HEADER Granulat 1920x700

Find the right compound

Select your fitting and find the right compound for your intend

Tensile Modulusin MPa
Tensile Strengthin MPa
Charpy impact strengthin kJ/mĀ²
558 Compounds found
Recommended Ā 
Tensile Modulus
Tensile Strength
Charpy impact strength
Description

AKROMIDĀ®

A3 GF 35 2 black (7226)

PA66 GF35

AKROMIDĀ® A3 GF 35 2 black (7226) - 35% glass fiber reinforced PA 6.6, UV-stabilised, technical parts in industrial engineering and automotive industry

Modulus

11.500MPa

Strength

215MPa

Impact

90kJ/mĀ²

AKROMIDĀ® A3 GF 35 2 black (7226) - 35% glass fiber reinforced PA 6.6, UV-stabilised, technical parts in industrial engineering and automotive industry

AKROMIDĀ®

B3 1 S3 black (7956)

PA6-I

AKROMIDĀ® B3 1 S3 black (7956) - PA 6 unreinforced, impact modified whilst maintaining good flowability, for connecting and fixing systems

Modulus

2.200MPa

Strength

55MPa

Impact

180kJ/mĀ²

AKROMIDĀ® B3 1 S3 black (7956) - PA 6 unreinforced, impact modified whilst maintaining good flowability, for connecting and fixing systems

AKROLOYĀ®

PARA ICF 40 black (6130)

PARA CF40

AKROLOYĀ® PARA ICF 40 black (6130) is a 40% carbon fibre reinforced Polyarylamide with very high stiffness. The material offers a higher process stability as well as a better weld line performance than its predecessor (6128), while the colour depth is reduced.

Modulus

39.000MPa

Strength

280MPa

Impact

35kJ/mĀ²

AKROLOYĀ® PARA ICF 40 black (6130) is a 40% carbon fibre reinforced Polyarylamide with very high stiffness. The material offers a higher process stability as well as a better weld line performance than its predecessor (6128), while the colour depth is reduced.

AKROMIDĀ®

UL

A3 GF 35 1 HU black (8417)

PA66 GF35

AKROMIDĀ® A3 GF 35 1 HU black (8417) - PA 6.6, 35% glass fibre, heat ageing resistant, high rigidity and strength, very good flowability, UL listed HB.

Modulus

12.000MPa

Strength

215MPa

Impact

75kJ/mĀ²

AKROMIDĀ® A3 GF 35 1 HU black (8417) - PA 6.6, 35% glass fibre, heat ageing resistant, high rigidity and strength, very good flowability, UL listed HB.

AKROMIDĀ®

Preliminary

C3 GF 30 1 natural (8574)

PA66 + PA6 GF30

AKROMIDĀ® C3 GF 30 1 natural (8574) - PA6.6/6 blend, 30% glass fiber reinforced, heat stabilised, industrial engineering, automotive industry

Modulus

9.300MPa

Strength

185MPa

Impact

75kJ/mĀ²

AKROMIDĀ® C3 GF 30 1 natural (8574) - PA6.6/6 blend, 30% glass fiber reinforced, heat stabilised, industrial engineering, automotive industry

AKROMIDĀ®

B3 GF 15 natural (2469)

PA6 GF15

AKROMIDĀ® B3 GF 15 natural (2469) is a 15% glass fibre reinforced polyamide 6 with medium stiffness and strength and light inherent color

Modulus

6.100MPa

Strength

120MPa

Impact

52kJ/mĀ²

AKROMIDĀ® B3 GF 15 natural (2469) is a 15% glass fibre reinforced polyamide 6 with medium stiffness and strength and light inherent color

AKROMIDĀ®

A3 2 S1 white (5973)

PA66-I

AKROMIDĀ® A3 2 S1 white (5973) - PA 6.6, unreinforced, impact modified, UV-stabilised, for connecting and fixing systems, automotive, electro, furniture

Modulus

1.700MPa

Strength

45MPa

Impact

180kJ/mĀ²

AKROMIDĀ® A3 2 S1 white (5973) - PA 6.6, unreinforced, impact modified, UV-stabilised, for connecting and fixing systems, automotive, electro, furniture

149505180

AKROMIDĀ®

B28 GF 30 6 LT black (6931)PA6 GF30

AKROMIDĀ® B28 GF 30 6 LT black (6931) is a 30% glass fibre reinforced, easy flowing Polyamide 6. The material is characterised by high stiffness and strength. Furthermore, it is high heat stabilised and therefore perfectly suitable for automotive and industrial applications. The compound can be welded via laser welding.

Features

heat stabilised 160
laser transparent

Properties

Modulus

9.800MPa

Strength

185MPa

Impact

90kJ/mĀ²

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
1 mm/min | conditioned
9800 MPa
6400 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
185 MPa
100 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
3 %
5,5 %

Flexural modulus

ISO 178

2 mm/min | d.a.m.
8000 MPa

Flexural strength

ISO 178

2 mm/min | d.a.m.
250 MPa

Charpy impact strength

ISO 179-1/1eU

23Ā°C | d.a.m.
90 kJ/mĀ²

Charpy notched impact strength

ISO 179-1/1eA

23Ā°C | d.a.m.
12 kJ/mĀ²

Thermal Properties

Temperature of deflection under load HDT/A

ISO 75

1,8 MPa
210 Ā°C

Melting temperature

ISO 11357-3

DSC, 10K/min
220 Ā°C

Flammability

Burning rate

UL 94

1,6 mm Wall thickness
HB Class

Burning rate (<100 mm/min)

FMVSS 302

> 1 mm Thickness
+

General properties

Density

ISO 1183

23Ā°C
1,35 g/cmĀ³

Humidity absorption

ISO 1110

70Ā°C, 62% r.H.
2,1 - 2,3 %

Molding shrinkage

ISO 294-4

flow
transverse
0,1 - 0,3 %
0,5 - 0,7 %

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKROĀ®, AKROMIDĀ®, AKROLENĀ®, AKROLOYĀ®, AKROTEKĀ®, ICXĀ® and PRECITEĀ® are registered trademarks of the Feddersen Group.

Contact

Do you have any questions? We are happy to help.

Would you like to learn more about AKRO-PLASTIC GmbH? Contact us! We will be happy to help you.

Learn more