Description

AKROMIDĀ®

B3 GF 60 1 black (4644)

PA6 GF60

AKROMIDĀ® B3 GF 60 1 black (4644) - 60% glass fiber reinforced, PA 6, heat stabilised, easy flow

Modulus

21.000MPa

Strength

250MPa

Impact

90kJ/mĀ²

AKROMIDĀ® B3 GF 60 1 black (4644) - 60% glass fiber reinforced, PA 6, heat stabilised, easy flow

AKROMIDĀ®

UL

B3 GF 30 FR orange (7857)

PA6 GF 30 FR(40)

AKROMIDĀ® B3 GF 30 FR orange (7857) is a 30% glass fibre reinforced, halogene free flame retardant polyamide 6 with flammability acc UL 94 V0 and low corrosion colored in orange (RAL 2003)

Modulus

10.500MPa

Strength

135MPa

Impact

65kJ/mĀ²

AKROMIDĀ® B3 GF 30 FR orange (7857) is a 30% glass fibre reinforced, halogene free flame retardant polyamide 6 with flammability acc UL 94 V0 and low corrosion colored in orange (RAL 2003)

AKROMIDĀ®

Preliminary

B3 GF 30 ECO black (7923)

PA6 GF30

AKROMIDĀ® B3 GF 30 ECO black (7923) - PA 6, 30% glass fiber, recycling, heat-stabilised, high stiffness and strength, automotive, mechanical engineering.

Modulus

9.500MPa

Strength

155MPa

Impact

75kJ/mĀ²

AKROMIDĀ® B3 GF 30 ECO black (7923) - PA 6, 30% glass fiber, recycling, heat-stabilised, high stiffness and strength, automotive, mechanical engineering.

AKROMIDĀ®

C28 M 30 6 black (7934)

PA66+PA6 MD30

AKROMIDĀ® C28 M 30 6 black (7934) is a 30% mineral filled, high heat stabilized polyamid 6.6/6 with very good surface low warpage and easy flow.

Modulus

6.000MPa

Strength

70MPa

Impact

30kJ/mĀ²

AKROMIDĀ® C28 M 30 6 black (7934) is a 30% mineral filled, high heat stabilized polyamid 6.6/6 with very good surface low warpage and easy flow.

AKROMIDĀ®

UL

C3 1 FR natural (8050)

PA66+PA6 FR(30)

AKROMIDĀ® C3 1 FR natural (8050) - PA6/6.6 blend, unreinforced, flame retardant, UL-listed, very good flowability, public transportation, new mobility.

Modulus

3.600MPa

Strength

77MPa

Impact

100kJ/mĀ²

AKROMIDĀ® C3 1 FR natural (8050) - PA6/6.6 blend, unreinforced, flame retardant, UL-listed, very good flowability, public transportation, new mobility.

AKROMIDĀ®

B3 GF 15 1 black (2482)

PA6 GF15

AKROMIDĀ® B3 GF 15 1 black (2482) is a 15% glass fibre reinforced, heat stabilised polyamide 6 with medium stiffness and strength.

Modulus

6.100MPa

Strength

120MPa

Impact

52kJ/mĀ²

AKROMIDĀ® B3 GF 15 1 black (2482) is a 15% glass fibre reinforced, heat stabilised polyamide 6 with medium stiffness and strength.

AKROMIDĀ®

C3 GF 30 5 XTC natural (4499)

PA66 + PA6 GF 30

AKROMIDĀ® C3 GF 30 5 XTC natural (4499) is a 30% glass fibre reinforced, high temperature stabilised polaymide 6.6/6 - Blend with high stiffness and strength and extra high temperature tolerance.

Modulus

9.500MPa

Strength

185MPa

Impact

95kJ/mĀ²

AKROMIDĀ® C3 GF 30 5 XTC natural (4499) is a 30% glass fibre reinforced, high temperature stabilised polaymide 6.6/6 - Blend with high stiffness and strength and extra high temperature tolerance.

132333480

AKROMIDĀ®

A3 S1 black (1071)PA66-I

AKROMIDĀ® A3 S1 black 950089 (1071) is an unreinforced, impact modified Polyamide 6.6. The material is characterised by a very high impact strength even at low temperatures and therefore perfectly suitable for connecting and fixing systems which are used in the automotive and electro industry and that are exposed to high loading speeds.

Features

impact modified

Properties

Modulus

2.000MPa

Strength

50MPa

Impact

180kJ/mĀ²

Mechanical Properties

Tensile modulus

ISO 527-2

1 mm/min | d.a.m.
1 mm/min | conditioned
2000 MPa
1200 MPa

Tensile stress at yield

ISO 527-2

50 mm/min | d.a.m.
50 mm/min | conditioned
50 MPa
40 MPa

Tensile strain at yield

ISO 527-2

50 mm/min | d.a.m.
4,8 %

Tensile strain at break

ISO 527-2

50 mm/min | d.a.m.
50 mm/min | conditioned
> 50 %
> 100 %

Flexural modulus

ISO 178

2 mm/min | d.a.m.
1950 MPa

Charpy impact strength

ISO 179-1/1eU

23Ā°C | d.a.m.
23Ā°C | conditioned
30Ā°C | d.a.m.
-
30Ā°C | conditioned
-
40Ā°C | d.a.m.
-
no break
no break
no break
no break
no break

Charpy notched impact strength

ISO 179-1/1eA

23Ā°C | d.a.m.
23Ā°C | conditioned
30Ā°C | d.a.m.
-
30Ā°C | conditioned
-
40Ā°C | d.a.m.
-
> 80 kJ/mĀ²
> 100 kJ/mĀ²
35 kJ/mĀ²
35 kJ/mĀ²
35 kJ/mĀ²

Ball indentation hardness

ISO 2039-1

358N/30s | d.a.m.
80 MPa

Thermal Properties

Temperature of deflection under load HDT/A

ISO 75

1,8 MPa
70 Ā°C

Temperature of deflection under load HDT/B

ISO 75

0,45 MPa
152 Ā°C

Melting temperature

ISO 11357-3

DSC, 10K/min
262 Ā°C

Flammability

Burning rate

UL 94

UL
0,8 mm Wall thickness
HB Class

Burning rate (<100 mm/min)

FMVSS 302

> 1 mm Thickness
+

General properties

Density

ISO 1183

23Ā°C
1,07 g/cmĀ³

Humidity absorption

ISO 1110

70Ā°C, 62% r.H.
1,9 - 2,1 %

Molding shrinkage

ISO 294-4

flow
transverse
1,3 - 1,5 %
1,5 - 1,7 %

Electrical Properties

Volume resistivity IEC

DIN EN IEC 62631-3-2

d.a.m.
1015 ā„¦ x cm

Surface resistivity

DIN EN 62631-3-2

d.a.m.
1014 ā„¦

Comparative tracking index

IEC 60112

Test liquid A
600 V

Disclaimer

All specifications and information given on this website are based on our current knowledge and experience. A legally binding promise of certain characteristics or suitability for a concrete individual case cannot be derived from this information. The information supplied here is not intended to release processors and users from the responsibility of carrying out their own tests and inspections in each concrete individual case. AKROĀ®, AKROMIDĀ®, AKROLENĀ®, AKROLOYĀ®, AKROTEKĀ®, ICXĀ® and PRECITEĀ® are registered trademarks of the Feddersen Group.

Contact

Do you have any questions? We are happy to help.

Would you like to learn more about AKRO-PLASTIC GmbH? Contact us! We will be happy to help you.

Learn more