AKROLOY®

PA GF 50 8 black (6732)

PA66+PA6I/6T GF50

AKROLOY® PA GF 50 8 black (6732) - semi-aromatic polyamide blend, 50% glass fiber reinforced, lower moisture uptake, high dimensional stability, metall replacement, FDA, EU10/2011, ACS

Modulus

17.500MPa

Strength

260MPa

Impact

105kJ/m²

AKROLOY® PA GF 50 8 black (6732) - semi-aromatic polyamide blend, 50% glass fiber reinforced, lower moisture uptake, high dimensional stability, metall replacement, FDA, EU10/2011, ACS

AKROMID®

B28 GF 30 6 LT black (6931)

PA6 GF30

AKROMID® B28 GF 30 6 LT black (6931) - 30% glass fibre reinforced PA6, easy flowing, inorganic high heat stabilised, laser-transparent

Modulus

9.800MPa

Strength

185MPa

Impact

90kJ/m²

AKROMID® B28 GF 30 6 LT black (6931) - 30% glass fibre reinforced PA6, easy flowing, inorganic high heat stabilised, laser-transparent

AKROMID®

B28 GM 10/20 1 LT black (7749)

PA6 (GF10+GB20)

AKROMID® B28 GM 10/20 1 LT black (7749) is a 10% glass fibre reinforced, 20% glass bead filled, heat stabilised, lasertransparent and laser markable polyamide 6 with good surface and low warpage

Modulus

6.300MPa

Strength

110MPa

Impact

40kJ/m²

AKROMID® B28 GM 10/20 1 LT black (7749) is a 10% glass fibre reinforced, 20% glass bead filled, heat stabilised, lasertransparent and laser markable polyamide 6 with good surface and low warpage

PRECITE®

Preliminary

P3 GF 30 4 black (8333)

PBT-I GF30

PRECITE®P3 GF 30 4 black (8333) - PBT, 30% GF, hydrolysis stabilised, high stiffness, high toughness, GMA free, low moisture absorption, dimensional stability.

Modulus

9.000MPa

Strength

115MPa

Impact

65kJ/m²

PRECITE®P3 GF 30 4 black (8333) - PBT, 30% GF, hydrolysis stabilised, high stiffness, high toughness, GMA free, low moisture absorption, dimensional stability.

AKROMID®

UL

C3 1 FR natural (8050)

PA66+PA6 FR(30)

AKROMID® C3 1 FR natural (8050) - PA6/6.6 blend, unreinforced, flame retardant, UL-listed, very good flowability, public transportation, new mobility.

Modulus

3.600MPa

Strength

77MPa

Impact

100kJ/m²

AKROMID® C3 1 FR natural (8050) - PA6/6.6 blend, unreinforced, flame retardant, UL-listed, very good flowability, public transportation, new mobility.

AKROTEK®

Preliminary

PK-VM GF 50 black (8688)

PK GF50

AKROTEK® PK-VM GF 50 black (8688) - Polyketon, 50% glass fibre reinforced, chemical and hydrolysis resistance

Modulus

14.500MPa

Strength

165MPa

Impact

60kJ/m²

AKROTEK® PK-VM GF 50 black (8688) - Polyketon, 50% glass fibre reinforced, chemical and hydrolysis resistance

AKROMID®

A3 GF 20 1 natural (1261)

PA66 GF20

AKROMID® A3 GF 20 1 natural (1261) is a 20% glass fibre reinforced and heat stabilised polyamide 6.6 with medium stiffness and strength and light inherent color..

Modulus

7.200MPa

Strength

160MPa

Impact

60kJ/m²

AKROMID® A3 GF 20 1 natural (1261) is a 20% glass fibre reinforced and heat stabilised polyamide 6.6 with medium stiffness and strength and light inherent color..

141424380

AKROMID®

Internal

A3 CF 30 5 black (8729)PA66 CF30

AKROMID® A3 CF 30 5 black (8729) is a 30% carbon fibre reinforced, high temperature stabilised polyamide 6.6 with elevated mechanical properties and good sliding properties.

Features

heat stabilised 160

Properties

Modulus

26.000MPa

Strength

300MPa

Impact

90kJ/m²

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
1 mm/min | conditioned
26000 MPa
17500 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
300 MPa
220 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
2 %
3,5 %

Flexural modulus

ISO 178

2 mm/min | d.a.m.
2 mm/min | conditioned
23000 MPa
17000 MPa

Flexural strength

ISO 178

2 mm/min | d.a.m.
2 mm/min | conditioned
400 MPa
300 MPa

Charpy impact strength

ISO 179-1/1eU

23°C | d.a.m.
23°C | conditioned
90 kJ/m²
110 kJ/m²

Charpy notched impact strength

ISO 179-1/1eA

23°C | d.a.m.
23°C | conditioned
40°C | d.a.m.
-
10 kJ/m²
13 kJ/m²
8 kJ/m²

Thermal Properties

Temperature of deflection under load HDT/A

ISO 75

1,8 MPa
254 °C

Melting temperature

ISO 11357-3

DSC, 10K/min
260 °C

Flammability

Burning rate

UL 94

1,6 mm Wall thickness
HB Class

Burning rate (<100 mm/min)

FMVSS 302

> 1 mm Thickness
+

General properties

Density

ISO 1183

23°C
1,26 g/cm³

Humidity absorption

ISO 1110

70°C, 62% r.H.
1,8 %

Molding shrinkage

ISO 294-4

flow
transverse
0,1 - 0,3 %
0,5 - 0,7 %

Electrical Properties

Volume resistivity IEC

DIN EN IEC 62631-3-2

d.a.m.
104 Ω x cm

Surface resistivity

DIN EN 62631-3-2

d.a.m.
104 Ω

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.

Contact

Do you have any questions? We are happy to help.

Would you like to learn more about AKRO-PLASTIC GmbH? Contact us! We will be happy to help you.

Learn more