AKROMIDĀ®
A28 GF 30 9 black (4915)
PA66 GF30
AKROMIDĀ® A28 GF 30 9 black (4915) - PA 6.6, 30% glassfiber reinforced, easy flow, process improved, technical parts in industrial engineering and automotive industry
9.600MPa
200MPa
70kJ/mĀ²
AKROMIDĀ® A28 GF 30 9 black (4915) - PA 6.6, 30% glassfiber reinforced, easy flow, process improved, technical parts in industrial engineering and automotive industry
AKROMIDĀ®
A3 GF 30 3 black (21005)
PA66 GF30
AKROMIDĀ® A3 GF 30 3 black (21005) - PA 6.6 30% glass fiber reinforced, inorganic heat stabilised, nucleated, technical parts in industrial engineering and in the automotive industry
10.000MPa
170MPa
55kJ/mĀ²
AKROMIDĀ® A3 GF 30 3 black (21005) - PA 6.6 30% glass fiber reinforced, inorganic heat stabilised, nucleated, technical parts in industrial engineering and in the automotive industry
AKROMIDĀ®
B3 GF 30 FR orange (7857)
PA6 GF 30 FR(40)
AKROMIDĀ® B3 GF 30 FR orange (7857) is a 30% glass fibre reinforced, halogene free flame retardant polyamide 6 with flammability acc UL 94 V0 and low corrosion colored in orange (RAL 2003)
10.500MPa
135MPa
65kJ/mĀ²
AKROMIDĀ® B3 GF 30 FR orange (7857) is a 30% glass fibre reinforced, halogene free flame retardant polyamide 6 with flammability acc UL 94 V0 and low corrosion colored in orange (RAL 2003)
AKROMIDĀ®
C3 5 S3 black (8029)
PA66+PA6
AKROMIDĀ® C3 5 S3 black (8029) - PA 6.6/6 blend unreinforced and high heat stabilised, impact modified whilst maintaining good flowability, for connecting and fixing systems
2.500MPa
65MPa
180kJ/mĀ²
AKROMIDĀ® C3 5 S3 black (8029) - PA 6.6/6 blend unreinforced and high heat stabilised, impact modified whilst maintaining good flowability, for connecting and fixing systems
AKROMIDĀ®
T9 GF 50 natural (8334)
PPA GF50
AKROMIDĀ® T9 GF 50 natural (8334) is a 50% glass fibre reinforced polyphthalamide with heat stabilization, high rigidity and strength, as well as high temperature and chemical resistance. The compound is based on PA9T and has lower moisture uptake than conventional PA6T variants. This leads to a significantly higher consistency of the glass transition temperature and higher strength at elevated temperatures especially in conditioned state.
16.500MPa
250MPa
95kJ/mĀ²
AKROMIDĀ® T9 GF 50 natural (8334) is a 50% glass fibre reinforced polyphthalamide with heat stabilization, high rigidity and strength, as well as high temperature and chemical resistance. The compound is based on PA9T and has lower moisture uptake than conventional PA6T variants. This leads to a significantly higher consistency of the glass transition temperature and higher strength at elevated temperatures especially in conditioned state.
AKROMIDĀ®
A3 ICF 40 black (5116)
PA66 CF40
AKROMIDĀ® A3 ICF 40 black (5116) is a 40% carbon fibre reinforced polyamide 6.6 with high flexural strength and good sliding properties
33.000MPa
270MPa
60kJ/mĀ²
AKROMIDĀ® A3 ICF 40 black (5116) is a 40% carbon fibre reinforced polyamide 6.6 with high flexural strength and good sliding properties
AKROMIDĀ®
C3 1 FR black (5266)
PA66+PA6 FR (30)
AKROMIDĀ® C3 1 FR black (5266) - PA6/6.6 blend, unreinforced, flame retardant, UL-listed, good flowability, public transportation, new mobility.
3.400MPa
75MPa
100kJ/mĀ²
AKROMIDĀ® C3 1 FR black (5266) - PA6/6.6 blend, unreinforced, flame retardant, UL-listed, good flowability, public transportation, new mobility.
AKROMIDĀ®
A3 GF 30 1 L natural (4715)PA66+PP GF30
AKROMIDĀ® A3 GF 30 1 L natural (4715) is a PA6.6-PP-blend with reduced density compared to standard PA66 GF 30. With 30% glass fibre reinforcement, the material is suitable for components with high strength and stiffness where cost and weight reduction are required at the same time. The chemical resistance of AKROMIDĀ® A3 GF 30 1 L natural (4715) is particularly superior to zinc chloride (ZnClā).
Features
Properties
8.600MPa
155MPa
77kJ/mĀ²
Mechanical Properties
Tensile modulus
ISO 527-2
Tensile stress at break
ISO 527-2
Tensile strain at break
ISO 527-2
Flexural modulus
ISO 178
Flexural strength
ISO 178
Flexural strain at break
ISO 178
Charpy impact strength
ISO 179-1/1eU
Charpy notched impact strength
ISO 179-1/1eA
Thermal Properties
Temperature of deflection under load HDT/A
ISO 75
Temperature of deflection under load HDT/B
ISO 75
Melting temperature
ISO 11357-3
Flammability
Burning rate
UL 94
Burning rate (<100 mm/min)
FMVSS 302
General properties
Density
ISO 1183
Humidity absorption
ISO 1110
Molding shrinkage
ISO 294-4
Rheological Properties
MVR
ISO 1133
Disclaimer
All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKROĀ®, AKROMIDĀ®, AKROLENĀ®, AKROLOYĀ®, AKROTEKĀ®, ICXĀ® and PRECITEĀ® are registered trademarks of the Feddersen Group.
Contact
Do you have any questions? We are happy to help.
Would you like to learn more about AKRO-PLASTIC GmbH? Contact us! We will be happy to help you.