AKROMID®

B3 GFM 10/20 1 black (2017)

PA6 (GF10+M20)

AKROMID® B3 GFM 10/20 1 black 950089 (2017) is a 10% glass fibre reinforced and 20% mineral filled, heat stabilised polyamide 6 with good surface and dimensional stability

Modulus

6.200MPa

Strength

110MPa

Impact

40kJ/m²

AKROMID® B3 GFM 10/20 1 black 950089 (2017) is a 10% glass fibre reinforced and 20% mineral filled, heat stabilised polyamide 6 with good surface and dimensional stability

AKROMID®

A3 GF 20 1 black (2307)

PA66 GF20

AKROMID® A3 GF 20 1 black (2307) is a 20% glass fibre reinforced and heat stabilised polyamide 6.6 with medium stiffness and strength.

Modulus

7.200MPa

Strength

160MPa

Impact

60kJ/m²

AKROMID® A3 GF 20 1 black (2307) is a 20% glass fibre reinforced and heat stabilised polyamide 6.6 with medium stiffness and strength.

AKROMID®

A3 GF 35 1 natural (2393)

PA66 GF35

AKROMID® A3 GF 35 1 natural (2393) - 35% glass fiber reinforced PA 6.6, heat stabilised, technical parts in industrial engineering and automotive industry

Modulus

11.600MPa

Strength

215MPa

Impact

92kJ/m²

AKROMID® A3 GF 35 1 natural (2393) - 35% glass fiber reinforced PA 6.6, heat stabilised, technical parts in industrial engineering and automotive industry

AKROMID®

UL
Preliminary

B3 1 FR grey (8051)

PA6 FR(30)

AKROMID® B3 1 FR grey (8051) - PA6, unreinforced, flame retardant, UL-listed, good surface, public transportation, new mobility.

Modulus

3.600MPa

Strength

75MPa

Impact

NA

AKROMID® B3 1 FR grey (8051) - PA6, unreinforced, flame retardant, UL-listed, good surface, public transportation, new mobility.

AKROMID®

Preliminary

T9 GF 30 grey (8134)

PPA GF30

AKROMID® T9 GF 30 grey (8134) - PPA, 50% glass fiber, high stiffness and strength, high temperature and chemical resistance, grey RAL 7047, E&E.

Modulus

10.000MPa

Strength

190MPa

Impact

70kJ/m²

AKROMID® T9 GF 30 grey (8134) - PPA, 50% glass fiber, high stiffness and strength, high temperature and chemical resistance, grey RAL 7047, E&E.

AKROLOY®

PARA ICF 40 black (6130)

PARA CF40

AKROLOY® PARA ICF 40 black (6130) is a 40% carbon fibre reinforced Polyarylamide with very high stiffness. The material offers a higher process stability as well as a better weld line performance than its predecessor (6128), while the colour depth is reduced.

Modulus

39.000MPa

Strength

280MPa

Impact

35kJ/m²

AKROLOY® PARA ICF 40 black (6130) is a 40% carbon fibre reinforced Polyarylamide with very high stiffness. The material offers a higher process stability as well as a better weld line performance than its predecessor (6128), while the colour depth is reduced.

AKROMID®

A3 GF 15 1 GIT black (4620)

PA66 GF15

AKROMID® A3 GF 15 1 GIT black (4620) - 15% Glasfaser, heat stabilised, easy flowing polyamide 6.6, gas injection technology, excellent surface

Modulus

5.500MPa

Strength

125MPa

Impact

40kJ/m²

AKROMID® A3 GF 15 1 GIT black (4620) - 15% Glasfaser, heat stabilised, easy flowing polyamide 6.6, gas injection technology, excellent surface

142434480

AKROLEN®

PP GFM 25/15 LA black (3143)PP (GF25+MD15)

AKROLEN® PP GFM 25/15 LA black (3143) is a 25% glass fibre reinforced, 15% mineralfilled, laser markable polypropylene with good surface and dimensional stability. This material is mainly used for thin wall housings for electronic parts in the automotive industry.

Features

laser markable
surface modified
low warpage

Properties

Modulus

6.500MPa

Strength

Na

Impact

45kJ/m²

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
6500 MPa

Tensile stress at break

ISO 527-2

50 mm/min | d.a.m.
75 MPa

Tensile strain at break

ISO 527-2

50 mm/min | d.a.m.
3,5 %

Flexural modulus

ISO 178

2 mm/min | d.a.m.
6600 MPa

Flexural strength

ISO 178

2 mm/min | d.a.m.
105 MPa

Flexural strain at break

ISO 178

2 mm/min | d.a.m.
3,5 %

Charpy impact strength

ISO 179-1/1eU

23°C | d.a.m.
30°C | d.a.m.
-
45 kJ/m²
45 kJ/m²

Charpy notched impact strength

ISO 179-1/1eA

23°C | d.a.m.
10 kJ/m²

Izod impact strength

ISO 180/1A

23°C | d.a.m.
10 kJ/m²

Ball indentation hardness

ISO 2039-1

358N/30s | d.a.m.
100 MPa

Thermal Properties

Temperature of deflection under load HDT/A

ISO 75

1,8 MPa
150 °C

Temperature of deflection under load HDT/B

ISO 75

0,45 MPa
163 °C

Melting temperature

ISO 11357-3

DSC, 10K/min
167 °C

Coefficient of linear thermal expansion

ISO 11359-1/2

23°C to 80°C | parallel
23°C to 80°C | transverse
0,2 10⁻⁴/K
1,25 10⁻⁴/K

Flammability

Burning rate

UL 94

1,6 mm Wall thickness
HB Class

Burning rate (<100 mm/min)

FMVSS 302

> 1 mm Thickness
+

General properties

Density

ISO 1183

23°C
1,21 g/cm³

Molding shrinkage

ISO 294-4

flow
transverse
0,1 - 0,3 %
0,4 - 0,6 %

Electrical Properties

Comparative tracking index

IEC 60112

Test liquid A
600 V

Dielectric strength

IEC 60243

3 mm
18 kV/mm

Rheological Properties

MVR

ISO 1133

230°C/2,16kg
13,5 cm³/10 min

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.

Contact

Do you have any questions? We are happy to help.

Would you like to learn more about AKRO-PLASTIC GmbH? Contact us! We will be happy to help you.

Learn more