AKROMIDĀ®

B3 GF 40 1 L black (4581)

PA6 + PP GF40

AKROMIDĀ® B3 GF 40 1 L black (4581) - PA6/PP-Blend 40% glass fibre reinforced with lower density, cost reduced, calcium chloride

Modulus

11.000MPa

Strength

150MPa

Impact

70kJ/mĀ²

AKROMIDĀ® B3 GF 40 1 L black (4581) - PA6/PP-Blend 40% glass fibre reinforced with lower density, cost reduced, calcium chloride

AKROMIDĀ®

A3 GF 50 1 EN black (5737)

PA66 GF50

AKROMIDĀ® A3 GF 50 1 EN black (5737) - 50% glass fiber reinforced PA 6.6, electrically neutral and heat stabilised, technical parts in industrial engineering and automotive industry

Modulus

16.700MPa

Strength

250MPa

Impact

105kJ/mĀ²

AKROMIDĀ® A3 GF 50 1 EN black (5737) - 50% glass fiber reinforced PA 6.6, electrically neutral and heat stabilised, technical parts in industrial engineering and automotive industry

AKROMIDĀ®

D3 CGM 15/20 S1 black (6284)

PA612 (CF15+GF20)

AKROMIDĀ® D3 CGM 15/20 S1 black (6284) - PA 6.12, carbon fiber, glass fiber, impact modified, connector, electrical conductivity

Modulus

13.500MPa

Strength

145MPa

Impact

80kJ/mĀ²

AKROMIDĀ® D3 CGM 15/20 S1 black (6284) - PA 6.12, carbon fiber, glass fiber, impact modified, connector, electrical conductivity

AKROMIDĀ®

B3 GF 30 2 S1 grey (4289)

PA6-I GF30

AKROMIDĀ® B3 GF 30 2 S1 grey (4289) - PA 6, 30% glass fiber reinforced, impact modified and UV stabilised, for industrial applications, housings and covers, automotive

Modulus

8.500MPa

Strength

120MPa

Impact

65kJ/mĀ²

AKROMIDĀ® B3 GF 30 2 S1 grey (4289) - PA 6, 30% glass fiber reinforced, impact modified and UV stabilised, for industrial applications, housings and covers, automotive

AKROMIDĀ®

B3 GF 15 1 natural (2461)

PA6 GF15

AKROMIDĀ® B3 GF 15 1 natural (2461) is a 15% glass fibre reinforced, heat stabilised polyamide 6 with medium stiffness and strength and light inherent color

Modulus

6.100MPa

Strength

120MPa

Impact

52kJ/mĀ²

AKROMIDĀ® B3 GF 15 1 natural (2461) is a 15% glass fibre reinforced, heat stabilised polyamide 6 with medium stiffness and strength and light inherent color

AKROMIDĀ®

B3 GF 30 9 RM-M black (3099)

PA6+X GF30

AKROMIDĀ® B3 GF 30 9 RM-M black (3099) is a 30% glass fibre reinforced and process improved polyamide 6 with high stiffness and strength and limited moisture absorption

Modulus

10.500MPa

Strength

170MPa

Impact

70kJ/mĀ²

AKROMIDĀ® B3 GF 30 9 RM-M black (3099) is a 30% glass fibre reinforced and process improved polyamide 6 with high stiffness and strength and limited moisture absorption

AKROMIDĀ®

B3 GF 45 1 black (3851)

PA6 GF45

AKROMIDĀ® B3 GF 45 1 black (3851) is a 45% glass fibre reinforced, heat stabilised polyamide 6 with very high rigidity and strength

Modulus

14.500MPa

Strength

200MPa

Impact

110kJ/mĀ²

AKROMIDĀ® B3 GF 45 1 black (3851) is a 45% glass fibre reinforced, heat stabilised polyamide 6 with very high rigidity and strength

135363780

AKROMIDĀ®

A3 S1 black (1071)PA66-I

AKROMIDĀ® A3 S1 black 950089 (1071) is an unreinforced, impact modified Polyamide 6.6. The material is characterised by a very high impact strength even at low temperatures and therefore perfectly suitable for connecting and fixing systems which are used in the automotive and electro industry and that are exposed to high loading speeds.

Features

impact modified

Properties

Modulus

2.000MPa

Strength

50MPa

Impact

180kJ/mĀ²

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
1 mm/min | conditioned
2000 MPa
1200 MPa

Tensile stress at yield

ISO 527-2

50 mm/min | d.a.m.
50 mm/min | conditioned
50 MPa
40 MPa

Tensile strain at yield

ISO 527-2

50 mm/min | d.a.m.
4,8 %

Tensile strain at break

ISO 527-2

50 mm/min | d.a.m.
50 mm/min | conditioned
> 50 %
> 100 %

Flexural modulus

ISO 178

2 mm/min | d.a.m.
1950 MPa

Charpy impact strength

ISO 179-1/1eU

23Ā°C | d.a.m.
23Ā°C | conditioned
30Ā°C | d.a.m.
-
30Ā°C | conditioned
-
40Ā°C | d.a.m.
-
no break
no break
no break
no break
no break

Charpy notched impact strength

ISO 179-1/1eA

23Ā°C | d.a.m.
23Ā°C | conditioned
30Ā°C | d.a.m.
-
30Ā°C | conditioned
-
40Ā°C | d.a.m.
-
> 80 kJ/mĀ²
> 100 kJ/mĀ²
35 kJ/mĀ²
35 kJ/mĀ²
35 kJ/mĀ²

Ball indentation hardness

ISO 2039-1

358N/30s | d.a.m.
80 MPa

Thermal Properties

Temperature of deflection under load HDT/A

ISO 75

1,8 MPa
70 Ā°C

Temperature of deflection under load HDT/B

ISO 75

0,45 MPa
152 Ā°C

Melting temperature

ISO 11357-3

DSC, 10K/min
262 Ā°C

Flammability

Burning rate

UL 94

UL
0,8 mm Wall thickness
HB Class

Burning rate (<100 mm/min)

FMVSS 302

> 1 mm Thickness
+

General properties

Density

ISO 1183

23Ā°C
1,07 g/cmĀ³

Humidity absorption

ISO 1110

70Ā°C, 62% r.H.
1,9 - 2,1 %

Molding shrinkage

ISO 294-4

flow
transverse
1,3 - 1,5 %
1,5 - 1,7 %

Electrical Properties

Volume resistivity IEC

DIN EN IEC 62631-3-2

d.a.m.
1015 ā„¦ x cm

Surface resistivity

DIN EN 62631-3-2

d.a.m.
1014 ā„¦

Comparative tracking index

IEC 60112

Test liquid A
600 V

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKROĀ®, AKROMIDĀ®, AKROLENĀ®, AKROLOYĀ®, AKROTEKĀ®, ICXĀ® and PRECITEĀ® are registered trademarks of the Feddersen Group.