AKROMID®

B28 GF 15 1 S3 black (7514)

PA6-I GF15

AKROMID® B28 GF 15 1 S3 black (7514) - PA6, 15% glass fibre reinforced, easy flowing and impact modified, for industrial engineering and automotive

Modulus

5.000MPa

Strength

110MPa

Impact

70kJ/m²

AKROMID® B28 GF 15 1 S3 black (7514) - PA6, 15% glass fibre reinforced, easy flowing and impact modified, for industrial engineering and automotive

AKROLEN®

PP GFM 25/15 LA black (3143)

PP (GF25+MD15)

AKROLEN® PP GFM 25/15 LA black (3143) - 25% glass fibre reinforced, 15% mineralfilled, laser markable polypropylene with good surface and dimensional stability.

Modulus

6.500MPa

Strength

NA

Impact

45kJ/m²

AKROLEN® PP GFM 25/15 LA black (3143) - 25% glass fibre reinforced, 15% mineralfilled, laser markable polypropylene with good surface and dimensional stability.

AKROMID®

C3 GF 30 5 XTC natural (4499)

PA66 + PA6 GF 30

AKROMID® C3 GF 30 5 XTC natural (4499) is a 30% glass fibre reinforced, high temperature stabilised polaymide 6.6/6 - Blend with high stiffness and strength and extra high temperature tolerance.

Modulus

9.500MPa

Strength

185MPa

Impact

95kJ/m²

AKROMID® C3 GF 30 5 XTC natural (4499) is a 30% glass fibre reinforced, high temperature stabilised polaymide 6.6/6 - Blend with high stiffness and strength and extra high temperature tolerance.

AKROMID®

A28 GF 30 9 black (4915)

PA66 GF30

AKROMID® A28 GF 30 9 black (4915) - PA 6.6, 30% glassfiber reinforced, easy flow, process improved, technical parts in industrial engineering and automotive industry

Modulus

9.600MPa

Strength

200MPa

Impact

70kJ/m²

AKROMID® A28 GF 30 9 black (4915) - PA 6.6, 30% glassfiber reinforced, easy flow, process improved, technical parts in industrial engineering and automotive industry

AKROMID®

UL

C3 1 FR black (5266)

PA66+PA6 FR (30)

AKROMID® C3 1 FR black (5266) - PA6/6.6 blend, unreinforced, flame retardant, UL-listed, good flowability, public transportation, new mobility.

Modulus

3.400MPa

Strength

75MPa

Impact

100kJ/m²

AKROMID® C3 1 FR black (5266) - PA6/6.6 blend, unreinforced, flame retardant, UL-listed, good flowability, public transportation, new mobility.

AKROMID®

UL
Preliminary

A3 GF 30 FR natural (7087)

PA66 GF30 FR(40)

AKROMID® A3 GF 30 FR natural (7087) is a 30% glass fibre reinforced, halogen free flame retardant polyamide 6.6 listed at UL in all colors.

Modulus

10.000MPa

Strength

140MPa

Impact

61kJ/m²

AKROMID® A3 GF 30 FR natural (7087) is a 30% glass fibre reinforced, halogen free flame retardant polyamide 6.6 listed at UL in all colors.

AKROMID®

B3 GF 45 1 black (3851)

PA6 GF45

AKROMID® B3 GF 45 1 black (3851) is a 45% glass fibre reinforced, heat stabilised polyamide 6 with very high rigidity and strength

Modulus

14.500MPa

Strength

200MPa

Impact

110kJ/m²

AKROMID® B3 GF 45 1 black (3851) is a 45% glass fibre reinforced, heat stabilised polyamide 6 with very high rigidity and strength

136373880

AKROLOY®

PARA ICF 40 black (6130)PARA CF40

AKROLOY® PARA ICF 40 black (6130) is a 40% carbon fibre reinforced Polyarylamide with very high stiffness. The material offers a higher process stability as well as a better weld line performance than its predecessor (6128), while the colour depth is reduced.

Features

tribological modified

Properties

Modulus

39.000MPa

Strength

280MPa

Impact

35kJ/m²

Sustainability

Recycled content

40 %

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
1 mm/min | conditioned
39000 MPa
38000 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
280 MPa
255 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
1,0 %
1,0 %

Flexural modulus

ISO 178

2 mm/min | d.a.m.
2 mm/min | conditioned
37000 MPa
35000 MPa

Flexural strength

ISO 178

2 mm/min | d.a.m.
2 mm/min | conditioned
420 MPa
360 MPa

Charpy impact strength

ISO 179-1/1eU

23°C | d.a.m.
30°C | d.a.m.
-
35 kJ/m²
35 kJ/m²

Charpy notched impact strength

ISO 179-1/1eA

23°C | d.a.m.
30°C | d.a.m.
-
6 kJ/m²
6 kJ/m²

Thermal Properties

Temperature of deflection under load HDT/A

ISO 75

1,8 MPa
230 °C

Melting temperature

ISO 11357-3

DSC, 10K/min
235 °C

Flammability

Burning rate

UL 94

1,6 mm Wall thickness
HB Class

Burning rate (<100 mm/min)

FMVSS 302

> 1 mm Thickness
+

General properties

Density

ISO 1183

23°C
1,4 g/cm³

Humidity absorption

ISO 1110

70°C, 62% r.H.
1,02 %

Molding shrinkage

ISO 294-4

flow
transverse
0,1 - 0,2 %
0,2 - 0,4 %

Electrical Properties

Volume resistivity IEC

DIN EN IEC 62631-3-2

d.a.m.
conditioned
104 Ω x cm
104 Ω x cm

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.

Contact

Do you have any questions? We are happy to help.

Would you like to learn more about AKRO-PLASTIC GmbH? Contact us! We will be happy to help you.

Learn more