B3 GF 60 1 black (4644)

PA6 GF60

AKROMIDĀ® B3 GF 60 1 black (4644) - 60% glass fiber reinforced, PA 6, heat stabilised, easy flow

Modulus

21.000MPa

Strength

250MPa

Impact

90kJ/mĀ²

AKROMIDĀ® B3 GF 60 1 black (4644) - 60% glass fiber reinforced, PA 6, heat stabilised, easy flow

AKROMIDĀ®

UL

B3 GF 30 FR orange (7857)

PA6 GF 30 FR(40)

AKROMIDĀ® B3 GF 30 FR orange (7857) is a 30% glass fibre reinforced, halogene free flame retardant polyamide 6 with flammability acc UL 94 V0 and low corrosion colored in orange (RAL 2003)

Modulus

10.500MPa

Strength

135MPa

Impact

65kJ/mĀ²

AKROMIDĀ® B3 GF 30 FR orange (7857) is a 30% glass fibre reinforced, halogene free flame retardant polyamide 6 with flammability acc UL 94 V0 and low corrosion colored in orange (RAL 2003)

AKROMIDĀ®

Preliminary

B3 GF 30 ECO black (7923)

PA6 GF30

AKROMIDĀ® B3 GF 30 ECO black (7923) - PA 6, 30% glass fiber, recycling, heat-stabilised, high stiffness and strength, automotive, mechanical engineering.

Modulus

9.500MPa

Strength

155MPa

Impact

75kJ/mĀ²

AKROMIDĀ® B3 GF 30 ECO black (7923) - PA 6, 30% glass fiber, recycling, heat-stabilised, high stiffness and strength, automotive, mechanical engineering.

AKROMIDĀ®

C28 M 30 6 black (7934)

PA66+PA6 MD30

AKROMIDĀ® C28 M 30 6 black (7934) is a 30% mineral filled, high heat stabilized polyamid 6.6/6 with very good surface low warpage and easy flow.

Modulus

6.000MPa

Strength

70MPa

Impact

30kJ/mĀ²

AKROMIDĀ® C28 M 30 6 black (7934) is a 30% mineral filled, high heat stabilized polyamid 6.6/6 with very good surface low warpage and easy flow.

AKROMIDĀ®

UL

C3 1 FR natural (8050)

PA66+PA6 FR(30)

AKROMIDĀ® C3 1 FR natural (8050) - PA6/6.6 blend, unreinforced, flame retardant, UL-listed, very good flowability, public transportation, new mobility.

Modulus

3.600MPa

Strength

77MPa

Impact

100kJ/mĀ²

AKROMIDĀ® C3 1 FR natural (8050) - PA6/6.6 blend, unreinforced, flame retardant, UL-listed, very good flowability, public transportation, new mobility.

AKROMIDĀ®

B3 GF 15 1 black (2482)

PA6 GF15

AKROMIDĀ® B3 GF 15 1 black (2482) is a 15% glass fibre reinforced, heat stabilised polyamide 6 with medium stiffness and strength.

Modulus

6.100MPa

Strength

120MPa

Impact

52kJ/mĀ²

AKROMIDĀ® B3 GF 15 1 black (2482) is a 15% glass fibre reinforced, heat stabilised polyamide 6 with medium stiffness and strength.

AKROMIDĀ®

C3 GF 30 5 XTC natural (4499)

PA66 + PA6 GF 30

AKROMIDĀ® C3 GF 30 5 XTC natural (4499) is a 30% glass fibre reinforced, high temperature stabilised polaymide 6.6/6 - Blend with high stiffness and strength and extra high temperature tolerance.

Modulus

9.500MPa

Strength

185MPa

Impact

95kJ/mĀ²

AKROMIDĀ® C3 GF 30 5 XTC natural (4499) is a 30% glass fibre reinforced, high temperature stabilised polaymide 6.6/6 - Blend with high stiffness and strength and extra high temperature tolerance.

132333480

AKROMIDĀ®

T5 GF 50 8 black (6205)PPA GF50

AKROMIDĀ® T5 GF 50 8 black (6205) is a 50% glass fibre reinforced polyphthalamide with very high rigidity and strength, as well as high temperature and chemical resistance. This aromatic PPA keeps mechanical performance even at elevated temperatures as well as moisture pic-up. The material fulfills the requirements according to ACS, WRAS and NSF 61. It is suitable for applications that are in contact with cold and hot drinking water. This material corresponds to the European food guideline EU 10/2011 and to the American FDA 21 CFR and is suitable for parts of kitchen and household appliances.

Regulatory

acseu102011fdansf-coldnsf-hotwras

Properties

Modulus

19.000MPa

Strength

270MPa

Impact

85kJ/mĀ²

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
1 mm/min | conditioned
19000 MPa
19000 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
270 MPa
270 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
2,1 %
2,1 %

Flexural modulus

ISO 178

2 mm/min | d.a.m.
2 mm/min | conditioned
18500 MPa
18500 MPa

Flexural strength

ISO 178

2 mm/min | d.a.m.
2 mm/min | conditioned
410 MPa
350 MPa

Standard bending strength RP 3,5

ISO 178

2mm/min | d.a.m.
2,5 MPa

Charpy impact strength

ISO 179-1/1eU

23Ā°C | d.a.m.
23Ā°C | conditioned
30Ā°C | d.a.m.
-
30Ā°C | conditioned
-
85 kJ/mĀ²
85 kJ/mĀ²
75 kJ/mĀ²
75 kJ/mĀ²

Charpy notched impact strength

ISO 179-1/1eA

23Ā°C | d.a.m.
23Ā°C | conditioned
13 kJ/mĀ²
13 kJ/mĀ²

Thermal Properties

Temperature of deflection under load HDT/A

ISO 75

1,8 MPa
280 Ā°C

Melting temperature

ISO 11357-3

DSC, 10K/min
325 Ā°C

Flammability

Burning rate

UL 94

1,6 mm Wall thickness
HB Class

General properties

Density

ISO 1183

23Ā°C
1,65 g/cmĀ³

Humidity absorption

ISO 1110

70Ā°C, 62% r.H.
0,8 %

Molding shrinkage

ISO 294-4

flow
transverse
0,1 - 0,3 %
0,4 - 0,6 %

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKROĀ®, AKROMIDĀ®, AKROLENĀ®, AKROLOYĀ®, AKROTEKĀ®, ICXĀ® and PRECITEĀ® are registered trademarks of the Feddersen Group.

Contact

Do you have any questions? We are happy to help.

Would you like to learn more about AKRO-PLASTIC GmbH? Contact us! We will be happy to help you.

Learn more