AKROMIDĀ®

B28 GF 15 1 S3 black (7514)

PA6-I GF15

AKROMIDĀ® B28 GF 15 1 S3 black (7514) - PA6, 15% glass fibre reinforced, easy flowing and impact modified, for industrial engineering and automotive

Modulus

5.000MPa

Strength

110MPa

Impact

70kJ/mĀ²

AKROMIDĀ® B28 GF 15 1 S3 black (7514) - PA6, 15% glass fibre reinforced, easy flowing and impact modified, for industrial engineering and automotive

AKROMIDĀ®

Preliminary

B25 GF 50 LA black (8280)

PA6 GF50

AKROMIDĀ® B25 GF 50 LA black (8280) is a 50% glass fibre reinforced, easy flowing polyamide 6 with very high stiffness and strength, lasermarkable.

Modulus

15.500MPa

Strength

235MPa

Impact

100kJ/mĀ²

AKROMIDĀ® B25 GF 50 LA black (8280) is a 50% glass fibre reinforced, easy flowing polyamide 6 with very high stiffness and strength, lasermarkable.

AKROMIDĀ®

B3 GK 30 natural (2719)

PA6 GB30

AKROMIDĀ® B3 GK 30 natural (2719) - PA 6, 30% glass beads reinforced, good surface, low warpage

Modulus

4.400MPa

Strength

70MPa

Impact

30kJ/mĀ²

AKROMIDĀ® B3 GK 30 natural (2719) - PA 6, 30% glass beads reinforced, good surface, low warpage

AKROMIDĀ®

B3 GM 10/20 1 L black (4646)

PA6+PP (GF10+GB20)

AKROMIDĀ® B3 GM 10/20 1 L black (4646) - PA6/PP-Blend, 10% glass fibre reinforced, 20% glass bead, lower density, cost reduced, calcium chloride

Modulus

5.100MPa

Strength

88MPa

Impact

46kJ/mĀ²

AKROMIDĀ® B3 GM 10/20 1 L black (4646) - PA6/PP-Blend, 10% glass fibre reinforced, 20% glass bead, lower density, cost reduced, calcium chloride

AKROMIDĀ®

B28 GF 50 1 GIT black (4732)

PA6 GF50

AKROMIDĀ® B28 GF 50 1 GIT black (4732) is a 50% glass fibre reinforced, heat stabilised, easy flowing polyamide 6 with very high stiffness and strength for gas injection technology.

Modulus

16.700MPa

Strength

235MPa

Impact

105kJ/mĀ²

AKROMIDĀ® B28 GF 50 1 GIT black (4732) is a 50% glass fibre reinforced, heat stabilised, easy flowing polyamide 6 with very high stiffness and strength for gas injection technology.

AKROMIDĀ®

UL

C3 1 FR orange (7470)

PA66+PA6 FR(30)

AKROMIDĀ® C3 1 FR orange (7470) - PA6/6.6 blend, unreinforced, flame retardant, UL-listed, good flowability, RAL 2003, for high voltage components e-mobility.

Modulus

3.500MPa

Strength

76MPa

Impact

NA

AKROMIDĀ® C3 1 FR orange (7470) - PA6/6.6 blend, unreinforced, flame retardant, UL-listed, good flowability, RAL 2003, for high voltage components e-mobility.

AKROMIDĀ®

B3 GM 15/15 natural (3079)

PA6 (GF15+GB15)

AKROMIDĀ® B3 GM 15/15 natural (3079) is a 15% glass fibre and 15% glass bead reinforced polyamide 6 with good surface, low warpage and light inherent color

Modulus

7.200MPa

Strength

130MPa

Impact

64kJ/mĀ²

AKROMIDĀ® B3 GM 15/15 natural (3079) is a 15% glass fibre and 15% glass bead reinforced polyamide 6 with good surface, low warpage and light inherent color

139404180

AKROMIDĀ®

B3 GF 50 8 natural (4301)PA6 GF50

AKROMIDĀ® B3 GF 50 8 natural (4301) is a 50% glass fibre reinforced polyamide 6 with very high rigidity and strength. The material corresponds to the European food guideline EU 10/2011 and to the American FDA 21 CFR. This grade is suitable for parts of kitchen and household appliances.

Regulatory

eu102011fda

Properties

Modulus

17.000MPa

Strength

240MPa

Impact

100kJ/mĀ²

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
1 mm/min | conditioned
17000 MPa
11500 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
240 MPa
160 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
3 %
4,9 %

Flexural modulus

ISO 178

2 mm/min | d.a.m.
2 mm/min | conditioned
16000 MPa
11500 MPa

Flexural strength

ISO 178

2 mm/min | d.a.m.
2 mm/min | conditioned
360 MPa
250 MPa

Charpy impact strength

ISO 179-1/1eU

23Ā°C | d.a.m.
30Ā°C | d.a.m.
-
100 kJ/mĀ²
90 kJ/mĀ²

Thermal Properties

Temperature of deflection under load HDT/A

ISO 75

1,8 MPa
220 Ā°C

Temperature of deflection under load HDT/B

ISO 75

0,45 MPa
220 Ā°C

Temperature of deflection under load HDT/C

ISO 75

8 MPa
185 Ā°C

Melting temperature

ISO 11357-3

DSC, 10K/min
220 Ā°C

Coefficient of linear thermal expansion

ISO 11359-1/2

23Ā°C to 80Ā°C | parallel
23Ā°C to 80Ā°C | transverse
0,11 10ā»ā“/K
0,94 10ā»ā“/K

Flammability

Burning rate

UL 94

1,6 mm Wall thickness
HB Class

GWFI

IEC 60695-2-12

1,6 mm Wall thickness
650 Ā°C

Burning rate (<100 mm/min)

FMVSS 302

> 1 mm Thickness
+

General properties

Density

ISO 1183

23Ā°C
1,56 g/cmĀ³

Humidity absorption

ISO 1110

70Ā°C, 62% r.H.
1,3 - 1,6 %

Water absorption

ISO 62

23Ā°C, saturated
4,5 - 5,1 %

Molding shrinkage

ISO 294-4

flow
transverse
0,1 - 0,3 %
0,4 - 0,6 %

Electrical Properties

Volume resistivity IEC

DIN EN IEC 62631-3-2

d.a.m.
1013 ā„¦ x cm

Surface resistivity

DIN EN 62631-3-2

d.a.m.
1012 ā„¦

Comparative tracking index

IEC 60112

Test liquid A
550 V

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKROĀ®, AKROMIDĀ®, AKROLENĀ®, AKROLOYĀ®, AKROTEKĀ®, ICXĀ® and PRECITEĀ® are registered trademarks of the Feddersen Group.

Contact

Do you have any questions? We are happy to help.

Would you like to learn more about AKRO-PLASTIC GmbH? Contact us! We will be happy to help you.

Learn more