Select your fitting and find the right compound for your intend
AKROMID®
B3 GF 40 1 L black (4581)
PA6 + PP GF40
AKROMID® B3 GF 40 1 L black (4581) - PA6/PP-Blend 40% glass fibre reinforced with lower density, cost reduced, calcium chloride
11.000MPa
150MPa
70kJ/m²
AKROMID® B3 GF 40 1 L black (4581) - PA6/PP-Blend 40% glass fibre reinforced with lower density, cost reduced, calcium chloride
AKROLOY®
PA GF 30 natural (6412)
PA66+PA6I/6T GF30
AKROLOY® PA GF 30 natur (6412) is a 30% glass fibre reinforced, semi-aromatic polyamide blend with high stiffness and strength, even in conditioned state.
10.200MPa
200MPa
70kJ/m²
AKROLOY® PA GF 30 natur (6412) is a 30% glass fibre reinforced, semi-aromatic polyamide blend with high stiffness and strength, even in conditioned state.
AKROMID®
A3 GF 30 6 black (6736)
PA66 GF30
AKROMID® A3 GF 30 6 black (6736) - PA 6.6 30% glass fiber reinforced, inorganic heat stabilised, technical parts in industrial engineering and in the automotive industry
10.000MPa
200MPa
75kJ/m²
AKROMID® A3 GF 30 6 black (6736) - PA 6.6 30% glass fiber reinforced, inorganic heat stabilised, technical parts in industrial engineering and in the automotive industry
PRECITE®
K GF 50 natural (7435)
PBT-PET- GF 50
PRECITE® K GF 50 natural (7435) - PBT/PET blend, 50% glass fiber, dimensional stability, good surface, low moisture, very good strength, automotive, E&E, household, industry.
20.000MPa
175MPa
60kJ/m²
PRECITE® K GF 50 natural (7435) - PBT/PET blend, 50% glass fiber, dimensional stability, good surface, low moisture, very good strength, automotive, E&E, household, industry.
AKROMID®
T9 GF 50 natural (8334)
PPA GF50
AKROMID® T9 GF 50 natural (8334) is a 50% glass fibre reinforced polyphthalamide with heat stabilization, high rigidity and strength, as well as high temperature and chemical resistance. The compound is based on PA9T and has lower moisture uptake than conventional PA6T variants. This leads to a significantly higher consistency of the glass transition temperature and higher strength at elevated temperatures especially in conditioned state.
16.500MPa
250MPa
95kJ/m²
AKROMID® T9 GF 50 natural (8334) is a 50% glass fibre reinforced polyphthalamide with heat stabilization, high rigidity and strength, as well as high temperature and chemical resistance. The compound is based on PA9T and has lower moisture uptake than conventional PA6T variants. This leads to a significantly higher consistency of the glass transition temperature and higher strength at elevated temperatures especially in conditioned state.
AKROLOY®
PA CF 40 1 black (8392)
PA66 + PA6I/6T CF40
AKROLOY® PA ICF 40 black (8392) is a 40% carbon fibre reinforced, semi-aromatic polyamide blend with high stiffness, good sliding properties and reduced moisture.
30.300MPa
300MPa
70kJ/m²
AKROLOY® PA ICF 40 black (8392) is a 40% carbon fibre reinforced, semi-aromatic polyamide blend with high stiffness, good sliding properties and reduced moisture.
AKROLOY®
PA GF 60 white (7973)
PA66+PA6I/6T GF60
AKROLOY® PA GF 60 white (7973) is a 60% glass fibre reinforced, easyflow, semi-aromatic polyamide-blend with very high stiffness and strength, even in conditioned state.
22.000MPa
270MPa
85kJ/m²
AKROLOY® PA GF 60 white (7973) is a 60% glass fibre reinforced, easyflow, semi-aromatic polyamide-blend with very high stiffness and strength, even in conditioned state.
AKROLEN®
AKROLEN® PP GFM 25/15 LA black (3143) is a 25% glass fibre reinforced, 15% mineralfilled, laser markable polypropylene with good surface and dimensional stability. This material is mainly used for thin wall housings for electronic parts in the automotive industry.
Features
Properties
6.500MPa
Na
45kJ/m²
ISO 527-2
ISO 527-2
ISO 527-2
ISO 178
ISO 178
ISO 178
ISO 179-1/1eU
ISO 179-1/1eA
ISO 180/1A
ISO 2039-1
ISO 75
ISO 75
ISO 11357-3
ISO 11359-1/2
UL 94
FMVSS 302
ISO 1183
ISO 294-4
IEC 60112
IEC 60243
ISO 1133
Disclaimer
All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.