AKROMID®

B3 GF 15 1 natural (2461)

PA6 GF15

AKROMID® B3 GF 15 1 natural (2461) is a 15% glass fibre reinforced, heat stabilised polyamide 6 with medium stiffness and strength and light inherent color

Modulus

6.100MPa

Strength

120MPa

Impact

52kJ/m²

AKROMID® B3 GF 15 1 natural (2461) is a 15% glass fibre reinforced, heat stabilised polyamide 6 with medium stiffness and strength and light inherent color

AKROMID®

A3 1 S3 15 natural (2892)

PA66-I

AKROMID® A3 1 S3 15 natural (2892) - PA66, unreinforced, impact modified, good flowability, for connecting and fixing systems, automotive, E&E

Modulus

2.700MPa

Strength

63MPa

Impact

180kJ/m²

AKROMID® A3 1 S3 15 natural (2892) - PA66, unreinforced, impact modified, good flowability, for connecting and fixing systems, automotive, E&E

AKROMID®

B3 GK 30 natural (2719)

PA6 GB30

AKROMID® B3 GK 30 natural (2719) - PA 6, 30% glass beads reinforced, good surface, low warpage

Modulus

4.400MPa

Strength

70MPa

Impact

30kJ/m²

AKROMID® B3 GK 30 natural (2719) - PA 6, 30% glass beads reinforced, good surface, low warpage

AKROLEN®

PP GFM 25/15 LA black (3143)

PP (GF25+MD15)

AKROLEN® PP GFM 25/15 LA black (3143) - 25% glass fibre reinforced, 15% mineralfilled, laser markable polypropylene with good surface and dimensional stability.

Modulus

6.500MPa

Strength

NA

Impact

45kJ/m²

AKROLEN® PP GFM 25/15 LA black (3143) - 25% glass fibre reinforced, 15% mineralfilled, laser markable polypropylene with good surface and dimensional stability.

AKROMID®

A3 GF 30 1 S3 black (3502)

PA66-I GF30

AKROMID® A3 GF 30 1 S3 black (3502) is a 30% glass fibre reinforced, heat stabilised, dry impact resistant polyamide 6.6 with high stiffness and strength

Modulus

8.000MPa

Strength

170MPa

Impact

100kJ/m²

AKROMID® A3 GF 30 1 S3 black (3502) is a 30% glass fibre reinforced, heat stabilised, dry impact resistant polyamide 6.6 with high stiffness and strength

AKROMID®

B3 GF 50 8 natural (4301)

PA6 GF50

AKROMID® B3 GF 50 8 natural (4301)- PA6, 50% glass fiber, FDA, EU 10/2010, food contact, kitchen and household appliances

Modulus

17.000MPa

Strength

240MPa

Impact

100kJ/m²

AKROMID® B3 GF 50 8 natural (4301)- PA6, 50% glass fiber, FDA, EU 10/2010, food contact, kitchen and household appliances

AKROTEK®

PK-HM natural (4773)

PK

AKROTEK® PK-HM natural (4773) - Polyketon, Tribology, friction and wear, chemical resistance

Modulus

1.400MPa

Strength

60MPa

Impact

180kJ/m²

AKROTEK® PK-HM natural (4773) - Polyketon, Tribology, friction and wear, chemical resistance

133343580

AKROMID®

Preliminary

NEXT U28 ICF 40 1 black (8238)PA11 CF40

AKROMID® NEXT U28 ICF 40 1 black (8238) is a Polyamide 11 reinforced with 40% recycled carbon fibre. The PA 11 is made from castor seed oil (bio-based content > 92%). The compound's low density as well as excellent ductility even at lower temperatures combined with high stiffness and strength enable the use for demanding applications, e.g., for lightweight construction or sports & leisure. The production of large-volume parts is possible with high throughputs > 1 kg/h in 3D-printing with pellets in screw extrusion additive manufacturing and Fused Granulate Fabrication (FGF).

Features

heat stabilised 130
recycled content
reduced density
reduced moisture
3D printing / additive manufacturing
Sports & leisure
lightweight construction

Properties

Modulus

20.000MPa

Strength

190MPa

Impact

80kJ/m²

Sustainability

Biobased carbon content

41 %

Recycled content

40 %

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
1 mm/min | conditioned
20000 MPa
14000 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
190 MPa
160 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
3,5 %
3,7 %

Flexural modulus

ISO 178

2 mm/min | d.a.m.
2 mm/min | conditioned
21000 MPa
17500 MPa

Flexural strength

ISO 178

2 mm/min | d.a.m.
2 mm/min | conditioned
295 MPa
250 MPa

Flexural strain at break

ISO 178

2 mm/min | d.a.m.
2 mm/min | conditioned
2,8 %
3,3 %

Charpy impact strength

ISO 179-1/1eU

23°C | d.a.m.
23°C | conditioned
30°C | d.a.m.
-
30°C | conditioned
-
80 kJ/m²
75 kJ/m²
75 kJ/m²
65 kJ/m²

Charpy notched impact strength

ISO 179-1/1eA

23°C | d.a.m.
23°C | conditioned
30°C | d.a.m.
-
30°C | conditioned
-
14 kJ/m²
14 kJ/m²
10 kJ/m²
9 kJ/m²

Thermal Properties

Temperature of deflection under load HDT/A

ISO 75

1,8 MPa
180 °C

Melting temperature

ISO 11357-3

DSC, 10K/min
189 °C

Flammability

Burning rate

UL 94

1,6 mm Wall thickness
HB Class

General properties

Density

ISO 1183

23°C
1,24 g/cm³

Humidity absorption

ISO 1110

70°C, 62% r.H.
0,4 - 0,6 %

Water absorption

ISO 62

23°C, saturated
1,1 - 1,5 %

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.

Contact

Do you have any questions? We are happy to help.

Would you like to learn more about AKRO-PLASTIC GmbH? Contact us! We will be happy to help you.

Learn more