B3 GK 50 natural (3690)

PA6 GB50

AKROMIDĀ® B3 GK 50 natural (3690) - PA 6, 50% glass beads reinforced, good surface, low warpage

Modulus

5.700MPa

Strength

75MPa

Impact

42kJ/mĀ²

AKROMIDĀ® B3 GK 50 natural (3690) - PA 6, 50% glass beads reinforced, good surface, low warpage

AKROMIDĀ®

B3 GF 60 1 black (4644)

PA6 GF60

AKROMIDĀ® B3 GF 60 1 black (4644) - 60% glass fiber reinforced, PA 6, heat stabilised, easy flow

Modulus

21.000MPa

Strength

250MPa

Impact

90kJ/mĀ²

AKROMIDĀ® B3 GF 60 1 black (4644) - 60% glass fiber reinforced, PA 6, heat stabilised, easy flow

AKROMIDĀ®

UL

C3 1 FR black (5266)

PA66+PA6 FR (30)

AKROMIDĀ® C3 1 FR black (5266) - PA6/6.6 blend, unreinforced, flame retardant, UL-listed, good flowability, public transportation, new mobility.

Modulus

3.400MPa

Strength

75MPa

Impact

100kJ/mĀ²

AKROMIDĀ® C3 1 FR black (5266) - PA6/6.6 blend, unreinforced, flame retardant, UL-listed, good flowability, public transportation, new mobility.

AKROLOYĀ®

Preliminary

PA GF 30 natural (6412)

PA66+PA6I/6T GF30

AKROLOYĀ® PA GF 30 natur (6412) is a 30% glass fibre reinforced, semi-aromatic polyamide blend with high stiffness and strength, even in conditioned state.

Modulus

10.200MPa

Strength

200MPa

Impact

70kJ/mĀ²

AKROLOYĀ® PA GF 30 natur (6412) is a 30% glass fibre reinforced, semi-aromatic polyamide blend with high stiffness and strength, even in conditioned state.

AKROMIDĀ®

A3 GF 30 3 black (21005)

PA66 GF30

AKROMIDĀ® A3 GF 30 3 black (21005) - PA 6.6 30% glass fiber reinforced, inorganic heat stabilised, nucleated, technical parts in industrial engineering and in the automotive industry

Modulus

10.000MPa

Strength

170MPa

Impact

55kJ/mĀ²

AKROMIDĀ® A3 GF 30 3 black (21005) - PA 6.6 30% glass fiber reinforced, inorganic heat stabilised, nucleated, technical parts in industrial engineering and in the automotive industry

AKROMIDĀ®

B3 GF 30 2 S1 grey (4289)

PA6-I GF30

AKROMIDĀ® B3 GF 30 2 S1 grey (4289) - PA 6, 30% glass fiber reinforced, impact modified and UV stabilised, for industrial applications, housings and covers, automotive

Modulus

8.500MPa

Strength

120MPa

Impact

65kJ/mĀ²

AKROMIDĀ® B3 GF 30 2 S1 grey (4289) - PA 6, 30% glass fiber reinforced, impact modified and UV stabilised, for industrial applications, housings and covers, automotive

AKROMIDĀ®

B3 GF 15 1 black (2482)

PA6 GF15

AKROMIDĀ® B3 GF 15 1 black (2482) is a 15% glass fibre reinforced, heat stabilised polyamide 6 with medium stiffness and strength.

Modulus

6.100MPa

Strength

120MPa

Impact

52kJ/mĀ²

AKROMIDĀ® B3 GF 15 1 black (2482) is a 15% glass fibre reinforced, heat stabilised polyamide 6 with medium stiffness and strength.

132333480

AKROMIDĀ®

B3 GF 30 S1 natural (1383)PA6-I GF30

AKROMIDĀ® B3 GF 30 S1 natural (1383) is a 30% glass fiber reinforced, impact modified Polyamide 6. It is characterised by high stiffness and strength as well as a higher impact strength compared to a standard PA 6 GF 30. The material is therefore perfectly suitable for industrial applications and for housings and covers in the automotive industry. The material has a light inherent color.

Features

impact modified

Properties

Modulus

7.500MPa

Strength

125MPa

Impact

110kJ/mĀ²

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
1 mm/min | conditioned
7500 MPa
4200 MPa

Tensile stress at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
125 MPa
70 MPa

Tensile strain at break

ISO 527-2

5 mm/min | d.a.m.
5 mm/min | conditioned
6 %
13 %

Flexural modulus

ISO 178

2 mm/min | d.a.m.
6400 MPa

Flexural strength

ISO 178

2 mm/min | d.a.m.
190 MPa

Charpy impact strength

ISO 179-1/1eU

23Ā°C | d.a.m.
23Ā°C | conditioned
10Ā°C | d.a.m.
-
20Ā°C | d.a.m.
-
30Ā°C | d.a.m.
-
40Ā°C | d.a.m.
-
110 kJ/mĀ²
135 kJ/mĀ²
112 kJ/mĀ²
117 kJ/mĀ²
117 kJ/mĀ²
115 kJ/mĀ²

Charpy notched impact strength

ISO 179-1/1eA

23Ā°C | d.a.m.
23Ā°C | conditioned
10Ā°C | d.a.m.
-
20Ā°C | d.a.m.
-
30Ā°C | d.a.m.
-
40Ā°C | d.a.m.
-
35 kJ/mĀ²
40 kJ/mĀ²
25 kJ/mĀ²
25 kJ/mĀ²
25 kJ/mĀ²
20 kJ/mĀ²

Thermal Properties

Temperature of deflection under load HDT/A

ISO 75

1,8 MPa
200 Ā°C

Melting temperature

ISO 11357-3

DSC, 10K/min
222 Ā°C

Flammability

Burning rate

UL 94

1,6 mm Wall thickness
HB Class

Burning rate (<100 mm/min)

FMVSS 302

> 1 mm Thickness
+

General properties

Density

ISO 1183

23Ā°C
1,28 g/cmĀ³

Humidity absorption

ISO 1110

70Ā°C, 62% r.H.
1,3 - 1,5 %

Molding shrinkage

ISO 294-4

flow
transverse
0,1 - 0,3 %
0,5 - 0,7 %

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKROĀ®, AKROMIDĀ®, AKROLENĀ®, AKROLOYĀ®, AKROTEKĀ®, ICXĀ® and PRECITEĀ® are registered trademarks of the Feddersen Group.

Contact

Do you have any questions? We are happy to help.

Would you like to learn more about AKRO-PLASTIC GmbH? Contact us! We will be happy to help you.

Learn more