AKROMIDĀ®
A28 GF 35 6 black (7278)
PA66 GF35
AKROMIDĀ® A28 GF 35 6 black (7278) - 35% glass fiber reinforced, inorganically highly heat-stabilized, easy-flowing polyamide 6.6 with high rigidity and strength, technical components in mechanical engineering and the automotive industry
11.500MPa
210MPa
85kJ/mĀ²
AKROMIDĀ® A28 GF 35 6 black (7278) - 35% glass fiber reinforced, inorganically highly heat-stabilized, easy-flowing polyamide 6.6 with high rigidity and strength, technical components in mechanical engineering and the automotive industry
AKROMIDĀ®
A3 GF 30 1 S3 black (3502)
PA66-I GF30
AKROMIDĀ® A3 GF 30 1 S3 black (3502) is a 30% glass fibre reinforced, heat stabilised, dry impact resistant polyamide 6.6 with high stiffness and strength
8.000MPa
170MPa
100kJ/mĀ²
AKROMIDĀ® A3 GF 30 1 S3 black (3502) is a 30% glass fibre reinforced, heat stabilised, dry impact resistant polyamide 6.6 with high stiffness and strength
AKROMIDĀ®
A3 GM 20/10 S1 black (4817)
PA66-I (GF20+GB10)
AKROMIDĀ® A3 GM 20/10 S1 black (4817) - PA 6.6, impact modified, glass fiber and glass beads reinforced, good surface, low warpage
6.900MPa
130MPa
80kJ/mĀ²
AKROMIDĀ® A3 GM 20/10 S1 black (4817) - PA 6.6, impact modified, glass fiber and glass beads reinforced, good surface, low warpage
AKROMIDĀ®
B3 ICF 30 black (5119)
PA6 CF30
AKROMIDĀ® B3 ICF 30 black (5119) is a 30% carbon fibre reinforced polyamide 6 with high flexural strength and good sliding properties
23.000MPa
200MPa
55kJ/mĀ²
AKROMIDĀ® B3 ICF 30 black (5119) is a 30% carbon fibre reinforced polyamide 6 with high flexural strength and good sliding properties
AKROLOYĀ®
PA GF 30 natural (6412)
PA66+PA6I/6T GF30
AKROLOYĀ® PA GF 30 natur (6412) is a 30% glass fibre reinforced, semi-aromatic polyamide blend with high stiffness and strength, even in conditioned state.
10.200MPa
200MPa
70kJ/mĀ²
AKROLOYĀ® PA GF 30 natur (6412) is a 30% glass fibre reinforced, semi-aromatic polyamide blend with high stiffness and strength, even in conditioned state.
AKROLOYĀ®
PA CF 40 1 black (8392)
PA66 + PA6I/6T CF40
AKROLOYĀ® PA ICF 40 black (8392) is a 40% carbon fibre reinforced, semi-aromatic polyamide blend with high stiffness, good sliding properties and reduced moisture.
30.300MPa
300MPa
70kJ/mĀ²
AKROLOYĀ® PA ICF 40 black (8392) is a 40% carbon fibre reinforced, semi-aromatic polyamide blend with high stiffness, good sliding properties and reduced moisture.
AKROMIDĀ®
B25 GF 50 LA black (8280)
PA6 GF50
AKROMIDĀ® B25 GF 50 LA black (8280) is a 50% glass fibre reinforced, easy flowing polyamide 6 with very high stiffness and strength, lasermarkable.
15.500MPa
235MPa
100kJ/mĀ²
AKROMIDĀ® B25 GF 50 LA black (8280) is a 50% glass fibre reinforced, easy flowing polyamide 6 with very high stiffness and strength, lasermarkable.
AKROMIDĀ®
A3 GF 30 1 S3 black (3502)PA66-I GF30
AKROMIDĀ® A3 GF 30 1 S3 black (3502) is a 30% glass fiber reinforced, impact modified Polyamide 6.6. It is characterised by high stiffness and strength as well as a higher impact strength compared to a standard PA 6.6 GF 30. Furthermore, the material is heat stabilised and therefore perfectly suitable for connecting and fixing systems which are used at elevated temperatures in the automotive and electro industry.
Features
Properties
8.000MPa
170MPa
100kJ/mĀ²
Mechanical Properties
Tensile modulus
ISO 527-2
Tensile stress at break
ISO 527-2
Tensile strain at break
ISO 527-2
Flexural modulus
ISO 178
Flexural strength
ISO 178
Flexural strain at break
ISO 178
Charpy impact strength
ISO 179-1/1eU
Charpy notched impact strength
ISO 179-1/1eA
Thermal Properties
Temperature of deflection under load HDT/A
ISO 75
Melting temperature
ISO 11357-3
Flammability
Burning rate
UL 94
Burning rate (<100 mm/min)
FMVSS 302
General properties
Density
ISO 1183
Molding shrinkage
ISO 294-4
Disclaimer
All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKROĀ®, AKROMIDĀ®, AKROLENĀ®, AKROLOYĀ®, AKROTEKĀ®, ICXĀ® and PRECITEĀ® are registered trademarks of the Feddersen Group.