HEADER Granulat 1920x700

Find the right compound

Select your fitting and find the right compound for your intend

Tensile Modulusin MPa
Tensile Strengthin MPa
Charpy impact strengthin kJ/mĀ²
558 Compounds found
Recommended Ā 
Tensile Modulus
Tensile Strength
Charpy impact strength
Description

AKROMIDĀ®

B28 GF 15 1 S3 black (7514)

PA6-I GF15

AKROMIDĀ® B28 GF 15 1 S3 black (7514) - PA6, 15% glass fibre reinforced, easy flowing and impact modified, for industrial engineering and automotive

Modulus

5.000MPa

Strength

110MPa

Impact

70kJ/mĀ²

AKROMIDĀ® B28 GF 15 1 S3 black (7514) - PA6, 15% glass fibre reinforced, easy flowing and impact modified, for industrial engineering and automotive

AKROLENĀ®

PP GFM 25/15 LA black (3143)

PP (GF25+MD15)

AKROLENĀ® PP GFM 25/15 LA black (3143) - 25% glass fibre reinforced, 15% mineralfilled, laser markable polypropylene with good surface and dimensional stability.

Modulus

6.500MPa

Strength

NA

Impact

45kJ/mĀ²

AKROLENĀ® PP GFM 25/15 LA black (3143) - 25% glass fibre reinforced, 15% mineralfilled, laser markable polypropylene with good surface and dimensional stability.

AKROMIDĀ®

C3 GF 30 5 XTC natural (4499)

PA66 + PA6 GF 30

AKROMIDĀ® C3 GF 30 5 XTC natural (4499) is a 30% glass fibre reinforced, high temperature stabilised polaymide 6.6/6 - Blend with high stiffness and strength and extra high temperature tolerance.

Modulus

9.500MPa

Strength

185MPa

Impact

95kJ/mĀ²

AKROMIDĀ® C3 GF 30 5 XTC natural (4499) is a 30% glass fibre reinforced, high temperature stabilised polaymide 6.6/6 - Blend with high stiffness and strength and extra high temperature tolerance.

AKROMIDĀ®

A28 GF 30 9 black (4915)

PA66 GF30

AKROMIDĀ® A28 GF 30 9 black (4915) - PA 6.6, 30% glassfiber reinforced, easy flow, process improved, technical parts in industrial engineering and automotive industry

Modulus

9.600MPa

Strength

200MPa

Impact

70kJ/mĀ²

AKROMIDĀ® A28 GF 30 9 black (4915) - PA 6.6, 30% glassfiber reinforced, easy flow, process improved, technical parts in industrial engineering and automotive industry

AKROMIDĀ®

UL

C3 1 FR black (5266)

PA66+PA6 FR (30)

AKROMIDĀ® C3 1 FR black (5266) - PA6/6.6 blend, unreinforced, flame retardant, UL-listed, good flowability, public transportation, new mobility.

Modulus

3.400MPa

Strength

75MPa

Impact

100kJ/mĀ²

AKROMIDĀ® C3 1 FR black (5266) - PA6/6.6 blend, unreinforced, flame retardant, UL-listed, good flowability, public transportation, new mobility.

AKROMIDĀ®

UL
Preliminary

A3 GF 30 FR natural (7087)

PA66 GF30 FR(40)

AKROMIDĀ® A3 GF 30 FR natural (7087) is a 30% glass fibre reinforced, halogen free flame retardant polyamide 6.6 listed at UL in all colors.

Modulus

10.000MPa

Strength

140MPa

Impact

61kJ/mĀ²

AKROMIDĀ® A3 GF 30 FR natural (7087) is a 30% glass fibre reinforced, halogen free flame retardant polyamide 6.6 listed at UL in all colors.

AKROMIDĀ®

B3 GF 45 1 black (3851)

PA6 GF45

AKROMIDĀ® B3 GF 45 1 black (3851) is a 45% glass fibre reinforced, heat stabilised polyamide 6 with very high rigidity and strength

Modulus

14.500MPa

Strength

200MPa

Impact

110kJ/mĀ²

AKROMIDĀ® B3 GF 45 1 black (3851) is a 45% glass fibre reinforced, heat stabilised polyamide 6 with very high rigidity and strength

136373880

AKROMIDĀ®

B3 GF 60 1 black (4644)PA6 GF60

AKROMIDĀ® B3 GF 60 1 black (4644) is a 60% glass fiber reinforced, heat stabilised polyamide 6. It is characterised by an improved flowability compared to a standard PA 6 GF 60. Furthermore, the material impresses with its high stiffness and strength. It is therefore perfectly suitable for technical applications in industrial engineering and in the automotive industry.

Features

heat stabilised 130
easy flow

Properties

Modulus

21.000MPa

Strength

250MPa

Impact

90kJ/mĀ²

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
1 mm/min | conditioned
21000 MPa
13500 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
250 MPa
160 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
2,5 %
3,5 %

Flexural modulus

ISO 178

2 mm/min | d.a.m.
19000 MPa

Flexural strength

ISO 178

2 mm/min | d.a.m.
370 MPa

Charpy impact strength

ISO 179-1/1eU

23Ā°C | d.a.m.
23Ā°C | conditioned
30Ā°C | d.a.m.
-
90 kJ/mĀ²
95 kJ/mĀ²
90 kJ/mĀ²

Charpy notched impact strength

ISO 179-1/1eA

23Ā°C | d.a.m.
23Ā°C | conditioned
30Ā°C | d.a.m.
-
20 kJ/mĀ²
25 kJ/mĀ²
20 kJ/mĀ²

Thermal Properties

Temperature of deflection under load HDT/A

ISO 75

1,8 MPa
220 Ā°C

Temperature of deflection under load HDT/B

ISO 75

0,45 MPa
220 Ā°C

Melting temperature

ISO 11357-3

DSC, 10K/min
220 Ā°C

Coefficient of linear thermal expansion

ISO 11359-1/2

23Ā°C to 80Ā°C | parallel
23Ā°C to 80Ā°C | transverse
0,13 10ā»ā“/K
0,60 10ā»ā“/K

Flammability

Burning rate

UL 94

0,8 mm Wall thickness
HB Class

GWFI

IEC 60695-2-12

1,6 mm Wall thickness
650 Ā°C

GWIT

IEC 60695-2-13

1,6 mm Wall thickness
675 Ā°C

Burning rate (<100 mm/min)

FMVSS 302

> 1 mm Thickness
+

General properties

Density

ISO 1183

23Ā°C
1,7 g/cmĀ³

Humidity absorption

ISO 1110

70Ā°C, 62% r.H.
0,9 - 1,2 %

Molding shrinkage

ISO 294-4

flow
transverse
0,1 - 0,3 %
0,3 - 0,5 %

Rheological Properties

Flowability

AKRO

2 mm Thickness
320 mm

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKROĀ®, AKROMIDĀ®, AKROLENĀ®, AKROLOYĀ®, AKROTEKĀ®, ICXĀ® and PRECITEĀ® are registered trademarks of the Feddersen Group.

Contact

Do you have any questions? We are happy to help.

Would you like to learn more about AKRO-PLASTIC GmbH? Contact us! We will be happy to help you.

Learn more