AKROMID®

Preliminary

B3 GF 25 1 L natural (4781)

PA6 + PP GF25

AKROMID® B3 GF 25 1 L natural (4781) - PA6/PP-Blend, 25% glass fibre reinforced, lower density, cost reduced, calcium chloride

Modulus

7.200MPa

Strength

130MPa

Impact

70kJ/m²

AKROMID® B3 GF 25 1 L natural (4781) - PA6/PP-Blend, 25% glass fibre reinforced, lower density, cost reduced, calcium chloride

AKROTEK®

PK-VM black (4973)

PK

AKROTEK® PK-VM black (4973) - Polyketon, Tribology, friction and wear, chemical resistance

Modulus

1.500MPa

Strength

60MPa

Impact

180kJ/m²

AKROTEK® PK-VM black (4973) - Polyketon, Tribology, friction and wear, chemical resistance

AKROMID®

A3 2 S1 grey (5972)

PA66-I

AKROMID® A3 2 S1 grey (5972) - PA 6.6, unreinforced, impact modified, UV-stabilised, for connecting and fixing systems, automotive, electro, furniture

Modulus

1.800MPa

Strength

45MPa

Impact

NA

AKROMID® A3 2 S1 grey (5972) - PA 6.6, unreinforced, impact modified, UV-stabilised, for connecting and fixing systems, automotive, electro, furniture

AKROMID®

B3 GF 15 grey (6270)

PA6 GF15

AKROMID® B3 GF 15 grey (6270) is a 15% glass fibre reinforced polyamide 6 with average stiffness and strength.

Modulus

6.000MPa

Strength

110MPa

Impact

50kJ/m²

AKROMID® B3 GF 15 grey (6270) is a 15% glass fibre reinforced polyamide 6 with average stiffness and strength.

AKROMID®

A3 GF 50 8 natural (7291)

PA66 GF50

AKROMID® A3 GF 50 8 natural (7291) - PA6.6, 50% glass fiber, food contact, kitchen and household appliances

Modulus

17.400MPa

Strength

265MPa

Impact

115kJ/m²

AKROMID® A3 GF 50 8 natural (7291) - PA6.6, 50% glass fiber, food contact, kitchen and household appliances

AKROMID®

Preliminary

B3 GF 50 ECO black (7926)

PA6 GF50

AKROMID® B3 GF 50 ECO black (7926) - PA 6, GF 50, high strength, high stiffness, heat stabilised, recycled, Co2 reduction, sustainable.

Modulus

16.000MPa

Strength

200MPa

Impact

95kJ/m²

AKROMID® B3 GF 50 ECO black (7926) - PA 6, GF 50, high strength, high stiffness, heat stabilised, recycled, Co2 reduction, sustainable.

AKROMID®

Preliminary

T5 GF 40 6 black (8002)

PPA GF40

AKROMID® T5 GF 40 6 black (8002) - 40% glass fibre reinforced with high stiffness and strength, high temperature resistance, e.g. under the hood applications

Modulus

16.000MPa

Strength

245MPa

Impact

80kJ/m²

AKROMID® T5 GF 40 6 black (8002) - 40% glass fibre reinforced with high stiffness and strength, high temperature resistance, e.g. under the hood applications

147484980

PRECITE®

Preliminary

P3 GF 30 9 FR black (8424)PBT GF30 FR(40)

PRECITE® P3 GF 30 9 FR black (8424) is a 30% glass fibre reinforced, flame retardant polybutylene terephthalate (PBT) with high stiffness and strength. The material offers outstanding long-term heat-aging stability as well as mechanical advantages to conventional products. It achieves V0 classification at thicknesses of 1.6 mm and above by using a flame retardant system which is free of red phosphorous and halogens. Due to its low moisture absorption, this material has very good dimensional stability and it is particularly suitable for precision parts in E-Mobility or E&E industry.

Features

heat stabilised 130
flame retardant
low warpage
E&E
E-Mobility

Properties

Modulus

10.500MPa

Strength

122MPa

Impact

50kJ/m²

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
10500 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.
122 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.
2,4 %

Flexural modulus

ISO 178

2 mm/min | d.a.m.
10500 MPa

Flexural strength

ISO 178

2 mm/min | d.a.m.
197 MPa

Flexural strain at break

ISO 178

2 mm/min | d.a.m.
2,6 %

Charpy impact strength

ISO 179-1/1eU

23°C | d.a.m.
30°C | d.a.m.
-
50 kJ/m²
58 kJ/m²

Charpy notched impact strength

ISO 179-1/1eA

23°C | d.a.m.
30°C | d.a.m.
-
9 kJ/m²
8 kJ/m²

Thermal Properties

Temperature of deflection under load HDT/A

ISO 75

1,8 MPa
205 °C

Temperature of deflection under load HDT/B

ISO 75

0,45 MPa
222 °C

Melting temperature

ISO 11357-3

DSC, 10K/min
224 °C

Flammability

Burning rate

UL 94

1,6 mm Wall thickness
V-0 Class

GWFI

IEC 60695-2-12

0,8 mm Wall thickness
1,6 mm Wall thickness
960 °C
960 °C

GWIT

IEC 60695-2-13

0,8 mm Wall thickness
1,6 mm Wall thickness
750 °C
750 °C

Burning rate (<100 mm/min)

FMVSS 302

> 1 mm Thickness
+

Oxygen index

ISO 4589-2

> 30 %

General properties

Density

ISO 1183

23°C
1,53 g/cm³

Humidity absorption

ISO 1110

70°C, 62% r.H.
0,1 - 0,3 %

Rheological Properties

MVR

ISO 1133

275°C/2,16kg
25,5 cm³/10 min

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.

Contact

Do you have any questions? We are happy to help.

Would you like to learn more about AKRO-PLASTIC GmbH? Contact us! We will be happy to help you.

Learn more