AKROMID®
B3 9 natural (6409)
PA6
AKROMID® B3 9 natural (6409) - PA6, unreinforced, process optimized, furniture industry, automotive, cable gland
3.300MPa
85MPa
NA
AKROMID® B3 9 natural (6409) - PA6, unreinforced, process optimized, furniture industry, automotive, cable gland
AKROMID®
A3 GF 35 2 black (7226)
PA66 GF35
AKROMID® A3 GF 35 2 black (7226) - 35% glass fiber reinforced PA 6.6, UV-stabilised, technical parts in industrial engineering and automotive industry
11.500MPa
215MPa
90kJ/m²
AKROMID® A3 GF 35 2 black (7226) - 35% glass fiber reinforced PA 6.6, UV-stabilised, technical parts in industrial engineering and automotive industry
AKROMID®
B3 GF 50 RM-M black (3146)
PA6 + X GF50
AKROMID® B3 GF 50 RM-M black (3146) - 50% glass fiber reinforced PA 6 with reduced moisture absorption and very high stiffness and strength
17.000MPa
210MPa
70kJ/m²
AKROMID® B3 GF 50 RM-M black (3146) - 50% glass fiber reinforced PA 6 with reduced moisture absorption and very high stiffness and strength
AKROMID®
B3 GF 30 2 RM-D black (3424)
PA6+ABS GF30
AKROMID® B3 GF 30 2 RM-D black (3424) is a 30% glass fibre reinforced, UV-stabilised polyamide 6 with limited moisture absorption.
9.300MPa
145MPa
55kJ/m²
AKROMID® B3 GF 30 2 RM-D black (3424) is a 30% glass fibre reinforced, UV-stabilised polyamide 6 with limited moisture absorption.
AKROMID®
B3 GM 10/20 1 black (8748)
PA6 (GF10+GB20)
AKROMID® B3 GM 10/20 1 black (8748) - PA6, 10% glass fibre, 20% glass bead, heat stabilised, easy flowing, good surface, reduced warpage.
5.700MPa
110MPa
30kJ/m²
AKROMID® B3 GM 10/20 1 black (8748) - PA6, 10% glass fibre, 20% glass bead, heat stabilised, easy flowing, good surface, reduced warpage.
AKROMID®
A3 ICF 30 black (5021)
PA66 CF30
AKROMID® A3 ICF 30 black (5021) is a 30% carbon fibre reinforced polyamide 6.6 with high flexural strength and good sliding properties
24.000MPa
240MPa
55kJ/m²
AKROMID® A3 ICF 30 black (5021) is a 30% carbon fibre reinforced polyamide 6.6 with high flexural strength and good sliding properties
AKROMID®
C3 GF 35 1 natural (4748)
PA66+PA6 GF35
AKROMID® C3 GF 35 1 natural (4748) - 35% glass fiber reinforced PA 6.6/6 blend, heat stabilised, technical parts in industrial engineering and automotive industry
11.000MPa
200MPa
100kJ/m²
AKROMID® C3 GF 35 1 natural (4748) - 35% glass fiber reinforced PA 6.6/6 blend, heat stabilised, technical parts in industrial engineering and automotive industry
AKROTEK®
PK-VM GF 10 natural (8679)PK GF10
AKROTEK® PK-VM GF 10 natural (8679) is a 10% glass fibre reinforced Polyketone with average stiffness and strength. Due to its very good media resistance, the material is suitable for use in applications that carry cooling water. This type was developed as the successor to PK-VM GF 10 natural (8534) in order to meet the requirements for a larger processing window during processing.
Features
Properties
3.600MPa
75MPa
61kJ/m²
Mechanical Properties
Tensile modulus
ISO 527-2
Tensile stress at break
ISO 527-2
Tensile strain at break
ISO 527-2
Charpy impact strength
ISO 179-1/1eU
Thermal Properties
Temperature of deflection under load HDT/A
ISO 75
Melting temperature
ISO 11357-3
Flammability
Burning rate
UL 94
Burning rate (<100 mm/min)
FMVSS 302
General properties
Humidity absorption
ISO 1110
Molding shrinkage
ISO 294-4
Disclaimer
All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.
Contact
Do you have any questions? We are happy to help.
Would you like to learn more about AKRO-PLASTIC GmbH? Contact us! We will be happy to help you.