AKROMID®

B28 GF 15 1 S3 black (7514)

PA6-I GF15

AKROMID® B28 GF 15 1 S3 black (7514) - PA6, 15% glass fibre reinforced, easy flowing and impact modified, for industrial engineering and automotive

Modulus

5.000MPa

Strength

110MPa

Impact

70kJ/m²

AKROMID® B28 GF 15 1 S3 black (7514) - PA6, 15% glass fibre reinforced, easy flowing and impact modified, for industrial engineering and automotive

AKROLEN®

PP GFM 25/15 LA black (3143)

PP (GF25+MD15)

AKROLEN® PP GFM 25/15 LA black (3143) - 25% glass fibre reinforced, 15% mineralfilled, laser markable polypropylene with good surface and dimensional stability.

Modulus

6.500MPa

Strength

NA

Impact

45kJ/m²

AKROLEN® PP GFM 25/15 LA black (3143) - 25% glass fibre reinforced, 15% mineralfilled, laser markable polypropylene with good surface and dimensional stability.

AKROMID®

C3 GF 30 5 XTC natural (4499)

PA66 + PA6 GF 30

AKROMID® C3 GF 30 5 XTC natural (4499) is a 30% glass fibre reinforced, high temperature stabilised polaymide 6.6/6 - Blend with high stiffness and strength and extra high temperature tolerance.

Modulus

9.500MPa

Strength

185MPa

Impact

95kJ/m²

AKROMID® C3 GF 30 5 XTC natural (4499) is a 30% glass fibre reinforced, high temperature stabilised polaymide 6.6/6 - Blend with high stiffness and strength and extra high temperature tolerance.

AKROMID®

A28 GF 30 9 black (4915)

PA66 GF30

AKROMID® A28 GF 30 9 black (4915) - PA 6.6, 30% glassfiber reinforced, easy flow, process improved, technical parts in industrial engineering and automotive industry

Modulus

9.600MPa

Strength

200MPa

Impact

70kJ/m²

AKROMID® A28 GF 30 9 black (4915) - PA 6.6, 30% glassfiber reinforced, easy flow, process improved, technical parts in industrial engineering and automotive industry

AKROMID®

UL

C3 1 FR black (5266)

PA66+PA6 FR (30)

AKROMID® C3 1 FR black (5266) - PA6/6.6 blend, unreinforced, flame retardant, UL-listed, good flowability, public transportation, new mobility.

Modulus

3.400MPa

Strength

75MPa

Impact

100kJ/m²

AKROMID® C3 1 FR black (5266) - PA6/6.6 blend, unreinforced, flame retardant, UL-listed, good flowability, public transportation, new mobility.

AKROMID®

UL
Preliminary

A3 GF 30 FR natural (7087)

PA66 GF30 FR(40)

AKROMID® A3 GF 30 FR natural (7087) is a 30% glass fibre reinforced, halogen free flame retardant polyamide 6.6 listed at UL in all colors.

Modulus

10.000MPa

Strength

140MPa

Impact

61kJ/m²

AKROMID® A3 GF 30 FR natural (7087) is a 30% glass fibre reinforced, halogen free flame retardant polyamide 6.6 listed at UL in all colors.

AKROMID®

B3 GF 45 1 black (3851)

PA6 GF45

AKROMID® B3 GF 45 1 black (3851) is a 45% glass fibre reinforced, heat stabilised polyamide 6 with very high rigidity and strength

Modulus

14.500MPa

Strength

200MPa

Impact

110kJ/m²

AKROMID® B3 GF 45 1 black (3851) is a 45% glass fibre reinforced, heat stabilised polyamide 6 with very high rigidity and strength

136373880

AKROMID®

Preliminary

NEXT U28 ICF 30 1 black (8233)PA11 CF30

AKROMID® NEXT U28 ICF 30 1 black (8233) is a Polyamide 11 reinforced with 30% recycled carbon fibre. The PA 11 is made from castor seed oil (bio-based content > 92%). The compound's low density as well as excellent ductility even at lower temperatures combined with high stiffness and strength enable the use for demanding applications, e.g., for lightweight construction or sports & leisure.

Features

heat stabilised 130
recycled content
reduced density
reduced moisture
3D printing / additive manufacturing
Sports & leisure
lightweight construction

Properties

Modulus

15.300MPa

Strength

165MPa

Impact

75kJ/m²

Sustainability

Biobased carbon content

52 %

Recycled content

30 %

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
1 mm/min | conditioned
15300 MPa
10900 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
165 MPa
140 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
4,8 %
4,8 %

Flexural modulus

ISO 178

2 mm/min | d.a.m.
2 mm/min | conditioned
15000 MPa
12000 MPa

Flexural strength

ISO 178

2 mm/min | d.a.m.
2 mm/min | conditioned
260 MPa
220 MPa

Flexural strain at break

ISO 178

2 mm/min | d.a.m.
2 mm/min | conditioned
3,7 %
4,2 %

Charpy impact strength

ISO 179-1/1eU

23°C | d.a.m.
23°C | conditioned
30°C | d.a.m.
-
30°C | conditioned
-
75 kJ/m²
70 kJ/m²
70 kJ/m²
65 kJ/m²

Charpy notched impact strength

ISO 179-1/1eA

23°C | d.a.m.
23°C | conditioned
30°C | d.a.m.
-
30°C | conditioned
-
13 kJ/m²
12 kJ/m²
9 kJ/m²
8 kJ/m²

Thermal Properties

Temperature of deflection under load HDT/A

ISO 75

1,8 MPa
180 °C

Melting temperature

ISO 11357-3

DSC, 10K/min
189 °C

General properties

Density

ISO 1183

23°C
1,22 g/cm³

Humidity absorption

ISO 1110

70°C, 62% r.H.
0,7 - 0,9 %

Water absorption

ISO 62

23°C, saturated
1,3 - 1,7 %

Molding shrinkage

ISO 294-4

flow
transverse
0,3 - 0,5 %
0,7 - 0,9 %

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.