AKROMID®

A3 GF 50 1 EN black (5737)

PA66 GF50

AKROMID® A3 GF 50 1 EN black (5737) - 50% glass fiber reinforced PA 6.6, electrically neutral and heat stabilised, technical parts in industrial engineering and automotive industry

Modulus

16.700MPa

Strength

250MPa

Impact

105kJ/m²

AKROMID® A3 GF 50 1 EN black (5737) - 50% glass fiber reinforced PA 6.6, electrically neutral and heat stabilised, technical parts in industrial engineering and automotive industry

AKROLOY®

Preliminary

PA GF 30 natural (6412)

PA66+PA6I/6T GF30

AKROLOY® PA GF 30 natur (6412) is a 30% glass fibre reinforced, semi-aromatic polyamide blend with high stiffness and strength, even in conditioned state.

Modulus

10.200MPa

Strength

200MPa

Impact

70kJ/m²

AKROLOY® PA GF 30 natur (6412) is a 30% glass fibre reinforced, semi-aromatic polyamide blend with high stiffness and strength, even in conditioned state.

AKROMID®

UL
Preliminary

A3 GF 60 HU natural (6452)

PA66 GF60

AKROMID® A3 GF 60 HU natural (6452) is a 60% glass fibre reinforced and heat stabilised polyamide 6.6 with very high rigidity and strength and light inherent color

Modulus

20.500MPa

Strength

270MPa

Impact

105kJ/m²

AKROMID® A3 GF 60 HU natural (6452) is a 60% glass fibre reinforced and heat stabilised polyamide 6.6 with very high rigidity and strength and light inherent color

AKROMID®

B28 GF 30 6 LT black (6931)

PA6 GF30

AKROMID® B28 GF 30 6 LT black (6931) - 30% glass fibre reinforced PA6, easy flowing, inorganic high heat stabilised, laser-transparent

Modulus

9.800MPa

Strength

185MPa

Impact

90kJ/m²

AKROMID® B28 GF 30 6 LT black (6931) - 30% glass fibre reinforced PA6, easy flowing, inorganic high heat stabilised, laser-transparent

PRECITE®

P3 GF 50 natural (6944)

PBT GF 50

PRECITE® P3 GF 50 natural (6944) is a 50% glass fibre reinforced, medium viscous poly(butylene terephthalate) (PBT) with very high stiffness and toughness as well as high dimensional and chemical resistance.

Modulus

17.000MPa

Strength

185MPa

Impact

60kJ/m²

PRECITE® P3 GF 50 natural (6944) is a 50% glass fibre reinforced, medium viscous poly(butylene terephthalate) (PBT) with very high stiffness and toughness as well as high dimensional and chemical resistance.

AKROMID®

B3 GK 30 natural (2719)

PA6 GB30

AKROMID® B3 GK 30 natural (2719) - PA 6, 30% glass beads reinforced, good surface, low warpage

Modulus

4.400MPa

Strength

70MPa

Impact

30kJ/m²

AKROMID® B3 GK 30 natural (2719) - PA 6, 30% glass beads reinforced, good surface, low warpage

AKROMID®

B28 GF 60 9 black (4662)

PA6 GF60

AKROMID® B28 GF 60 9 black (4662) is a 60% glass fibre reinforced, process improved, easy flowing polyamide 6 with very high stiffness and strength as well as improved surface quality. Colored without carbon black.

Modulus

21.000MPa

Strength

250MPa

Impact

90kJ/m²

AKROMID® B28 GF 60 9 black (4662) is a 60% glass fibre reinforced, process improved, easy flowing polyamide 6 with very high stiffness and strength as well as improved surface quality. Colored without carbon black.

138394080

AKROTEK®

PK-HM natural (7536)PK

PK-HM natural (7536) is an unreinforced, purified Polyketone with average flowability. The outstanding friction and wear properties enable the use for demanding components exposed to tribological stress. PK is characterized by its outstanding media resistance, which qualifies it to be used for components that are in contact with chemicals. This grade is especially designed for extrusion process.

Features

hydrolysis / chemically stabilised

Properties

Modulus

1.400MPa

Strength

60MPa

Impact

180kJ/m²

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
1 mm/min | conditioned
1400 MPa
1400 MPa

Tensile stress at yield

ISO 527-2

50 mm/min | d.a.m.
50 mm/min | conditioned
60 MPa
60 MPa

Tensile strain at break

ISO 527-2

50 mm/min | d.a.m.
50 mm/min | conditioned
> 300 %
> 300 %

Flexural modulus

ISO 178

2 mm/min | d.a.m.
2 mm/min | conditioned
1600 MPa
1200 MPa

Flexural strength

ISO 178

2 mm/min | d.a.m.
2 mm/min | conditioned
60 MPa
60 MPa

Charpy impact strength

ISO 179-1/1eU

23°C | d.a.m.
23°C | conditioned
no break
no break

Charpy notched impact strength

ISO 179-1/1eA

23°C | d.a.m.
23°C | conditioned
15 kJ/m²
15 kJ/m²

Thermal Properties

Temperature of deflection under load HDT/A

ISO 75

1,8 MPa
100 °C

Temperature of deflection under load HDT/B

ISO 75

0,45 MPa
190 °C

Melting temperature

ISO 11357-3

DSC, 10K/min
220 °C

Flammability

Burning rate

UL 94

UL
1,6 mm Wall thickness
HB Class

Burning rate (<100 mm/min)

FMVSS 302

> 1 mm Thickness
+

General properties

Density

ISO 1183

23°C
1,24 g/cm³

Humidity absorption

ISO 1110

70°C, 62% r.H.
0,8 - 0,9 %

Water absorption

ISO 62

23°C, saturated
2,2 %

Molding shrinkage

ISO 294-4

flow
transverse
1,4 - 1,6 %
1,5 - 1,7 %

Rheological Properties

MVR

ISO 1133

240°C/2,16kg
6 cm³/10 min

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.

Contact

Do you have any questions? We are happy to help.

Would you like to learn more about AKRO-PLASTIC GmbH? Contact us! We will be happy to help you.

Learn more