistance, good dimensional stability and high elongation at break it is suitable for high voltage components in e-mobility.

Features

hydrolysis / chemically stabilised
flame retardant
process improved
E&E
E-Mobility

Regulatory

ul

Properties

Modulus

8.600MPa

Strength

125MPa

Impact

70kJ/m²

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
8600 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.
125 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.
3,5 %

Charpy impact strength

ISO 179-1/1eU

23°C | d.a.m.
70 kJ/m²

Charpy notched impact strength

ISO 179-1/1eA

23°C | d.a.m.
13 kJ/m²

Thermal Properties

RTI electrical

UL 746B

UL
0,8mm Wall thickness
UL
1,6mm Wall thickness
UL
3,2mm Wall thickness
105 °C
105 °C
105 °C

RTI impact

UL 746B

UL
0,8mm Wall thickness
UL
1,6mm Wall thickness
UL
3,2mm Wall thickness
70 °C
70 °C
80 °C

RTI strength

UL 746B

UL
0,8mm Wall thickness
UL
1,6mm Wall thickness
UL
3,2mm Wall thickness
115 °C
115 °C
125 °C

Melting temperature

ISO 11357-3

DSC, 10K/min
220 °C

Flammability

Burning rate

UL 94

UL
0,8 mm Wall thickness
UL
1,6 mm Wall thickness
UL
3,2 mm Wall thickness
V-0 Class
V-0 Class
V-0 Class

GWFI

IEC 60695-2-12

UL
0,8 mm Wall thickness
UL
1,6 mm Wall thickness
UL
3,2 mm Wall thickness
960 °C
960 °C
960 °C

GWIT

IEC 60695-2-13

UL
0,8 mm Wall thickness
UL
1,6 mm Wall thickness
UL
3,2 mm Wall thickness
825 °C
825 °C
850 °C

HWI

UL 746A

UL
0,8 mm Wall thickness
UL
1,6 mm Wall thickness
UL
3,2 mm Wall thickness
0 PLC
0 PLC
0 PLC

HAI

UL 746A

UL
0,8 mm Wall thickness
UL
1,6 mm Wall thickness
UL
3,2 mm Wall thickness
0 PLC
0 PLC
0 PLC

Burning rate (<100 mm/min)

FMVSS 302

> 1 mm Thickness
+

General properties

Density

ISO 1183

23°C
1,48 g/cm³

Molding shrinkage

ISO 294-4

flow
transverse
0,3 - 0,5 %
0,8 - 1,0 %

Electrical Properties

Volume resistivity IEC

DIN EN IEC 62631-3-2

UL
d.a.m.
1010 Ω x cm

Surface resistivity

DIN EN 62631-3-2

UL
d.a.m.
1013 Ω

Comparative tracking index

IEC 60112

UL
Test liquid A
600 V

Comparative tracking index

ASTM D3638

UL
0 PLC

Dielectric strength

IEC 60243

1 mm
29 kV/mm

Inclined-Plane Tracking, IPT

ASTM D2303-13

UL
1 kV

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.

Contact

Do you have any questions? We are happy to help.

Would you like to learn more about AKRO-PLASTIC GmbH? Contact us! We will be happy to help you.

Learn more