AKROMIDĀ®
B3 GF 40 1 L black (4581)
PA6 + PP GF40
AKROMIDĀ® B3 GF 40 1 L black (4581) - PA6/PP-Blend 40% glass fibre reinforced with lower density, cost reduced, calcium chloride
11.000MPa
150MPa
70kJ/mĀ²
AKROMIDĀ® B3 GF 40 1 L black (4581) - PA6/PP-Blend 40% glass fibre reinforced with lower density, cost reduced, calcium chloride
AKROLOYĀ®
PA GF 30 natural (6412)
PA66+PA6I/6T GF30
AKROLOYĀ® PA GF 30 natur (6412) is a 30% glass fibre reinforced, semi-aromatic polyamide blend with high stiffness and strength, even in conditioned state.
10.200MPa
200MPa
70kJ/mĀ²
AKROLOYĀ® PA GF 30 natur (6412) is a 30% glass fibre reinforced, semi-aromatic polyamide blend with high stiffness and strength, even in conditioned state.
AKROMIDĀ®
A3 GF 30 6 black (6736)
PA66 GF30
AKROMIDĀ® A3 GF 30 6 black (6736) - PA 6.6 30% glass fiber reinforced, inorganic heat stabilised, technical parts in industrial engineering and in the automotive industry
10.000MPa
200MPa
75kJ/mĀ²
AKROMIDĀ® A3 GF 30 6 black (6736) - PA 6.6 30% glass fiber reinforced, inorganic heat stabilised, technical parts in industrial engineering and in the automotive industry
PRECITEĀ®
K GF 50 natural (7435)
PBT-PET- GF 50
PRECITEĀ® K GF 50 natural (7435) - PBT/PET blend, 50% glass fiber, dimensional stability, good surface, low moisture, very good strength, automotive, E&E, household, industry.
20.000MPa
175MPa
60kJ/mĀ²
PRECITEĀ® K GF 50 natural (7435) - PBT/PET blend, 50% glass fiber, dimensional stability, good surface, low moisture, very good strength, automotive, E&E, household, industry.
AKROMIDĀ®
T9 GF 50 natural (8334)
PPA GF50
AKROMIDĀ® T9 GF 50 natural (8334) is a 50% glass fibre reinforced polyphthalamide with heat stabilization, high rigidity and strength, as well as high temperature and chemical resistance. The compound is based on PA9T and has lower moisture uptake than conventional PA6T variants. This leads to a significantly higher consistency of the glass transition temperature and higher strength at elevated temperatures especially in conditioned state.
16.500MPa
250MPa
95kJ/mĀ²
AKROMIDĀ® T9 GF 50 natural (8334) is a 50% glass fibre reinforced polyphthalamide with heat stabilization, high rigidity and strength, as well as high temperature and chemical resistance. The compound is based on PA9T and has lower moisture uptake than conventional PA6T variants. This leads to a significantly higher consistency of the glass transition temperature and higher strength at elevated temperatures especially in conditioned state.
AKROLOYĀ®
PA CF 40 1 black (8392)
PA66 + PA6I/6T CF40
AKROLOYĀ® PA ICF 40 black (8392) is a 40% carbon fibre reinforced, semi-aromatic polyamide blend with high stiffness, good sliding properties and reduced moisture.
30.300MPa
300MPa
70kJ/mĀ²
AKROLOYĀ® PA ICF 40 black (8392) is a 40% carbon fibre reinforced, semi-aromatic polyamide blend with high stiffness, good sliding properties and reduced moisture.
AKROLOYĀ®
PA GF 60 white (7973)
PA66+PA6I/6T GF60
AKROLOYĀ® PA GF 60 white (7973) is a 60% glass fibre reinforced, easyflow, semi-aromatic polyamide-blend with very high stiffness and strength, even in conditioned state.
22.000MPa
270MPa
85kJ/mĀ²
AKROLOYĀ® PA GF 60 white (7973) is a 60% glass fibre reinforced, easyflow, semi-aromatic polyamide-blend with very high stiffness and strength, even in conditioned state.
AKROMIDĀ®
AKROMIDĀ® A3 GF 30 6 black (6736) is a 30% glass fiber reinforced polyamide 6.6. It is characterised by high stiffness and strength. Furthermore, the material is anorganically heat stabilised and therefore perfectly suitable for technical parts in industrial engineering and in the automotive industry which are exposed to higher temperatures.
Features
Properties
10.000MPa
200MPa
75kJ/mĀ²
ISO 527-2
ISO 527-2
ISO 527-2
ISO 179-1/1eU
ISO 75
ISO 11357-3
IEC 60216
FMVSS 302
ISO 1183
ISO 1110
ISO 294-4
Disclaimer
All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKROĀ®, AKROMIDĀ®, AKROLENĀ®, AKROLOYĀ®, AKROTEKĀ®, ICXĀ® and PRECITEĀ® are registered trademarks of the Feddersen Group.