AKROMID®
B28 GM 5/25 FR black (7492)
PA6 (GF5+GB25) FR(40)
AKROMID® B28 GM 5/25 FR black (7492) is a 5% glass fibre reinforced, 25% glass bead filled, halogen-free flame retardant, easy flowing polyamide 6 with high stiffness and strength
5.000MPa
55MPa
30kJ/m²
AKROMID® B28 GM 5/25 FR black (7492) is a 5% glass fibre reinforced, 25% glass bead filled, halogen-free flame retardant, easy flowing polyamide 6 with high stiffness and strength
AKROLOY®
PA GF 50 black (2706)
PA66+PA6I/6T GF50
AKROLOY® PA GF 50 black (2706) is a 50% glass fibre reinforced, semi-aromatic polyamide-blend with very high stiffness and strength, even in conditioned state. The advanced version of this Product is AKROLOY® PA GF 50 black (6507) with a modern stabilization technology, featuring improved weld-line strength and an even wider process window.
17.500MPa
250MPa
105kJ/m²
AKROLOY® PA GF 50 black (2706) is a 50% glass fibre reinforced, semi-aromatic polyamide-blend with very high stiffness and strength, even in conditioned state. The advanced version of this Product is AKROLOY® PA GF 50 black (6507) with a modern stabilization technology, featuring improved weld-line strength and an even wider process window.
AKROMID®
B3 ICF 10 1 black (6194)
PA6 CF10
AKROMID® B3 ICF 10 1 black (6194) is a 10% carbon fibre reinforced, heat stabilised polyamide 6 with good sliding properties
8.500MPa
125MPa
45kJ/m²
AKROMID® B3 ICF 10 1 black (6194) is a 10% carbon fibre reinforced, heat stabilised polyamide 6 with good sliding properties
AKROMID®
D3 GF 30 2 black (7026)
PA612 GF30
AKROMID® D3 GF 30 2 black (7026) - PA 6.12, glass fiber, UV stabilized, connector
9.500MPa
180MPa
95kJ/m²
AKROMID® D3 GF 30 2 black (7026) - PA 6.12, glass fiber, UV stabilized, connector
AKROMID®
A3 GF 35 2 black (7226)
PA66 GF35
AKROMID® A3 GF 35 2 black (7226) - 35% glass fiber reinforced PA 6.6, UV-stabilised, technical parts in industrial engineering and automotive industry
11.500MPa
215MPa
90kJ/m²
AKROMID® A3 GF 35 2 black (7226) - 35% glass fiber reinforced PA 6.6, UV-stabilised, technical parts in industrial engineering and automotive industry
AKROMID®
B28 GF 35 FR EN black (7484)
PA6 GF35 FR(40)
AKROMID® B28 GF 35 FR EN black (7484) - PA6, 35% glass fibre, flame retardant, free of halogens, electrically neutral, heatstabilised, easy flow, UL94 V0 from 1,6 mm, e-mobility.
12.600MPa
152MPa
70kJ/m²
AKROMID® B28 GF 35 FR EN black (7484) - PA6, 35% glass fibre, flame retardant, free of halogens, electrically neutral, heatstabilised, easy flow, UL94 V0 from 1,6 mm, e-mobility.
AKROMID®
T9 ICF 20 6 black (7907)
PPA CF 20
AKROMID® T9 ICF 20 6 black (7907) is a with 20% recycled carbon fibre reinforced polyphthalamide with high stiffness and strength, as well as high chemical resistance. The compound is based on PA9T and has lower moisture uptake than conventional PA6T variants. This leads to a significantly higher consistency of the glass transition temperature and higher strength at elevated temperatures especially in conditioned state.
14.000MPa
190MPa
35kJ/m²
AKROMID® T9 ICF 20 6 black (7907) is a with 20% recycled carbon fibre reinforced polyphthalamide with high stiffness and strength, as well as high chemical resistance. The compound is based on PA9T and has lower moisture uptake than conventional PA6T variants. This leads to a significantly higher consistency of the glass transition temperature and higher strength at elevated temperatures especially in conditioned state.
AKROMID®
C3 1 FR orange (8799)PA66+PA6 FR(30)
AKROMID® C3 1 FR orange (8799) is an unreinforced, flame retardant and heat stabilised PA6/6.6 blend, colored in orange similar to RAL 2003. Listed to UL 94 in all-colours, the material is based on a flame retardant system that is free of red phosphorus and halogens. Due to its good flowability, an improved surface quality is achieved and it is quite suitable for film hinges. This grade meets the requirements for public transportation (EN 45545-2 and ISO 4589-2) and is also suitable for applications in the automotive and E&E markets.
Features
Regulatory
Properties
3.500MPa
75MPa
Na
Mechanical Properties
Tensile modulus
ISO 527-2
Tensile stress at yield
ISO 527-2
Tensile strain at break
ISO 527-2
Thermal Properties
Temperature of deflection under load HDT/A
ISO 75
Temperature of deflection under load HDT/B
ISO 75
Melting temperature
ISO 11357-3
Temperature index for 50% loss of tensile strength
IEC 60216
Flammability
Burning rate
UL 94
GWFI
IEC 60695-2-12
GWIT
IEC 60695-2-13
HWI
UL 746A
HAI
UL 746A
Burning rate (<100 mm/min)
FMVSS 302
Oxygen index
ISO 4589-2
Protection Train
EN 45545-2
General properties
Density
ISO 1183
Humidity absorption
ISO 1110
Molding shrinkage
ISO 294-4
Electrical Properties
Volume resistivity IEC
DIN EN IEC 62631-3-2
Comparative tracking index
IEC 60112
Comparative tracking index
ASTM D3638
Dielectric strength
IEC 60243
Inclined-Plane Tracking, IPT
ASTM D2303-13
High voltage arc tracking rate (HVTR)
UL 746A
High Volt, Low Current Arc Resistance
ASTM D495
Disclaimer
All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.
Contact
Do you have any questions? We are happy to help.
Would you like to learn more about AKRO-PLASTIC GmbH? Contact us! We will be happy to help you.