AKROMIDĀ®

Preliminary

B3 S1 natural (7748)

PA6-I

AKROMIDĀ® B3 S1 natural (7748) is an unreinforced, cold impact strength polyamide 6

Modulus

1.350MPa

Strength

35MPa

Impact

180kJ/mĀ²

AKROMIDĀ® B3 S1 natural (7748) is an unreinforced, cold impact strength polyamide 6

AKROMIDĀ®

A3 GK 30 LA black (4624)

PA66 GB30

AKROMIDĀ® A3 GK 30 LA black (4624) is a 30% glass bead filled polyamide 6.6 with low warpage, high surface appearance and lasermarkable.

Modulus

5.000MPa

Strength

90MPa

Impact

25kJ/mĀ²

AKROMIDĀ® A3 GK 30 LA black (4624) is a 30% glass bead filled polyamide 6.6 with low warpage, high surface appearance and lasermarkable.

AKROTEKĀ®

PK-VM black (4973)

PK

AKROTEKĀ® PK-VM black (4973) - Polyketon, Tribology, friction and wear, chemical resistance

Modulus

1.500MPa

Strength

60MPa

Impact

180kJ/mĀ²

AKROTEKĀ® PK-VM black (4973) - Polyketon, Tribology, friction and wear, chemical resistance

AKROMIDĀ®

A3 2 S1 white (5973)

PA66-I

AKROMIDĀ® A3 2 S1 white (5973) - PA 6.6, unreinforced, impact modified, UV-stabilised, for connecting and fixing systems, automotive, electro, furniture

Modulus

1.700MPa

Strength

45MPa

Impact

180kJ/mĀ²

AKROMIDĀ® A3 2 S1 white (5973) - PA 6.6, unreinforced, impact modified, UV-stabilised, for connecting and fixing systems, automotive, electro, furniture

AKROMIDĀ®

T5 GF 50 8 black (6205)

PPA GF50

AKROMIDĀ® T5 GF 50 8 black (6205) - PPA, 50% glass fiber, food contact, kitchen and household appliances, fitting, water meter, ACS, WRAS, NSF 61, EU 10/2011, FDA

Modulus

19.000MPa

Strength

270MPa

Impact

85kJ/mĀ²

AKROMIDĀ® T5 GF 50 8 black (6205) - PPA, 50% glass fiber, food contact, kitchen and household appliances, fitting, water meter, ACS, WRAS, NSF 61, EU 10/2011, FDA

AKROMIDĀ®

T5 GF 30 8 black (6457)

PPA GF30

AKROMIDĀ® T5 GF 30 8 black (6457) - PPA, 30% glass fiber, food contact, kitchen and household appliances, fitting, water meter, ACS, WRAS, NSF 61, EU 10/2011, FDA

Modulus

11.500MPa

Strength

210MPa

Impact

65kJ/mĀ²

AKROMIDĀ® T5 GF 30 8 black (6457) - PPA, 30% glass fiber, food contact, kitchen and household appliances, fitting, water meter, ACS, WRAS, NSF 61, EU 10/2011, FDA

AKROLOYĀ®

Preliminary

PA FGF 60 black (6765)

PA66 + PA6I/6T GF 60

AKROLOYĀ® PA FGF 60 black (6765) - semi-aromatic polyamide blend, 60% flat glass fiber reinforced,improved properties 90Ā° to the flow direction

Modulus

20.000MPa

Strength

290MPa

Impact

90kJ/mĀ²

AKROLOYĀ® PA FGF 60 black (6765) - semi-aromatic polyamide blend, 60% flat glass fiber reinforced,improved properties 90Ā° to the flow direction

145464780

AKROMIDĀ®

B3 GF 60 1 black (4644)PA6 GF60

AKROMIDĀ® B3 GF 60 1 black (4644) is a 60% glass fiber reinforced, heat stabilised polyamide 6. It is characterised by an improved flowability compared to a standard PA 6 GF 60. Furthermore, the material impresses with its high stiffness and strength. It is therefore perfectly suitable for technical applications in industrial engineering and in the automotive industry.

Features

heat stabilised 130
easy flow

Properties

Modulus

21.000MPa

Strength

250MPa

Impact

90kJ/mĀ²

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
1 mm/min | conditioned
21000 MPa
13500 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
250 MPa
160 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
2,5 %
3,5 %

Flexural modulus

ISO 178

2 mm/min | d.a.m.
19000 MPa

Flexural strength

ISO 178

2 mm/min | d.a.m.
370 MPa

Charpy impact strength

ISO 179-1/1eU

23Ā°C | d.a.m.
23Ā°C | conditioned
30Ā°C | d.a.m.
-
90 kJ/mĀ²
95 kJ/mĀ²
90 kJ/mĀ²

Charpy notched impact strength

ISO 179-1/1eA

23Ā°C | d.a.m.
23Ā°C | conditioned
30Ā°C | d.a.m.
-
20 kJ/mĀ²
25 kJ/mĀ²
20 kJ/mĀ²

Thermal Properties

Temperature of deflection under load HDT/A

ISO 75

1,8 MPa
220 Ā°C

Temperature of deflection under load HDT/B

ISO 75

0,45 MPa
220 Ā°C

Melting temperature

ISO 11357-3

DSC, 10K/min
220 Ā°C

Coefficient of linear thermal expansion

ISO 11359-1/2

23Ā°C to 80Ā°C | parallel
23Ā°C to 80Ā°C | transverse
0,13 10ā»ā“/K
0,60 10ā»ā“/K

Flammability

Burning rate

UL 94

0,8 mm Wall thickness
HB Class

GWFI

IEC 60695-2-12

1,6 mm Wall thickness
650 Ā°C

GWIT

IEC 60695-2-13

1,6 mm Wall thickness
675 Ā°C

Burning rate (<100 mm/min)

FMVSS 302

> 1 mm Thickness
+

General properties

Density

ISO 1183

23Ā°C
1,7 g/cmĀ³

Humidity absorption

ISO 1110

70Ā°C, 62% r.H.
0,9 - 1,2 %

Molding shrinkage

ISO 294-4

flow
transverse
0,1 - 0,3 %
0,3 - 0,5 %

Rheological Properties

Flowability

AKRO

2 mm Thickness
320 mm

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKROĀ®, AKROMIDĀ®, AKROLENĀ®, AKROLOYĀ®, AKROTEKĀ®, ICXĀ® and PRECITEĀ® are registered trademarks of the Feddersen Group.

Contact

Do you have any questions? We are happy to help.

Would you like to learn more about AKRO-PLASTIC GmbH? Contact us! We will be happy to help you.

Learn more