AKROTEK®
PK-VM 8 natural (6146)
PK
AKROTEK® PK-VM 8 natural (6146) - Polyketon, unreinforced, Tribology, friction and wear, chemical resistance, EU 10/2011, FDA 21 CFR
1.500MPa
60MPa
180kJ/m²
AKROTEK® PK-VM 8 natural (6146) - Polyketon, unreinforced, Tribology, friction and wear, chemical resistance, EU 10/2011, FDA 21 CFR
AKROMID®
B3 GF 15 grey (6270)
PA6 GF15
AKROMID® B3 GF 15 grey (6270) is a 15% glass fibre reinforced polyamide 6 with average stiffness and strength.
6.000MPa
110MPa
50kJ/m²
AKROMID® B3 GF 15 grey (6270) is a 15% glass fibre reinforced polyamide 6 with average stiffness and strength.
AKROLOY®
PA FGF 60 black (6765)
PA66 + PA6I/6T GF 60
AKROLOY® PA FGF 60 black (6765) - semi-aromatic polyamide blend, 60% flat glass fiber reinforced,improved properties 90° to the flow direction
20.000MPa
290MPa
90kJ/m²
AKROLOY® PA FGF 60 black (6765) - semi-aromatic polyamide blend, 60% flat glass fiber reinforced,improved properties 90° to the flow direction
AKROMID®
D3 GF 30 2 black (7026)
PA612 GF30
AKROMID® D3 GF 30 2 black (7026) - PA 6.12, glass fiber, UV stabilized, connector
9.500MPa
180MPa
95kJ/m²
AKROMID® D3 GF 30 2 black (7026) - PA 6.12, glass fiber, UV stabilized, connector
AKROMID®
B3 GF 40 5 black (7286)
PA6 GF40
AKROMID® B3 GF 40 5 black (7286) - 40% glass fiber reinforced PA 6, high heat stabilised, technical parts in industrial engineering and automotive industry
12.500MPa
200MPa
95kJ/m²
AKROMID® B3 GF 40 5 black (7286) - 40% glass fiber reinforced PA 6, high heat stabilised, technical parts in industrial engineering and automotive industry
AKROMID®
B3 1 FR orange (7698)
PA6 FR(30)
AKROMID® B3 1 FR orange (7698) - PA6, unreinforced, flame retardant, UL-listed, good surface, public transportation, new mobility.
3.600MPa
75MPa
NA
AKROMID® B3 1 FR orange (7698) - PA6, unreinforced, flame retardant, UL-listed, good surface, public transportation, new mobility.
AKROMID®
T9 GF 30 S1 black (7873)
PPA-I GF30
AKROMID® T9 GF 30 S1 black (7873) is a 30% glass fibre reinforced, cold impact strength polyphthalamide with medium stiffness and strength, as well as high chemical resistance. The compound is based on PA9T and has lower moisture uptake than conventional PA6T variants. This leads to a significantly higher consistency of the glass transition temperature and higher strength at elevated temperatures especially in conditioned state.
8.700MPa
165MPa
95kJ/m²
AKROMID® T9 GF 30 S1 black (7873) is a 30% glass fibre reinforced, cold impact strength polyphthalamide with medium stiffness and strength, as well as high chemical resistance. The compound is based on PA9T and has lower moisture uptake than conventional PA6T variants. This leads to a significantly higher consistency of the glass transition temperature and higher strength at elevated temperatures especially in conditioned state.
AKROMID®
T5 GF 20 8 black (6456)PPA GF20
AKROMID® T5 GF 20 8 black (6456) is a 20% glass fibre reinforced polyphthalamide with average rigidity and strength, as well as high temperature and chemical resistance. This aromatic PPA keeps mechanical performance even at elevated temperatures as well as moisture pic-up. The material fulfills the requirements according to ACS, WRAS and NSF 61. It is suitable for applications that are in contact with cold and hot drinking water. This material corresponds to the European food guideline EU 10/2011 and to the American FDA 21 CFR and is suitable for parts of kitchen and household appliances.
Regulatory
Properties
8.500MPa
160MPa
40kJ/m²
Mechanical Properties
Tensile modulus
ISO 527-2
Tensile stress at break
ISO 527-2
Tensile strain at break
ISO 527-2
Charpy impact strength
ISO 179-1/1eU
Thermal Properties
Melting temperature
ISO 11357-3
Flammability
Burning rate
UL 94
Burning rate (<100 mm/min)
FMVSS 302
General properties
Density
ISO 1183
Molding shrinkage
ISO 294-4
Disclaimer
All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.
Contact
Do you have any questions? We are happy to help.
Would you like to learn more about AKRO-PLASTIC GmbH? Contact us! We will be happy to help you.