HEADER Granulat 1920x700

Find the right compound

Select your fitting and find the right compound for your intend

Tensile Modulusin MPa
Tensile Strengthin MPa
Charpy impact strengthin kJ/m²
558 Compounds found
Recommended  
Tensile Modulus
Tensile Strength
Charpy impact strength
Description

AKROMID®

A3 GF 30 6 black (6736)

PA66 GF30

AKROMID® A3 GF 30 6 black (6736) - PA 6.6 30% glass fiber reinforced, inorganic heat stabilised, technical parts in industrial engineering and in the automotive industry

Modulus

10.000MPa

Strength

200MPa

Impact

75kJ/m²

AKROMID® A3 GF 30 6 black (6736) - PA 6.6 30% glass fiber reinforced, inorganic heat stabilised, technical parts in industrial engineering and in the automotive industry

PRECITE®

Preliminary

K GF 50 natural (7435)

PBT-PET- GF 50

PRECITE® K GF 50 natural (7435) - PBT/PET blend, 50% glass fiber, dimensional stability, good surface, low moisture, very good strength, automotive, E&E, household, industry.

Modulus

20.000MPa

Strength

175MPa

Impact

60kJ/m²

PRECITE® K GF 50 natural (7435) - PBT/PET blend, 50% glass fiber, dimensional stability, good surface, low moisture, very good strength, automotive, E&E, household, industry.

AKROMID®

UL

B3 GF 30 FR orange (7857)

PA6 GF 30 FR(40)

AKROMID® B3 GF 30 FR orange (7857) is a 30% glass fibre reinforced, halogene free flame retardant polyamide 6 with flammability acc UL 94 V0 and low corrosion colored in orange (RAL 2003)

Modulus

10.500MPa

Strength

135MPa

Impact

65kJ/m²

AKROMID® B3 GF 30 FR orange (7857) is a 30% glass fibre reinforced, halogene free flame retardant polyamide 6 with flammability acc UL 94 V0 and low corrosion colored in orange (RAL 2003)

AKROMID®

UL

C3 1 FR orange (7470)

PA66+PA6 FR(30)

AKROMID® C3 1 FR orange (7470) - PA6/6.6 blend, unreinforced, flame retardant, UL-listed, good flowability, RAL 2003, for high voltage components e-mobility.

Modulus

3.500MPa

Strength

76MPa

Impact

NA

AKROMID® C3 1 FR orange (7470) - PA6/6.6 blend, unreinforced, flame retardant, UL-listed, good flowability, RAL 2003, for high voltage components e-mobility.

AKROMID®

B3 GK 30 natural (2719)

PA6 GB30

AKROMID® B3 GK 30 natural (2719) - PA 6, 30% glass beads reinforced, good surface, low warpage

Modulus

4.400MPa

Strength

70MPa

Impact

30kJ/m²

AKROMID® B3 GK 30 natural (2719) - PA 6, 30% glass beads reinforced, good surface, low warpage

AKROMID®

B3 GF 30 RM-M natural (3291)

PA6 + X GF30

AKROMID® B3 GF 30 RM-M natural (3291) - 30% glass fiber reinforced PA 6, reduced moisture absorption, for technical applications where high dimensional stability is required

Modulus

11.000MPa

Strength

165MPa

Impact

70kJ/m²

AKROMID® B3 GF 30 RM-M natural (3291) - 30% glass fiber reinforced PA 6, reduced moisture absorption, for technical applications where high dimensional stability is required

AKROLEN®

PP GFM 25/15 LA black (3143)

PP (GF25+MD15)

AKROLEN® PP GFM 25/15 LA black (3143) - 25% glass fibre reinforced, 15% mineralfilled, laser markable polypropylene with good surface and dimensional stability.

Modulus

6.500MPa

Strength

NA

Impact

45kJ/m²

AKROLEN® PP GFM 25/15 LA black (3143) - 25% glass fibre reinforced, 15% mineralfilled, laser markable polypropylene with good surface and dimensional stability.

133343580

AKROMID®

B3 1 S3 black (7956)PA6-I

AKROMID® B3 1 S3 black (7956) is an unreinforced, impact modified Polyamide 6. It is characterised by a medium dry impact strength whilst maintaining good flowability. Furthermore, the material is heat stabilised and therefore perfectly suitable for connecting and fixing systems which are used at elevated temperatures in the automotive and electro industry.

Features

heat stabilised 130
impact modified
easy flow

Properties

Modulus

2.200MPa

Strength

55MPa

Impact

180kJ/m²

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
1 mm/min | conditioned
2200 MPa
700 MPa

Tensile stress at yield

ISO 527-2

50 mm/min | d.a.m.
50 mm/min | conditioned
55 MPa
32 MPa

Tensile strain at break

ISO 527-2

50 mm/min | d.a.m.
60 %

Charpy impact strength

ISO 179-1/1eU

23°C | d.a.m.
no break

Charpy notched impact strength

ISO 179-1/1eA

23°C | d.a.m.
23°C | conditioned
18 kJ/m²
100 kJ/m²

Thermal Properties

Melting temperature

ISO 11357-3

DSC, 10K/min
220 °C

Flammability

Burning rate

UL 94

1,6 mm Wall thickness
HB Class

Burning rate (<100 mm/min)

FMVSS 302

> 1 mm Thickness
+

General properties

Density

ISO 1183

23°C
1,1 g/cm³

Humidity absorption

ISO 1110

70°C, 62% r.H.
2,6 - 2,8 %

Molding shrinkage

ISO 294-4

flow
transverse
1,0 - 1,2 %
1,1 - 1,3 %

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.

Contact

Do you have any questions? We are happy to help.

Would you like to learn more about AKRO-PLASTIC GmbH? Contact us! We will be happy to help you.

Learn more