Find the right compound
Select your fitting and find the right compound for your intend
AKROMID®
A3 ICF 40 black (5116)
PA66 CF40
AKROMID® A3 ICF 40 black (5116) is a 40% carbon fibre reinforced polyamide 6.6 with high flexural strength and good sliding properties
33.000MPa
270MPa
60kJ/m²
AKROMID® A3 ICF 40 black (5116) is a 40% carbon fibre reinforced polyamide 6.6 with high flexural strength and good sliding properties
AKROLOY®
PA GF 30 natural (6412)
PA66+PA6I/6T GF30
AKROLOY® PA GF 30 natur (6412) is a 30% glass fibre reinforced, semi-aromatic polyamide blend with high stiffness and strength, even in conditioned state.
10.200MPa
200MPa
70kJ/m²
AKROLOY® PA GF 30 natur (6412) is a 30% glass fibre reinforced, semi-aromatic polyamide blend with high stiffness and strength, even in conditioned state.
AKROMID®
A3 GF 50 6 black (6860)
PA66 GF50
AKROMID® A3 GF 50 6 black (6860) - 50% glass fiber reinforced PA 6.6, inorganically high heat stabilised, technical parts in industrial engineering and automotive industry
18.000MPa
250MPa
105kJ/m²
AKROMID® A3 GF 50 6 black (6860) - 50% glass fiber reinforced PA 6.6, inorganically high heat stabilised, technical parts in industrial engineering and automotive industry
AKROMID®
A3 GF 30 3 black (21005)
PA66 GF30
AKROMID® A3 GF 30 3 black (21005) - PA 6.6 30% glass fiber reinforced, inorganic heat stabilised, nucleated, technical parts in industrial engineering and in the automotive industry
10.000MPa
170MPa
55kJ/m²
AKROMID® A3 GF 30 3 black (21005) - PA 6.6 30% glass fiber reinforced, inorganic heat stabilised, nucleated, technical parts in industrial engineering and in the automotive industry
AKROMID®
C3 5 S3 black (8029)
PA66+PA6
AKROMID® C3 5 S3 black (8029) - PA 6.6/6 blend unreinforced and high heat stabilised, impact modified whilst maintaining good flowability, for connecting and fixing systems
2.500MPa
65MPa
180kJ/m²
AKROMID® C3 5 S3 black (8029) - PA 6.6/6 blend unreinforced and high heat stabilised, impact modified whilst maintaining good flowability, for connecting and fixing systems
AKROMID®
A3 1 S3 15 natural (2892)
PA66-I
AKROMID® A3 1 S3 15 natural (2892) - PA66, unreinforced, impact modified, good flowability, for connecting and fixing systems, automotive, E&E
2.700MPa
63MPa
180kJ/m²
AKROMID® A3 1 S3 15 natural (2892) - PA66, unreinforced, impact modified, good flowability, for connecting and fixing systems, automotive, E&E
AKROMID®
B3 GF 30 9 RM-M black (3099)
PA6+X GF30
AKROMID® B3 GF 30 9 RM-M black (3099) is a 30% glass fibre reinforced and process improved polyamide 6 with high stiffness and strength and limited moisture absorption
10.500MPa
170MPa
70kJ/m²
AKROMID® B3 GF 30 9 RM-M black (3099) is a 30% glass fibre reinforced and process improved polyamide 6 with high stiffness and strength and limited moisture absorption
AKROLOY®
PARA ICF 40 black (6130)PARA CF40
AKROLOY® PARA ICF 40 black (6130) is a 40% carbon fibre reinforced Polyarylamide with very high stiffness. The material offers a higher process stability as well as a better weld line performance than its predecessor (6128), while the colour depth is reduced.
Features
Properties
39.000MPa
280MPa
35kJ/m²
Sustainability
Recycled content
Mechanical Properties
Tensile modulus
ISO 527-2
Tensile stress at break
ISO 527-2
Tensile strain at break
ISO 527-2
Flexural modulus
ISO 178
Flexural strength
ISO 178
Charpy impact strength
ISO 179-1/1eU
Charpy notched impact strength
ISO 179-1/1eA
Thermal Properties
Temperature of deflection under load HDT/A
ISO 75
Melting temperature
ISO 11357-3
Flammability
Burning rate
UL 94
Burning rate (<100 mm/min)
FMVSS 302
General properties
Density
ISO 1183
Humidity absorption
ISO 1110
Molding shrinkage
ISO 294-4
Electrical Properties
Volume resistivity IEC
DIN EN IEC 62631-3-2
Disclaimer
All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKRO®, AKROMID®, AKROLEN®, AKROLOY®, AKROTEK®, ICX® and PRECITE® are registered trademarks of the Feddersen Group.
Contact
Do you have any questions? We are happy to help.
Would you like to learn more about AKRO-PLASTIC GmbH? Contact us! We will be happy to help you.