AKROMID®

UL
Preliminary

A3 GF 60 HU natural (6452)

PA66 GF60

AKROMID® A3 GF 60 HU natural (6452) is a 60% glass fibre reinforced and heat stabilised polyamide 6.6 with very high rigidity and strength and light inherent color

Modulus

20.500MPa

Strength

270MPa

Impact

105kJ/m²

AKROMID® A3 GF 60 HU natural (6452) is a 60% glass fibre reinforced and heat stabilised polyamide 6.6 with very high rigidity and strength and light inherent color

AKROMID®

D3 CGM 15/20 S1 black (6284)

PA612 (CF15+GF20)

AKROMID® D3 CGM 15/20 S1 black (6284) - PA 6.12, carbon fiber, glass fiber, impact modified, connector, electrical conductivity

Modulus

13.500MPa

Strength

145MPa

Impact

80kJ/m²

AKROMID® D3 CGM 15/20 S1 black (6284) - PA 6.12, carbon fiber, glass fiber, impact modified, connector, electrical conductivity

AKROMID®

B28 GM 10/20 1 LT black (7749)

PA6 (GF10+GB20)

AKROMID® B28 GM 10/20 1 LT black (7749) is a 10% glass fibre reinforced, 20% glass bead filled, heat stabilised, lasertransparent and laser markable polyamide 6 with good surface and low warpage

Modulus

6.300MPa

Strength

110MPa

Impact

40kJ/m²

AKROMID® B28 GM 10/20 1 LT black (7749) is a 10% glass fibre reinforced, 20% glass bead filled, heat stabilised, lasertransparent and laser markable polyamide 6 with good surface and low warpage

PRECITE®

Preliminary

P3 GF 30 4 black (8333)

PBT-I GF30

PRECITE®P3 GF 30 4 black (8333) - PBT, 30% GF, hydrolysis stabilised, high stiffness, high toughness, GMA free, low moisture absorption, dimensional stability.

Modulus

9.000MPa

Strength

115MPa

Impact

65kJ/m²

PRECITE®P3 GF 30 4 black (8333) - PBT, 30% GF, hydrolysis stabilised, high stiffness, high toughness, GMA free, low moisture absorption, dimensional stability.

AKROMID®

B3 GK 50 natural (3690)

PA6 GB50

AKROMID® B3 GK 50 natural (3690) - PA 6, 50% glass beads reinforced, good surface, low warpage

Modulus

5.700MPa

Strength

75MPa

Impact

42kJ/m²

AKROMID® B3 GK 50 natural (3690) - PA 6, 50% glass beads reinforced, good surface, low warpage

AKROMID®

B3 GF 45 1 black (3851)

PA6 GF45

AKROMID® B3 GF 45 1 black (3851) is a 45% glass fibre reinforced, heat stabilised polyamide 6 with very high rigidity and strength

Modulus

14.500MPa

Strength

200MPa

Impact

110kJ/m²

AKROMID® B3 GF 45 1 black (3851) is a 45% glass fibre reinforced, heat stabilised polyamide 6 with very high rigidity and strength

AKROMID®

B3 CGM 6/20 black (4362)

PA6 (CF6+GF20)

AKROMID® B3 CGM 6/20 black (4362) - PA 6, 20% glass fiber reinforced, 6% carbon fiber reinforced, heat stabilized, electrical conductivity

Modulus

11.000MPa

Strength

175MPa

Impact

60kJ/m²

AKROMID® B3 CGM 6/20 black (4362) - PA 6, 20% glass fiber reinforced, 6% carbon fiber reinforced, heat stabilized, electrical conductivity

139404180

AKROMID®

B3 GFM 10/20 1 black (2017)PA6 (GF10+M20)

AKROMID® B3 GFM 10/20 1 black 950089 (2017) is a 10% glass fibre reinforced and 20% mineral filled, heat stabilised polyamide 6 with good surface and dimensional stability

Features

heat stabilised 130
surface modified
low warpage

Properties

Modulus

6.200MPa

Strength

110MPa

Impact

40kJ/m²

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
6200 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.
110 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.
3,5 %

Flexural modulus

ISO 178

2 mm/min | d.a.m.
4000 MPa

Flexural strength

ISO 178

2 mm/min | d.a.m.
170 MPa

Flexural strain at break

ISO 178

2 mm/min | d.a.m.
5,5 %

Charpy impact strength

ISO 179-1/1eU

23°C | d.a.m.
30°C | d.a.m.
-
40 kJ/m²
40 kJ/m²

Charpy notched impact strength

ISO 179-1/1eA

23°C | d.a.m.
3 kJ/m²

Thermal Properties

Temperature of deflection under load HDT/A

ISO 75

1,8 MPa
185 °C

Temperature of deflection under load HDT/B

ISO 75

0,45 MPa
215 °C

Temperature of deflection under load HDT/C

ISO 75

8 MPa
55 °C

Melting temperature

ISO 11357-3

DSC, 10K/min
222 °C

Flammability

Burning rate

UL 94

1,6 mm Wall thickness
HB Class

Burning rate (<100 mm/min)

FMVSS 302

> 1 mm Thickness
+

General properties

Density

ISO 1183

23°C
1,36 g/cm³

Molding shrinkage

ISO 294-4

flow
transverse
0,6 %
0,8 %

Rheological Properties

Flowability

AKRO

1 mm Thickness
2 mm Thickness
170 mm
390 mm

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.

Contact

Do you have any questions? We are happy to help.

Would you like to learn more about AKRO-PLASTIC GmbH? Contact us! We will be happy to help you.

Learn more