Select your fitting and find the right compound for your intend
AKROMID®
D3 GF 30 2 black (7026)
PA612 GF30
AKROMID® D3 GF 30 2 black (7026) - PA 6.12, glass fiber, UV stabilized, connector
9.500MPa
180MPa
95kJ/m²
AKROMID® D3 GF 30 2 black (7026) - PA 6.12, glass fiber, UV stabilized, connector
AKROMID®
A3 GF 35 2 black (7226)
PA66 GF35
AKROMID® A3 GF 35 2 black (7226) - 35% glass fiber reinforced PA 6.6, UV-stabilised, technical parts in industrial engineering and automotive industry
11.500MPa
215MPa
90kJ/m²
AKROMID® A3 GF 35 2 black (7226) - 35% glass fiber reinforced PA 6.6, UV-stabilised, technical parts in industrial engineering and automotive industry
AKROMID®
B28 GF 35 FR EN black (7484)
PA6 GF35 FR(40)
AKROMID® B28 GF 35 FR EN black (7484) - PA6, 35% glass fibre, flame retardant, free of halogens, electrically neutral, heatstabilised, easy flow, UL94 V0 from 1,6 mm, e-mobility.
12.600MPa
152MPa
70kJ/m²
AKROMID® B28 GF 35 FR EN black (7484) - PA6, 35% glass fibre, flame retardant, free of halogens, electrically neutral, heatstabilised, easy flow, UL94 V0 from 1,6 mm, e-mobility.
AKROMID®
T9 ICF 20 6 black (7907)
PPA CF 20
AKROMID® T9 ICF 20 6 black (7907) is a with 20% recycled carbon fibre reinforced polyphthalamide with high stiffness and strength, as well as high chemical resistance. The compound is based on PA9T and has lower moisture uptake than conventional PA6T variants. This leads to a significantly higher consistency of the glass transition temperature and higher strength at elevated temperatures especially in conditioned state.
14.000MPa
190MPa
35kJ/m²
AKROMID® T9 ICF 20 6 black (7907) is a with 20% recycled carbon fibre reinforced polyphthalamide with high stiffness and strength, as well as high chemical resistance. The compound is based on PA9T and has lower moisture uptake than conventional PA6T variants. This leads to a significantly higher consistency of the glass transition temperature and higher strength at elevated temperatures especially in conditioned state.
AKROLOY®
PARA ICF 40 black (6130)
PARA CF40
AKROLOY® PARA ICF 40 black (6130) is a 40% carbon fibre reinforced Polyarylamide with very high stiffness. The material offers a higher process stability as well as a better weld line performance than its predecessor (6128), while the colour depth is reduced.
39.000MPa
280MPa
35kJ/m²
AKROLOY® PARA ICF 40 black (6130) is a 40% carbon fibre reinforced Polyarylamide with very high stiffness. The material offers a higher process stability as well as a better weld line performance than its predecessor (6128), while the colour depth is reduced.
AKROMID®
B3 GF 15 natural (2469)
PA6 GF15
AKROMID® B3 GF 15 natural (2469) is a 15% glass fibre reinforced polyamide 6 with medium stiffness and strength and light inherent color
6.100MPa
120MPa
52kJ/m²
AKROMID® B3 GF 15 natural (2469) is a 15% glass fibre reinforced polyamide 6 with medium stiffness and strength and light inherent color
AKROMID®
B3 GF 50 RM-M black (3146)
PA6 + X GF50
AKROMID® B3 GF 50 RM-M black (3146) - 50% glass fiber reinforced PA 6 with reduced moisture absorption and very high stiffness and strength
17.000MPa
210MPa
70kJ/m²
AKROMID® B3 GF 50 RM-M black (3146) - 50% glass fiber reinforced PA 6 with reduced moisture absorption and very high stiffness and strength
AKROMID®
AKROMID® C28 GFM 10/20 5 XTC black (7367) is a 10% glass fiber and 20% mineral reinforced, easy flowing polyamide 6.6/6 blend. It is characterised by excellent temperature resistance as well as a very high surface quality. Furthermore, the material impresses with low warpage, resulting in high dimensional stability. It is therefore perfectly suitable for parts in industrial engineering and in the automotive industry, e.g. under the hood, which are exposed to high temperatures.
Features
Properties
9.500MPa
120MPa
40kJ/m²
ISO 527-2
ISO 527-2
ISO 527-2
ISO 178
ISO 178
ISO 178
ISO 179-1/1eU
ISO 179-1/1eA
ISO 75
ISO 11357-3
ISO 11359-1/2
UL 94
FMVSS 302
ISO 1183
ISO 1110
ISO 294-4
Disclaimer
All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.