Select your fitting and find the right compound for your intend
AKROMID®
A3 ICF 30 5 black (6495)
PA66 CF30
AKROMID® A3 ICF 30 5 black (6495) is a 30% carbon fibre reinforced, high heat stabilised polyamide 6.6 with high flexural strength and good sliding properties
23.000MPa
235MPa
50kJ/m²
AKROMID® A3 ICF 30 5 black (6495) is a 30% carbon fibre reinforced, high heat stabilised polyamide 6.6 with high flexural strength and good sliding properties
AKROMID®
B3 S1 black (7629)
PA6-I
AKROMID® B3 S1 black (7629) - PA 6 unreinforced and cold impact modified, for furniture and cunstruction industry, sports and leisure
1.700MPa
45MPa
180kJ/m²
AKROMID® B3 S1 black (7629) - PA 6 unreinforced and cold impact modified, for furniture and cunstruction industry, sports and leisure
AKROMID®
T9 GF 30 S1 black (7873)
PPA-I GF30
AKROMID® T9 GF 30 S1 black (7873) is a 30% glass fibre reinforced, cold impact strength polyphthalamide with medium stiffness and strength, as well as high chemical resistance. The compound is based on PA9T and has lower moisture uptake than conventional PA6T variants. This leads to a significantly higher consistency of the glass transition temperature and higher strength at elevated temperatures especially in conditioned state.
8.700MPa
165MPa
95kJ/m²
AKROMID® T9 GF 30 S1 black (7873) is a 30% glass fibre reinforced, cold impact strength polyphthalamide with medium stiffness and strength, as well as high chemical resistance. The compound is based on PA9T and has lower moisture uptake than conventional PA6T variants. This leads to a significantly higher consistency of the glass transition temperature and higher strength at elevated temperatures especially in conditioned state.
AKROLOY®
PA GF 60 beige (7632)
PA66+PA6I/6T GF60
AKROLOY® PA GF 60 beige(7632) is a 60% glass fibre reinforced, semi-aromatic polyamide-blend with very high stiffness and strength, even in conditioned state.
22.300MPa
265MPa
85kJ/m²
AKROLOY® PA GF 60 beige(7632) is a 60% glass fibre reinforced, semi-aromatic polyamide-blend with very high stiffness and strength, even in conditioned state.
AKROMID®
A3 GF 15 1 GIT black (4620)
PA66 GF15
AKROMID® A3 GF 15 1 GIT black (4620) - 15% Glasfaser, heat stabilised, easy flowing polyamide 6.6, gas injection technology, excellent surface
5.500MPa
125MPa
40kJ/m²
AKROMID® A3 GF 15 1 GIT black (4620) - 15% Glasfaser, heat stabilised, easy flowing polyamide 6.6, gas injection technology, excellent surface
AKROMID®
A3 2 S1 grey (5972)
PA66-I
AKROMID® A3 2 S1 grey (5972) - PA 6.6, unreinforced, impact modified, UV-stabilised, for connecting and fixing systems, automotive, electro, furniture
1.800MPa
45MPa
NA
AKROMID® A3 2 S1 grey (5972) - PA 6.6, unreinforced, impact modified, UV-stabilised, for connecting and fixing systems, automotive, electro, furniture
AKROMID®
B3 ICF 10 1 black (6194)
PA6 CF10
AKROMID® B3 ICF 10 1 black (6194) is a 10% carbon fibre reinforced, heat stabilised polyamide 6 with good sliding properties
8.500MPa
125MPa
45kJ/m²
AKROMID® B3 ICF 10 1 black (6194) is a 10% carbon fibre reinforced, heat stabilised polyamide 6 with good sliding properties
AKROMID®
AKROMID® NEXT G3 GF 30 1 L CR black (8314) is a 30% glass fiber reinforced PA 6.9/PP blend with high strength and stiffness. The partially bio-based grade is characterised by particularly low moisture absorption and high chemical resistance compared to classic PA 6 and PA 6.6. It is suitable for applications where weight reduction and sustainability are required. The material is certified according to REDcert². 33% of the fossil raw materials required for manufacturing this product were replaced by sustainable biomass-balanced PP (≙ allocation factor).
Features
Regulatory
Properties
8.000MPa
125MPa
65kJ/m²
ISO 527-2
ISO 527-2
ISO 527-2
ISO 179-1/1eU
ISO 179-1/1eA
ISO 11357-3
ISO 1183
ISO 1110
ISO 62
ISO 294-4
Disclaimer
All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.