Select your fitting and find the right compound for your intend
AKROMIDĀ®
A3 ICF 40 black (5116)
PA66 CF40
AKROMIDĀ® A3 ICF 40 black (5116) is a 40% carbon fibre reinforced polyamide 6.6 with high flexural strength and good sliding properties
33.000MPa
270MPa
60kJ/mĀ²
AKROMIDĀ® A3 ICF 40 black (5116) is a 40% carbon fibre reinforced polyamide 6.6 with high flexural strength and good sliding properties
AKROLOYĀ®
PA GF 30 natural (6412)
PA66+PA6I/6T GF30
AKROLOYĀ® PA GF 30 natur (6412) is a 30% glass fibre reinforced, semi-aromatic polyamide blend with high stiffness and strength, even in conditioned state.
10.200MPa
200MPa
70kJ/mĀ²
AKROLOYĀ® PA GF 30 natur (6412) is a 30% glass fibre reinforced, semi-aromatic polyamide blend with high stiffness and strength, even in conditioned state.
AKROMIDĀ®
A3 GF 50 6 black (6860)
PA66 GF50
AKROMIDĀ® A3 GF 50 6 black (6860) - 50% glass fiber reinforced PA 6.6, inorganically high heat stabilised, technical parts in industrial engineering and automotive industry
18.000MPa
250MPa
105kJ/mĀ²
AKROMIDĀ® A3 GF 50 6 black (6860) - 50% glass fiber reinforced PA 6.6, inorganically high heat stabilised, technical parts in industrial engineering and automotive industry
AKROMIDĀ®
A3 GF 30 3 black (21005)
PA66 GF30
AKROMIDĀ® A3 GF 30 3 black (21005) - PA 6.6 30% glass fiber reinforced, inorganic heat stabilised, nucleated, technical parts in industrial engineering and in the automotive industry
10.000MPa
170MPa
55kJ/mĀ²
AKROMIDĀ® A3 GF 30 3 black (21005) - PA 6.6 30% glass fiber reinforced, inorganic heat stabilised, nucleated, technical parts in industrial engineering and in the automotive industry
AKROMIDĀ®
C3 5 S3 black (8029)
PA66+PA6
AKROMIDĀ® C3 5 S3 black (8029) - PA 6.6/6 blend unreinforced and high heat stabilised, impact modified whilst maintaining good flowability, for connecting and fixing systems
2.500MPa
65MPa
180kJ/mĀ²
AKROMIDĀ® C3 5 S3 black (8029) - PA 6.6/6 blend unreinforced and high heat stabilised, impact modified whilst maintaining good flowability, for connecting and fixing systems
AKROMIDĀ®
A3 1 S3 15 natural (2892)
PA66-I
AKROMIDĀ® A3 1 S3 15 natural (2892) - PA66, unreinforced, impact modified, good flowability, for connecting and fixing systems, automotive, E&E
2.700MPa
63MPa
180kJ/mĀ²
AKROMIDĀ® A3 1 S3 15 natural (2892) - PA66, unreinforced, impact modified, good flowability, for connecting and fixing systems, automotive, E&E
AKROMIDĀ®
B3 GF 30 9 RM-M black (3099)
PA6+X GF30
AKROMIDĀ® B3 GF 30 9 RM-M black (3099) is a 30% glass fibre reinforced and process improved polyamide 6 with high stiffness and strength and limited moisture absorption
10.500MPa
170MPa
70kJ/mĀ²
AKROMIDĀ® B3 GF 30 9 RM-M black (3099) is a 30% glass fibre reinforced and process improved polyamide 6 with high stiffness and strength and limited moisture absorption
AKROMIDĀ®
AKROMIDĀ® A3 S1 black 950089 (1071) is an unreinforced, impact modified Polyamide 6.6. The material is characterised by a very high impact strength even at low temperatures and therefore perfectly suitable for connecting and fixing systems which are used in the automotive and electro industry and that are exposed to high loading speeds.
Features
Properties
2.000MPa
50MPa
180kJ/mĀ²
ISO 527-2
ISO 527-2
ISO 527-2
ISO 527-2
ISO 178
ISO 179-1/1eU
ISO 179-1/1eA
ISO 2039-1
ISO 75
ISO 75
ISO 11357-3
UL 94
FMVSS 302
ISO 1183
ISO 1110
ISO 294-4
DIN EN IEC 62631-3-2
DIN EN 62631-3-2
IEC 60112
Disclaimer
All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKROĀ®, AKROMIDĀ®, AKROLENĀ®, AKROLOYĀ®, AKROTEKĀ®, ICXĀ® and PRECITEĀ® are registered trademarks of the Feddersen Group.