HEADER Granulat 1920x700

Find the right compound

Select your fitting and find the right compound for your intend

Tensile Modulusin MPa
Tensile Strengthin MPa
Charpy impact strengthin kJ/m²
558 Compounds found
Recommended  
Tensile Modulus
Tensile Strength
Charpy impact strength
Description

AKROMID®

Preliminary

T9 GF 30 grey (8134)

PPA GF30

AKROMID® T9 GF 30 grey (8134) - PPA, 50% glass fiber, high stiffness and strength, high temperature and chemical resistance, grey RAL 7047, E&E.


Modulus

10.000MPa

Strength

190MPa

Impact

70kJ/m²

AKROMID® T9 GF 30 grey (8134) - PPA, 50% glass fiber, high stiffness and strength, high temperature and chemical resistance, grey RAL 7047, E&E.

AKROMID®

Preliminary

B3 GF 50 4 RM-M 2 black (8234)

PA6+X GF50

AKROMID® B3 GF 50 4 RM-M 2 black (8234) - 50% glass fiber reinforced PA 6 with good surface properties, UV stabilised, chemically stabilised, reduced moisture absorption


Modulus

16.800MPa

Strength

210MPa

Impact

50kJ/m²

AKROMID® B3 GF 50 4 RM-M 2 black (8234) - 50% glass fiber reinforced PA 6 with good surface properties, UV stabilised, chemically stabilised, reduced moisture absorption

AKROLOY®

PA GF 30 black (2718)

PA66+PA6I/6T

AKROLOY® PA GF 30 black (2718) is a 30% glass fibre reinforced, semi-aromatic polyamide blend with high stiffness and strength, even in conditioned state. The advanced version of this Product is AKROLOY® PA GF 30 black (6415) with a modern stabilization technology, featuring improved weld-line strength and an even wider process window.


Modulus

10.500MPa

Strength

210MPa

Impact

80kJ/m²

AKROLOY® PA GF 30 black (2718) is a 30% glass fibre reinforced, semi-aromatic polyamide blend with high stiffness and strength, even in conditioned state. The advanced version of this Product is AKROLOY® PA GF 30 black (6415) with a modern stabilization technology, featuring improved weld-line strength and an even wider process window.

AKROMID®

B3 GF 30 2 RM-D black (3424)

PA6+ABS GF30

AKROMID® B3 GF 30 2 RM-D black (3424) is a 30% glass fibre reinforced, UV-stabilised polyamide 6 with limited moisture absorption.


Modulus

9.300MPa

Strength

145MPa

Impact

55kJ/m²

AKROMID® B3 GF 30 2 RM-D black (3424) is a 30% glass fibre reinforced, UV-stabilised polyamide 6 with limited moisture absorption.

AKROMID®

C3 1 S3 black (4297)

PA66+PA6

AKROMID® C3 1 S3 black (4297) - PA 6.6/6 blend unreinforced, impact modified whilst maintaining good flowability, for connecting and fixing systems


Modulus

2.500MPa

Strength

65MPa

Impact

180kJ/m²

AKROMID® C3 1 S3 black (4297) - PA 6.6/6 blend unreinforced, impact modified whilst maintaining good flowability, for connecting and fixing systems

AKROTEK®

PK-VM 8 natural (6146)

PK

AKROTEK® PK-VM 8 natural (6146) - Polyketon, unreinforced, Tribology, friction and wear, chemical resistance, EU 10/2011, FDA 21 CFR


Modulus

1.500MPa

Strength

60MPa

Impact

180kJ/m²

AKROTEK® PK-VM 8 natural (6146) - Polyketon, unreinforced, Tribology, friction and wear, chemical resistance, EU 10/2011, FDA 21 CFR

AKROMID®

B3 9 natural (6409)

PA6

AKROMID® B3 9 natural (6409) - PA6, unreinforced, process optimized, furniture industry, automotive, cable gland


Modulus

3.300MPa

Strength

85MPa

Impact

NA

AKROMID® B3 9 natural (6409) - PA6, unreinforced, process optimized, furniture industry, automotive, cable gland

149505180

AKROMID®

Preliminary

T5 GF 50 9 black (8001)PPA GF50

AKROMID® T5 GF 50 9 black (8001) is a 50% glass fibre reinforced polyphthalamide with very high rigidity and strength, as well as high temperature and chemical resistance. This aromatic PPA keeps mechanical performance even at elevated temperatures or moisture pic-up. This product was optimized and provides a very good surface quality.

Features

surface modified

Properties

Modulus

18.500MPa

Strength

255MPa

Impact

65kJ/m²

Mechanical Properties


Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
1 mm/min | conditioned
18500 MPa
18500 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
255 MPa
255 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
1,9 %
1,9 %

Charpy impact strength

ISO 179-1/1eU

23°C | d.a.m.
23°C | conditioned
65 kJ/m²
58 kJ/m²

Charpy notched impact strength

ISO 179-1/1eA

23°C | d.a.m.
13 kJ/m²

Thermal Properties


Temperature of deflection under load HDT/C

ISO 75

8 MPa
220 °C

Glass transition temperature

ISO 11357-2

DSC, 2nd heating
135 °C

Melting temperature

ISO 11357-3

DSC, 10K/min
325 °C

Flammability


Burning rate

UL 94

1,6 mm Wall thickness
HB Class

General properties


Density

ISO 1183

23°C
1,65 g/cm³

Molding shrinkage

ISO 294-4

flow
transverse
0,1 - 0,3 %
0,4 - 0,6 %

Rheological Properties


Flowability

AKRO

2 mm Thickness
400 mm

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.

Contact

Do you have any questions? We are happy to help.

Would you like to learn more about AKRO-PLASTIC GmbH? Contact us! We will be happy to help you.

Learn more