AKROMID®
B3 GF 50 1 grey (5507)
PA6 GF50
AKROMID® B3 GF 50 1 grey (5507) - 50% glass fiber reinforced PA 6, heat stabilised, technical parts in industrial engineering and automotive industry
16.500MPa
190MPa
70kJ/m²
AKROMID® B3 GF 50 1 grey (5507) - 50% glass fiber reinforced PA 6, heat stabilised, technical parts in industrial engineering and automotive industry
AKROMID®
B3 GF 40 5 black (7286)
PA6 GF40
AKROMID® B3 GF 40 5 black (7286) - 40% glass fiber reinforced PA 6, high heat stabilised, technical parts in industrial engineering and automotive industry
12.500MPa
200MPa
95kJ/m²
AKROMID® B3 GF 40 5 black (7286) - 40% glass fiber reinforced PA 6, high heat stabilised, technical parts in industrial engineering and automotive industry
AKROMID®
B3 S1 natural (7748)
PA6-I
AKROMID® B3 S1 natural (7748) is an unreinforced, cold impact strength polyamide 6
1.350MPa
35MPa
180kJ/m²
AKROMID® B3 S1 natural (7748) is an unreinforced, cold impact strength polyamide 6
AKROMID®
A3 GF 30 6 natural (6398)
PA66 GF30
AKROMID® A3 GF 30 6 natural (6398) is a 30% glass fibre reinforced, inorganic high heat stabilised polyamide 6.6 with high stiffness and strength
10.000MPa
200MPa
85kJ/m²
AKROMID® A3 GF 30 6 natural (6398) is a 30% glass fibre reinforced, inorganic high heat stabilised polyamide 6.6 with high stiffness and strength
AKROMID®
B3 GF 15 grey (6270)
PA6 GF15
AKROMID® B3 GF 15 grey (6270) is a 15% glass fibre reinforced polyamide 6 with average stiffness and strength.
6.000MPa
110MPa
50kJ/m²
AKROMID® B3 GF 15 grey (6270) is a 15% glass fibre reinforced polyamide 6 with average stiffness and strength.
AKROMID®
T5 ICF 20 black (6773)
PPA CF20
AKROMID® T5 ICF 20 black (6773) is a 20% carbon fibre reinforced polyphthalamide with good flexural strength and good sliding properties
18.000MPa
222MPa
37kJ/m²
AKROMID® T5 ICF 20 black (6773) is a 20% carbon fibre reinforced polyphthalamide with good flexural strength and good sliding properties
AKROMID®
A3 GM 25/15 1 black (7003)
PA66 (GF25+GB15)
AKROMID® A3 GM 25/15 1 black (7003) - 25% glass fibre, 15% glass bead, heat stabilised, polyamide 6.6, good surface, low warpage
10.000MPa
180MPa
70kJ/m²
AKROMID® A3 GM 25/15 1 black (7003) - 25% glass fibre, 15% glass bead, heat stabilised, polyamide 6.6, good surface, low warpage
AKROMID®
B3 GF 35 ECO black (8472)PA6 GF35
AKROMID® B3 GF 35 ECO black (8472) is a 35% glass fibre-reinforced, heat-stabilised polyamide 6. The material is suitable for technical components in mechanical engineering and automotive industry with demands for high stiffness and strength. The formulations of the sustainable ECO products are partly based on regenerated post-industrial feedstock and thus contribute to reducing the consumption of valuable raw materials.
Features
Properties
10.500MPa
160MPa
82kJ/m²
Sustainability
Recycled content
Mechanical Properties
Tensile modulus
ISO 527-2
Tensile stress at break
ISO 527-2
Tensile strain at break
ISO 527-2
Charpy impact strength
ISO 179-1/1eU
Thermal Properties
Melting temperature
ISO 11357-3
Flammability
Burning rate
UL 94
Burning rate (<100 mm/min)
FMVSS 302
General properties
Molding shrinkage
ISO 294-4
Disclaimer
All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.
Contact
Do you have any questions? We are happy to help.
Would you like to learn more about AKRO-PLASTIC GmbH? Contact us! We will be happy to help you.