Find the right compound
Select your fitting and find the right compound for your intend
AKROMID®
B3 GF 50 ECO black (7926)
PA6 GF50
AKROMID® B3 GF 50 ECO black (7926) - PA 6, GF 50, high strength, high stiffness, heat stabilised, recycled, Co2 reduction, sustainable.
16.000MPa
200MPa
95kJ/m²
AKROMID® B3 GF 50 ECO black (7926) - PA 6, GF 50, high strength, high stiffness, heat stabilised, recycled, Co2 reduction, sustainable.
PRECITE®
P3 GF 10 black (7813)
PBT GF 10
PRECITE® P3 GF 10 black (7813) is a 10% glass fibre reinforced, medium viscous poly(butylene terephthalate) with medium stiffness and toughness as well as high dimensional and chemical resistance.
4.600MPa
90MPa
25kJ/m²
PRECITE® P3 GF 10 black (7813) is a 10% glass fibre reinforced, medium viscous poly(butylene terephthalate) with medium stiffness and toughness as well as high dimensional and chemical resistance.
AKROMID®
B3 GF 50 4 RM-M 2 black (8234)
PA6+X GF50
AKROMID® B3 GF 50 4 RM-M 2 black (8234) - 50% glass fiber reinforced PA 6 with good surface properties, UV stabilised, chemically stabilised, reduced moisture absorption
16.800MPa
210MPa
50kJ/m²
AKROMID® B3 GF 50 4 RM-M 2 black (8234) - 50% glass fiber reinforced PA 6 with good surface properties, UV stabilised, chemically stabilised, reduced moisture absorption
AKROMID®
NEXT U28 ICF 30 1 black (8233)
PA11 CF30
AKROMID® NEXT U28 ICF 30 1 black (8233) - PA11 made of renewable raw materials, recycled carbon fibre, low density, high ductility
15.300MPa
165MPa
75kJ/m²
AKROMID® NEXT U28 ICF 30 1 black (8233) - PA11 made of renewable raw materials, recycled carbon fibre, low density, high ductility
AKROMID®
B3 GF 30 2 RM-D black (3424)
PA6+ABS GF30
AKROMID® B3 GF 30 2 RM-D black (3424) is a 30% glass fibre reinforced, UV-stabilised polyamide 6 with limited moisture absorption.
9.300MPa
145MPa
55kJ/m²
AKROMID® B3 GF 30 2 RM-D black (3424) is a 30% glass fibre reinforced, UV-stabilised polyamide 6 with limited moisture absorption.
AKROTEK®
PK-VM black (4973)
PK
AKROTEK® PK-VM black (4973) - Polyketon, Tribology, friction and wear, chemical resistance
1.500MPa
60MPa
180kJ/m²
AKROTEK® PK-VM black (4973) - Polyketon, Tribology, friction and wear, chemical resistance
AKROTEK®
PK-VM 8 natural (6146)
PK
AKROTEK® PK-VM 8 natural (6146) - Polyketon, unreinforced, Tribology, friction and wear, chemical resistance, EU 10/2011, FDA 21 CFR
1.500MPa
60MPa
180kJ/m²
AKROTEK® PK-VM 8 natural (6146) - Polyketon, unreinforced, Tribology, friction and wear, chemical resistance, EU 10/2011, FDA 21 CFR
AKROMID®
B3 GF 35 1 HU red (8416)PA6 GF35
AKROMID® B3 GF 35 1 HU red (8416) is a 35% glass fibre reinforced, heat ageing resistant polyamide 6 with high rigidity and strength. The material is colored in red similar to RAL 3001. This UL94 HB listed grade is suitable for technical components in mechanical engineering and the automotive industry.
Features
Regulatory
Properties
12.000MPa
190MPa
Na
Mechanical Properties
Tensile modulus
ISO 527-2
Tensile stress at break
ISO 527-2
Tensile strain at break
ISO 527-2
Thermal Properties
Melting temperature
ISO 11357-3
Flammability
Burning rate
UL 94
Burning rate (<100 mm/min)
FMVSS 302
General properties
Density
ISO 1183
Humidity absorption
ISO 1110
Molding shrinkage
ISO 294-4
Electrical Properties
Comparative tracking index
IEC 60112
Comparative tracking index
ASTM D3638
Disclaimer
All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.
Contact
Do you have any questions? We are happy to help.
Would you like to learn more about AKRO-PLASTIC GmbH? Contact us! We will be happy to help you.