AKROMID®

Preliminary

A28 GF 35 6 black (7278)

PA66 GF35

AKROMID® A28 GF 35 6 black (7278) - 35% glass fiber reinforced, inorganically highly heat-stabilized, easy-flowing polyamide 6.6 with high rigidity and strength, technical components in mechanical engineering and the automotive industry

Modulus

11.500MPa

Strength

210MPa

Impact

85kJ/m²

AKROMID® A28 GF 35 6 black (7278) - 35% glass fiber reinforced, inorganically highly heat-stabilized, easy-flowing polyamide 6.6 with high rigidity and strength, technical components in mechanical engineering and the automotive industry

AKROMID®

A3 GF 30 1 S3 black (3502)

PA66-I GF30

AKROMID® A3 GF 30 1 S3 black (3502) is a 30% glass fibre reinforced, heat stabilised, dry impact resistant polyamide 6.6 with high stiffness and strength

Modulus

8.000MPa

Strength

170MPa

Impact

100kJ/m²

AKROMID® A3 GF 30 1 S3 black (3502) is a 30% glass fibre reinforced, heat stabilised, dry impact resistant polyamide 6.6 with high stiffness and strength

AKROMID®

A3 GM 20/10 S1 black (4817)

PA66-I (GF20+GB10)

AKROMID® A3 GM 20/10 S1 black (4817) - PA 6.6, impact modified, glass fiber and glass beads reinforced, good surface, low warpage

Modulus

6.900MPa

Strength

130MPa

Impact

80kJ/m²

AKROMID® A3 GM 20/10 S1 black (4817) - PA 6.6, impact modified, glass fiber and glass beads reinforced, good surface, low warpage

AKROMID®

B3 ICF 30 black (5119)

PA6 CF30

AKROMID® B3 ICF 30 black (5119) is a 30% carbon fibre reinforced polyamide 6 with high flexural strength and good sliding properties

Modulus

23.000MPa

Strength

200MPa

Impact

55kJ/m²

AKROMID® B3 ICF 30 black (5119) is a 30% carbon fibre reinforced polyamide 6 with high flexural strength and good sliding properties

AKROLOY®

Preliminary

PA GF 30 natural (6412)

PA66+PA6I/6T GF30

AKROLOY® PA GF 30 natur (6412) is a 30% glass fibre reinforced, semi-aromatic polyamide blend with high stiffness and strength, even in conditioned state.

Modulus

10.200MPa

Strength

200MPa

Impact

70kJ/m²

AKROLOY® PA GF 30 natur (6412) is a 30% glass fibre reinforced, semi-aromatic polyamide blend with high stiffness and strength, even in conditioned state.

AKROLOY®

Preliminary

PA CF 40 1 black (8392)

PA66 + PA6I/6T CF40

AKROLOY® PA ICF 40 black (8392) is a 40% carbon fibre reinforced, semi-aromatic polyamide blend with high stiffness, good sliding properties and reduced moisture.

Modulus

30.300MPa

Strength

300MPa

Impact

70kJ/m²

AKROLOY® PA ICF 40 black (8392) is a 40% carbon fibre reinforced, semi-aromatic polyamide blend with high stiffness, good sliding properties and reduced moisture.

AKROMID®

Preliminary

B25 GF 50 LA black (8280)

PA6 GF50

AKROMID® B25 GF 50 LA black (8280) is a 50% glass fibre reinforced, easy flowing polyamide 6 with very high stiffness and strength, lasermarkable.

Modulus

15.500MPa

Strength

235MPa

Impact

100kJ/m²

AKROMID® B25 GF 50 LA black (8280) is a 50% glass fibre reinforced, easy flowing polyamide 6 with very high stiffness and strength, lasermarkable.

140414280

AKROMID®

C3 5 S3 black (8029)PA66+PA6

AKROMID® C3 5 S3 black (8029) is an unreinforced, impact modified polyamide 6.6/6 blend. It is characterised by higher dry impact strength compared to standard polyamide 6.6/6 blends while maintaining good flowability. Furthermore, the material is high heat stabilised and therefore perfectly suitable for connecting and fixing systems which are used at elevated temperatures in the automotive and electro industry.

Features

heat stabilised 130
impact modified
easy flow

Properties

Modulus

2.500MPa

Strength

65MPa

Impact

180kJ/m²

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
1 mm/min | conditioned
2500 MPa
900 MPa

Tensile stress at yield

ISO 527-2

50 mm/min | d.a.m.
50 mm/min | conditioned
65 MPa
45 MPa

Tensile strain at break

ISO 527-2

50 mm/min | d.a.m.
50 mm/min | conditioned
> 25 %
> 250 %

Flexural modulus

ISO 178

2 mm/min | d.a.m.
2100 MPa

Flexural strength

ISO 178

2 mm/min | d.a.m.
85 MPa

Charpy impact strength

ISO 179-1/1eU

23°C | d.a.m.
no break

Charpy notched impact strength

ISO 179-1/1eA

23°C | d.a.m.
23°C | conditioned
7 kJ/m²
23 kJ/m²

Thermal Properties

Temperature of deflection under load HDT/B

ISO 75

0,45 MPa
160 °C

Melting temperature

ISO 11357-3

DSC, 10K/min
260 °C

Flammability

Burning rate (<100 mm/min)

FMVSS 302

> 1 mm Thickness
+

General properties

Density

ISO 1183

23°C
1,12 g/cm³

Molding shrinkage

ISO 294-4

flow
transverse
1,3 - 1,5 %
1,5 - 1,7 %

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.

Contact

Do you have any questions? We are happy to help.

Would you like to learn more about AKRO-PLASTIC GmbH? Contact us! We will be happy to help you.

Learn more